Polymer Property : Density = 1.31 g/cc Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Density 1.19 - 1.31 g/cc

@Temperature 250 - 250 °C
0.0430 - 0.0473 lb/in³

@Temperature 482 - 482 °F
Average value: 1.25 g/cc Grade Count:2
Overview of materials for Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled".Specific grades with glass content between 5% ..
Density 1.25 - 1.31 g/cc
0.0452 - 0.0473 lb/in³
Sibur ONZ-40 Compound M-258 Polyvinyl Chloride (PVC)
Shall correspond to control sample, approved in accordance with the established procedure. Pores, which can be seen by eyes, are not allowed. Plastic shall no burn at stop of worm extruder for a p..
Density 1.27 - 1.31 g/cc
0.0459 - 0.0473 lb/in³
ISO R 1183
Fainplast Compounds CL 70/2 Flexible PVC, Sheathing
General purposes
Density 1.27 - 1.31 g/cc
0.0459 - 0.0473 lb/in³
ISO R 1183
Fainplast Compounds FR 70 Flexible PVC, Insulation
Good flexibility cables
Density 1.27 - 1.31 g/cc
0.0459 - 0.0473 lb/in³
ISO R 1183
Fainplast Compounds FR 83/1 Flexible PVC, Insulation
General purposes
Density 1.27 - 1.31 g/cc
0.0459 - 0.0473 lb/in³
ISO R 1183
Fainplast Compounds GS 6820 Flexible PVC, Injection Molding for Footwear
Soles
Density 1.27 - 1.31 g/cc
0.0459 - 0.0473 lb/in³
ISO R 1183
Fainplast Compounds GS 7016 Flexible PVC, Injection Molding for Footwear
Soles for mild climates
Density 1.27 - 1.31 g/cc
0.0459 - 0.0473 lb/in³
ISO R 1183
Fainplast Compounds GS 7216 Flexible PVC, Injection Molding for Footwear
Soles
Density 1.27 - 1.31 g/cc
0.0459 - 0.0473 lb/in³
ISO R 1183
Fainplast Compounds GS 7716 Flexible PVC, Injection Molding for Footwear
Soles for mild climates
Density 1.27 - 1.31 g/cc
0.0459 - 0.0473 lb/in³
ISO R 1183
Fainplast Compounds GS 90/K Flexible PVC, Injection Molding for Footwear
Technical items for sandals
Density 1.27 - 1.31 g/cc
0.0459 - 0.0473 lb/in³
ISO R 1183
Fainplast Compounds GS 90/T Flexible PVC, Injection Molding for Footwear
Technical items for footwear
Density 1.27 - 1.31 g/cc
0.0459 - 0.0473 lb/in³
ISO R 1183
Fainplast Compounds GSK 74/UV Flexible PVC, Injection Molding, Lead Free
Technical items for outdoor
Density 1.27 - 1.31 g/cc
0.0459 - 0.0473 lb/in³
ISO R 1183
Fainplast Compounds CKL 0252/R Flexible PVC, Sheathing Lead Free
Mineral oil resistant sheathing
Density 1.27 - 1.31 g/cc
0.0459 - 0.0473 lb/in³
ISO R 1183
Fainplast Compounds CKL 59/OP Flexible PVC, Sheathing Lead Free
Sheathing music instruments
Density 1.27 - 1.31 g/cc
0.0459 - 0.0473 lb/in³
ISO R 1183
Fainplast Compounds CL 74/R Flexible PVC, Sheathing
Mineral oil resistent
Density 1.27 - 1.31 g/cc
0.0459 - 0.0473 lb/in³
ISO R 1183
Fainplast Compounds PH 90/AS Flexible PVC, Transparent Extrusion
Food belt carriers
Density 1.27 - 1.31 g/cc
0.0459 - 0.0473 lb/in³
ISO R 1183
Fainplast Compounds PK 91 Flexible PVC, Lead Free
Fencing
Density 1.30 - 1.31 g/cc
0.0470 - 0.0473 lb/in³
ISO 1183
Beijing Ranger Chem BLUESTAR® 1079 PBT
Can be used directly for spinning, and producing color concentrates. It can also be used for production after reinforcement & compounding.Information provided by Beijing Ranger Chemical Co.
Density 1.30 - 1.31 g/cc
0.0470 - 0.0473 lb/in³
ISO 1183
Beijing Ranger Chem BLUESTAR® 1084 PBT
Can be used directly for spinning, and producing color concentrates. It can also be used for production after reinforcement & compounding.Information provided by Beijing Ranger Chemical Co.
Density 1.30 - 1.31 g/cc
0.0470 - 0.0473 lb/in³
ISO 1183
Beijing Ranger Chem BLUESTAR® 1110 PBT
Can be used directly for spinning, or it can be used after reinforcement & compounding. It can also be used to produce cable sheath through tackificationInformation provided by Beijing Ranger Chemic..
Density 1.30 - 1.31 g/cc
0.0470 - 0.0473 lb/in³
ISO 1183
Beijing Ranger Chem BLUESTAR® 1135 PBT
Can be used directly to produce cable sheathInformation provided by Beijing Ranger Chemical Co.
Density 1.20 - 1.31 g/cc

@Temperature 250 - 270 °C
0.0434 - 0.0473 lb/in³

@Temperature 482 - 518 °F
Average value: 1.27 g/cc Grade Count:3
Overview of materials for Nylon 6, 30% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E..
Density 1.28 - 1.31 g/cc
0.0462 - 0.0473 lb/in³
Average value: 1.30 g/cc Grade Count:3
Overview of materials for PEKK, Unreinforced
This property data is a summary of similar materials in the MatWeb database for the category "PEKK, Unreinforced". Each property range of values reported is minimum and maximum values of appropriate..
Density 1.26 - 1.31 g/cc
0.0455 - 0.0473 lb/in³
Average value: 1.27 g/cc Grade Count:28
Overview of materials for Cellulose Acetate, Molded
This property data is a summary of similar materials in the MatWeb database for the category "Cellulose Acetate, Molded". Each property range of values reported is minimum and maximum values of appr..
Density 1.16 - 1.31 g/cc
0.0419 - 0.0473 lb/in³
Average value: 1.19 g/cc Grade Count:92
Overview of materials for Cellulose Acetate Butyrate, Molded
This property data is a summary of similar materials in the MatWeb database for the category "Cellulose Acetate Butyrate, Molded". Each property range of values reported is minimum and maximum value..
Density 1.27 - 1.31 g/cc
0.0459 - 0.0473 lb/in³
ISO R 1183
Fainplast Compounds PM 70/FR Flexible PVC, Lead Free
Spiral pipes, UL 94 Class V0
Density 1.27 - 1.31 g/cc
0.0459 - 0.0473 lb/in³
ISO R 1183
Fainplast Compounds PM 8012 Flexible PVC, Lead Free
Various profiles
Density 1.30 - 1.31 g/cc
0.0470 - 0.0473 lb/in³
ISO 1183
Beijing Ranger Chem BLUESTAR® 1120 PBT
Can be used directly to produce cable sheathInformation provided by Beijing Ranger Chemical Co.