- Polymer Property : Particle Size = 125 µm
Polymer Property : Particle Size = 125 µm Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Particle Size | 125 - 500 µm | 125 - 500 µm | Average value: 283 µm Grade Count:3 |
| Overview of materials for Anhydride-Modified Polyethylene This property data is a summary of similar materials in the MatWeb database for the category "Anhydride-Modified Polyethylene". Each property range of values reported is minimum and maximum values o.. |
|||
| Particle Size | 125 µm | 125 µm | 3% max, wet sieve |
| Magyar Aluminum ALO-DFM Alumina Alumina for Polishing |
|||
| Particle Size | 125 µm | 125 µm | Average Size |
| Inhance Fluoro-Seal INHANCE® UH-1080 Ultra High Molecular Weight Polyethylene Product Description: INHANCE UH-1000 series particles are surface-activated Ultra High Molecular Weight Polyethylene (UHMWPE) in powder form. Surface activation makes the particles easy to disperse.. |
|||
| Particle Size | 125 µm | 125 µm | Maximum of 10% greater than |
| H.C. Starck Amperit® 155.093 Titanium (Ti) HS Number: 81081010 |
|||
| Particle Size | 125 µm | 125 µm | Maximum of 7% greater than |
| H.C. Starck Amperit® 413.6 Gas Atomized (NiCoCrAlY) |
|||
| Particle Size | 125 µm | 125 µm | 100% less than |
| H.C. Starck Amperit® 527.088 Agglomerated, Sintered Tungsten Carbide-Cobalt (WC-Co) 83-17 |
|||
| Particle Size | 125 µm | 125 µm | 100% less than |
| H.C. Starck Amperit® 558.088 Tungsten Carbide-Cobalt-Chromium 86-10-4 (WC-Co-Cr) |
|||
| Particle Size | 125 µm | 125 µm | Maximum of 2% greater than |
| H.C. Starck Amperit® 847.6 Agglomerated Yttria (Y2O3) |
|||
| Particle Size | <= 125 µm | <= 125 µm | 0.15; Malvern |
| SABIC Innovative Plastics NORYL SA120FIN PPE (Asia Pacific) Noryl* SA120FIN resin is a powder version of a low molecular weight polymer based on Polyphenylene ether (PPE). Noryl* SA120FIN is intended for use as additive or building block in a variety of the.. |
|||
| Particle Size | <= 125 µm | <= 125 µm | 0.15; Malvern |
| SABIC Innovative Plastics NORYL SA120FIN PPE (Europe-Africa-Middle East) Noryl* SA120FIN resin is a powder version of a low molecular weight polymer based on Polyphenylene ether (PPE). Noryl* SA120FIN is intended for use as additive or building block in a variety of the.. |
|||
| Particle Size | 125 µm | 125 µm | <16 g/kg greater than value; ISO 1624 |
| SolVin 173GB Polyvinyl Chloride Emulsion Polymer Made by emulsion polymerization.
APPLICATIONS
Calendering : plasticized films and sheets
Extrusion : rigid or plasticized pipes and profiles
In most cases, SolVin 173GB resin is used in blends with .. |
|||
| Particle Size | 125 µm | 125 µm | <0.05 g/kg greater than value; ISO 1624 |
| SolVin 266SF Polyvinyl Chloride Pastes - filler Polymers Made by suspension polymerisation.
APPLICATIONS
Filler polymer for plastisols
- Floor covering : hard-wearing top coats, chemically blown and mechanical foams, impregnation layers
- Wall coverings
-.. |
|||
| Particle Size | 125 µm | 125 µm | <0.2 g/kg greater than value; ISO 787-18 |
| SolVin 360NA Polyvinyl Chloride Low Viscosity Paste Made by microsuspension polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- artificial leather compact layer
- artificial leather foam layer
- flooring backing foam .
Mold.. |
|||
| Particle Size | 125 µm | 125 µm | <0.15 g/kg greater than value; ISO 787-18 |
| SolVin 367NC Polyvinyl Chloride Low Viscosity Paste Made by emulsion polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- artificial leather compact layer
- artificial leather foam layer
- artificial leather automotive.
ADVA.. |
|||
| Particle Size | 125 µm | 125 µm | <0.2 g/kg greater than value; ISO 787-18 |
| SolVin 367NF Polyvinyl Chloride Low Viscosity Paste Made by microsuspension polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- artificial leather compact layer
- artificial leather foam layer
- flooring foam layer
- floori.. |
|||
| Particle Size | 125 µm | 125 µm | <0.15 g/kg greater than value; ISO 787-18 |
| SolVin 370HD Polyvinyl Chloride High Viscosity Paste Made by emulsion polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- artificial leather compact layer
- artificial leather foam layer
- artificial leather automotive
Mold.. |
|||
| Particle Size | 125 µm | 125 µm | <0.2 g/kg greater than value; ISO 787-18 |
| SolVin 372HA Polyvinyl Chloride High Viscosity Paste Made by emulsion polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- artificial leather compact layer
- artificial leather foam layer
- tarpaulins
Molding and dipping.
