Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.50 - 1.60 g/cc | 0.0542 - 0.0578 lb/in³ | |
Prodways PLASTCure Rigid 10 500 3D Printing Polymer Superior thermo-mechanical properties.Suitable for the manufacture of parts that require thermal stability, extreme accuracy and quick turnaround. Exceptional for parts that are designed for wind tu.. |
|||
Density | 1.47 - 1.60 g/cc @Temperature 250 - 260 °C |
0.0531 - 0.0578 lb/in³ @Temperature 482 - 500 °F |
Average value: 1.54 g/cc Grade Count:2 |
Overview of materials for Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled". Specific grades with glass content between 45.. |
|||
Density | 1.36 - 1.60 g/cc | 0.0491 - 0.0578 lb/in³ | Average value: 1.44 g/cc Grade Count:13 |
Overview of materials for PEKK, Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PEKK, Reinforced". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
Density | 1.10 - 1.60 g/cc | 0.0397 - 0.0578 lb/in³ | Average value: 1.24 g/cc Grade Count:254 |
Overview of materials for Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced". Each property range of values repor.. |
|||
Density | 1.59 - 1.60 g/cc | 0.0574 - 0.0578 lb/in³ | Average value: 1.59 g/cc Grade Count:5 |
Overview of materials for Polyetherimide (PEI), 40% Glass Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 40% Glass Fiber". Specific grades with glass content between 35% and 44% are included. E.. |
|||
Density | 1.45 - 1.60 g/cc | 0.0524 - 0.0578 lb/in³ | Average value: 1.53 g/cc Grade Count:21 |
Overview of materials for Phenolic, Novolac, Mineral/Flock Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral/Flock Filled". Each property range of values reported is minimum and maximum .. |
|||
Density | 1.34 - 1.60 g/cc | 0.0484 - 0.0578 lb/in³ | Average value: 1.51 g/cc Grade Count:3 |
Overview of materials for Phenolic/Rubber; Molded This property data is a summary of similar materials in the MatWeb database for the category "Phenolic/Rubber; Molded". Each property range of values reported is minimum and maximum values of approp.. |
|||
Density | 1.48 - 1.60 g/cc | 0.0535 - 0.0578 lb/in³ | Average value: 1.52 g/cc Grade Count:12 |
Overview of materials for Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler". Specific grades with carbon fiber content bet.. |
|||
Density | 1.14 - 1.60 g/cc | 0.0412 - 0.0578 lb/in³ | Average value: 1.28 g/cc Grade Count:250 |
Overview of materials for Nylon 66, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. .. |
|||
Density | 1.12 - 1.60 g/cc | 0.0405 - 0.0578 lb/in³ | Average value: 1.29 g/cc Grade Count:122 |
Overview of materials for Nylon 66, Glass Reinforced, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Reinforced, Impact Grade". Each property range of values reported is minimum and maximum.. |
|||
Density | 1.10 - 1.60 g/cc | 0.0397 - 0.0578 lb/in³ | Average value: 1.33 g/cc Grade Count:12 |
Overview of materials for Nylon 66, 10% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 10% Mineral Filled". Specific grades with primary filler content between 5% and 14% are includ.. |
|||
Density | 1.45 - 1.60 g/cc | 0.0524 - 0.0578 lb/in³ | Compounded |
Epichlorohydrin Rubber (CO, ECO) CO is the ISO designation for the homopolymer and ECO is the ISO designation for the ethylene oxide copolymer. Epichlorohydrin rubber is generally damaged by chlorinated solvents, ketones, aldehyde.. |
|||
Density | 1.45 - 1.60 g/cc | 0.0524 - 0.0578 lb/in³ | Compounded |
Chlorosulfonated Polyethylene Rubber (CM, CSM) The chlorine (in CM) or chlorine and chlorosulfonyl (CSM) groups prevent the crystallization that occurs on unmodified polyethylene. |
|||
Density | 1.56 - 1.60 g/cc | 0.0564 - 0.0578 lb/in³ | ISO R 1184 |
Fainplast Compounds RE 330 Rigid PVC, Extrusion Various profiles |
|||
Density | 1.56 - 1.60 g/cc | 0.0564 - 0.0578 lb/in³ | ISO R 1184 |
Fainplast Compounds RE 425 Rigid PVC, Extrusion Electric channels |
|||
Density | 1.56 - 1.60 g/cc | 0.0564 - 0.0578 lb/in³ | ISO R 1184 |
Fainplast Compounds RE 425/R Rigid PVC, Extrusion Shiny electric channels |
|||
Density | 1.56 - 1.60 g/cc | 0.0564 - 0.0578 lb/in³ | ISO R 1184 |
Fainplast Compounds RH 306/W Rigid PVC, Antishock Extrusion Antishock profiles |
|||
Density | 1.56 - 1.60 g/cc | 0.0564 - 0.0578 lb/in³ | ISO R 1184 |
Fainplast Compounds RK 335/1 Rigid PVC, Extrusion Lead Free Profiles |
|||
Density | 1.50 - 1.60 g/cc | 0.0542 - 0.0578 lb/in³ | |
Chengdu Polyster MCA Melamine Cyanurate White crystal power with satiny. It is an excellent non-halogen N flame retardant. The product is mainly used as non-halogen flame retardant for synthetic resin(PA, PVC, PS, POM), synthetic rubber a.. |
|||
Density | 1.45 - 1.60 g/cc | 0.0524 - 0.0578 lb/in³ | Molding; IS 867-1963 |
Amity Thermosets ATF 197 Phenolic Molding Inorganic and glass Filler, Compression Molded Characteristics:Flame retardantSpark resistant Good electrical insulationHeat stability ( 200°C )Good mouldability Low water absorptionLow shrinkageColor-blackSoft/medium flow Applications:Switchg.. |
|||
Density | 1.11 - 1.60 g/cc | 0.0401 - 0.0578 lb/in³ | Average value: 1.30 g/cc Grade Count:112 |
Overview of materials for Nylon 66, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, PTFE Filled". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Density | 1.46 - 1.60 g/cc | 0.0527 - 0.0578 lb/in³ | Average value: 1.51 g/cc Grade Count:9 |
Overview of materials for Polysulfone, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are inc.. |