Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ISO 294-4 |
Premix Thermoplastics PRE-ELEC® ESD 5300 Static Dissipative Thermoplastic Compound PRE-ELEC® ESD 5300 is a static dissipative thermoplastic compound based on polypropylene homopolymer. The dissipative property is permanent and built into the polymer chain. Surface resistance valu.. |
|||
Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ISO 294-4 |
Premix Thermoplastics PRE-ELEC® ESD 5500 Static Dissipative Thermoplastic Compound PRE-ELEC® ESD 5500 is a static dissipative thermoplastic compound based on polypropylene. The dissipative property is permanent and built into the polymer chain. PRE-ELEC® ESD 5500 can be injectio.. |
|||
Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | Across Flow; ISO 2577 |
Polykemi AB SCANMID 6 B52^ E Nylon 6, Modified Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.016 - 0.022 cm/cm | 0.016 - 0.022 in/in | ASTM D955 |
Polymer Resources TP-GP1-IM Polybutylene Terephthalate, Impact Modified, Medium Flow Polybutylene Terephthalate, Impact Modified, Medium FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informat.. |
|||
Linear Mold Shrinkage | 0.016 - 0.020 cm/cm | 0.016 - 0.020 in/in | ASTM D955 |
Polymer Resources NY6-IM1 Nylon 6, Impact Modified Nylon 6, Impact ModifiedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (.. |
|||
Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | Exxon Method |
ExxonMobil Escorene® HD-6733 HDPE, Injection Grade
(discontinued **) Data Provided by Exxon Chemical Canada.Characteristics: High Flow, Good StiffnessUses: Food containers, Small pails, Nursery containers |
|||
Linear Mold Shrinkage | 0.016 - 0.019 cm/cm | 0.016 - 0.019 in/in | ASTM D955 |
LG Chemical LUCEL GB-325 Low Warpage POM, 25% Glass Bead Filled LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Linear Mold Shrinkage | 0.016 - 0.019 cm/cm | 0.016 - 0.019 in/in | ASTM D955 |
LG Chemical LUCEL HI-525 High Impact POM, Unreinforced LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM D955 |
Ineos 3950 Polypropylene Impact Copolymer Grade 3950 typically has a 35 melt flow rate and is a low gloss, high impact polypropylene copolymer. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21.. |
|||
Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM D955 |
Teknor Apex Monprene® MP-1301A Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM D955 |
Teknor Apex Monprene® MP-2228 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM D955 |
Tipco Tipcolene® FPC 20 PPC - 20% Calcium Carbonate Reinforced Polypropylene Copolymer 20% Calcium Carbonate Filled PP CopolymerApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India. |
|||
Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM D955 |
Tipco Tipcolene® FPZ-CL - 10% Talc/Mineral Reinforced Polypropylene Copolymer Compound 10% Mineral Reinforced PP CopolymerApplications: Automotive InteriorsProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
Linear Mold Shrinkage | 0.016 cm/cm @Thickness 2.00 mm |
0.016 in/in @Thickness 0.0787 in |
|
Toyobo Pelprene™ P-280B Polyester TPE Key Feature: Pelprene P typePelprene™ can be processed into a wide variety of articles from ultra-small precision parts to sheets by injection, extrusion, and blow molding. The 'P' type is a block.. |
|||
Linear Mold Shrinkage | 0.016 cm/cm @Thickness 3.17 mm |
0.016 in/in @Thickness 0.125 in |
ASTM D955 |
Diamond Polymers NYLON 6615 Black, Super Tough Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | |
E-Polymers TEKAFIN® PH40FR2 Flame Retardant Heat Resistance Compounded-PP Modified PP: TEKAFIN is modified PP resins formulated with various fillers and modifiers. It has product lines for impact modified, glass fiber reinforced, inorganic filler reinforced and hybrids.I.. |
|||
Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | |
E-Polymers TEKASTER® F100 low-mid viscosity PBT Polyester Resin: TEKASTER is thermoplastic polyester resins (PBT, PET) mostly injection molding. PBT has excellent mechanical properties and well balanced engineering plastics with an electrical pe.. |
|||
Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM Data; MD |
BASF Ultramid® 1310-11 NF2001 PA66 (Dry) Ultramid 1310-11 NF2001 is a controlled crystallization, fast cycling PA6/6 which provides extremely fast cycle times and improved productivity over Ultramid 1000. |
|||
Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM Data; MD |
BASF Ultramid® 1000-11 NF2001 PA66 (Dry) Ultramid 1000-11 NF2001 is a general purpose nylon 6/6. |
|||
Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM Data; MD |
BASF Ultramid® 1000-2 NF2001 PA66 (Dry) Ultramid 1000-2 NF2001 is a general purpose PA6/6. |
|||
Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM D955 |
Aaron Industries AAROPRENE® AEN 6600-1 Nylon 6/6 Engineered Resin |
|||
Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM D955 |
Aaron Industries AAROPRENE® AEN 6600-3 Nylon 6/6 Engineered Resin |
|||
Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM D955 |
Multibase Multi-Flex® TPE A 7606 UV NAT The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM D955 |
Asahi Kasei Thermofil P-10CC-Y488 10% Calcium Carbonate Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||
Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM D955 |
Ashley Polymers Ashlene® R6041 Nylon 66, PTFE and Silicone Modified Nylon 66 PTFE and Silicone modified for excellent wear characteristics and low friction.Data provided by the manufacturer |