Sp.. |
|||
| Particle Size | 125 µm | 125 µm | <0.2 g/kg greater than value; ISO 787-18 |
| SolVin 372NA Polyvinyl Chloride Low Viscosity Paste Made by emulsion polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- flooring foam layer
- flooring impregnation layer
- flooring backing foam
- tarpaulins
- coil coating... |
|||
| Particle Size | 125 µm | 125 µm | <0.2 g/kg greater than value; ISO 787-18 |
| SolVin 372NF Polyvinyl Chloride Low Viscosity Paste Made by microsuspension polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- artificial leather compact layer
- artificial leather foam layer
- flooring foam layer
- floori.. |
|||
| Particle Size | 125 µm | 125 µm | <0.15 g/kg greater than value; ISO 787-18 |
| SolVin 375MD Polyvinyl Chloride Medium Viscosity Paste Made by emulsion polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- artificial leather compact layer
- artificial leather foam layer
- artificial leather automotive.
ADVA.. |
|||
| Particle Size | 125 µm | 125 µm | <0.2 g/kg greater than value; ISO 787-18 |
| SolVin 376NB Polyvinyl Chloride Low Viscosity Paste Made by emulsion polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- artificial leather compact layer
- flooring top coat
- tarpaulins .
Molding and dipping.
ADVANTAGES
- .. |
|||
| Particle Size | <= 125 µm | <= 125 µm | <0.2 g/kg retained on 125 micron sieve; ISO 787-18 |
| SolVin 382NG Polyvinyl Chloride Homopolymer Polyvinyl chloride made by microsuspension polymerization. Uses: Spread coating - flooring top coat. Attributes: High filler acceptance; Matte appearance in flooring top coat; Good viscosity stabil.. |
|||
| Particle Size | 125 µm | 125 µm | <0.15 g/kg greater than value; ISO 787-18 |
| SolVin 386NB Polyvinyl Chloride Low Viscosity Paste Made by emulsion polymerization for plastisol preparation.
MAIN APPLICATION
Spread coating :
- flooring top coat.
ADVANTAGES
- Matt appearance in flooring to coat.
- Good viscosity stability on stor.. |
|||
| Particle Size | <= 125 µm | <= 125 µm | 0.2 |
| Arkema Group OREVAC® 18345 RNP Pipe Coating Binder Resin OREVAC 18345 RNP is a range of modified polyethylene which, when molten, have excellent adhesive properties to various substrates and are designed to bond dissimilar materials. It is supplied in bla.. |
|||
| Particle Size | <= 125 µm | <= 125 µm | 0.1 |
| Arkema Group OREVAC® 18350P Grafted Maleic Anhydride Polyethylene OREVAC 18350P is a maleic anhydride grafted polyethylene used in the manufacturing of three layer MDPE and HDPE coating for steel pipeline. It is mainly used in pipe coating to have good adhesion pe.. |
|||
| Particle Size | 125 - 315 µm | 125 - 315 µm | 0.65 |
| Arkema Group OREVAC® 18350P Grafted Maleic Anhydride Polyethylene OREVAC 18350P is a maleic anhydride grafted polyethylene used in the manufacturing of three layer MDPE and HDPE coating for steel pipeline. It is mainly used in pipe coating to have good adhesion pe.. |
|||
| Particle Size | 125 - 315 µm | 125 - 315 µm | 80-90% |
| Arkema Group OREVAC® 18510P Grafted Maleic Anhydride Polyethylene OREVAC 18510P is a maleic anhydride grafted polyethylene used in the manufacturing of three layer MDPE or HDPE coating for steel pipeline. It is a powder product. OREVAC 18510P is mainly used in pip.. |
|||
| Particle Size | <= 125 µm | <= 125 µm | 0.2 |
| Arkema Group OREVAC® 18732 Grafted Maleic Anhydride Polypropylene OREVAC 18732 and 18732P are maleic anhydride grafted polypropylene used in the manufacturing of multiplayer structures. These products are available in pellets or in powder. OREVAC 18732 and 18732P .. |
|||
| Particle Size | 125 µm | 125 µm | 100% less than |
| H.C. Starck Amperit® 588.088 Chromium Carbide-Nickel Chromium 75-25 (Cr3C2-NiCr) 53/20 µm |
|||
| Particle Size | 125 µm | 125 µm | <0.15 g/kg greater than value; ISO 787-18 |
| SolVin 374MB Polyvinyl Chloride Medium Viscosity Paste Made by emulsion polymerization for plastisol preparation.
MAIN APPLICATIONS
Spread coating :
- artificial leather compact layer
- artificial leather foam layer
- tarpaulins.
Molding and dipping.
Sp.. |
|||