Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | Euronil |
Nilit Nilamid B3 H G8 40% Glass Fiber Reinforced PA6 Description: Nilamid B3 H G8 is a product that combines outstanding strength and stiffness with good moldability and good impact strength. It is widely used for structural applications.Key character.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0035 cm/cm @Thickness 3.20 mm |
0.0025 - 0.0035 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics Cycoloy® NX07353 PC+ABS (Asia Pacific) Cycoloy* C7230P resin is a mineral filled, flame retardant PC/ABS. Good stiffness combined with balanced flow and impact performance, makes it a good candidate for various applications. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | ISO 294-4 |
Radici Raditer® B RVA 300 Polybutylene Terephthalate with 30% Glass fiber Raditer® B RVA is a range of glass fiber reinforced Polybutylene terephthalate blends for injection molding, with excellent dimensional stability, low warpage and good surface aspect.Information pr.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0035 cm/cm @Thickness 3.20 mm |
0.0025 - 0.0035 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics Cycoloy® C7230P PC+ABS (Asia Pacific) Cycoloy* C7230P resin is a mineral filled, flame retardant PC/ABS. Good stiffness combined with balanced flow and impact performance, makes it a good candidate for various applications. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | |
Solvay Specialty Polymers Ixef® 1501/0003 Polyarylamide, 30% Glass Fiber, DAM
(discontinued **) The IXEF compounds are a family of semi-crystalline polyarylamide thermoplastics reinforced with glass fibers and/or mineral fillers for injection molding.Data provided by the manufacturer, Solvay A.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | ASTM D955 |
Solvay Specialty Polymers Mindel® B-430 Polysulfone, Modified (PSU, Modified)
(discontinued **) Mindel B-430 is a 30% glass reinforced thermoplastic with excellent dimensional stability, exceptional resistance to warp, good chemical resistance, and high stiffness. It was developed specifically.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 |
Lanxess Durethan® BKV 130 CS DUS008 600091 Nylon 6, 30% Glass Fiber PA 6, 30% glass fiber, injection molding, impact modifiedInformation provided by LANXESS. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0045 cm/cm | 0.0025 - 0.0045 in/in | |
LATI Latamid 6 H2 G/30-V0CT1 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0050 cm/cm | 0.0025 - 0.0050 in/in | |
LATI Latamid 6 H2E04 G/30 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized Polyamide 6 (PA6) based compound. Heat stabilized. Toughened. Glass fibers. Good elongation.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0055 cm/cm | 0.0025 - 0.0055 in/in | |
LATI Laticonther 82 CP1/800 PA12 High thermal conductivity product based on Polyamide 12 (PA12). Special fillerAvailability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Indus.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | |
Solvay TECHNYLSTARâ„¢ SX 218 V50 BK 38N-K PA6, 50% glass filled, DRY Description: High stiffness materials Technylstar polyamide 6, reinforced with 50% of glass fiber, heat stabilized, for injection molding. Characterized by a high fluidity of the melt.Available in: .. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Thickness 3.17 mm |
0.0025 in/in @Thickness 0.125 in |
ASTM D955 |
Techmer ES HiFill® PA6 GF50 HS L 50% Glass Filled (Conditioned) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizerInformati.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Thickness 3.17 mm |
0.0025 in/in @Thickness 0.125 in |
ASTM D955 |
Techmer ES HiFill® PA6 GF50 HS UV BK 50% Glass Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAdditive: Lubricant, UV Stabilizer and Heat StabilizerFeatures: Lubricated, Good UV Resi.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Thickness 3.17 mm |
0.0025 in/in @Thickness 0.125 in |
ASTM D955 |
Techmer ES HiFill® PA6 GF50 L 50% Glass Filled (Conditioned) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAdditive: LubricantFeatures: LubricatedInformation provided by TP Composites, Inc. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Thickness 3.17 mm |
0.0025 in/in @Thickness 0.125 in |
ASTM D955 |
Techmer ES HiFill® PA6 GF50 L BN047 LE 50% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAdditive: LubricantFeatures: Low Extractables and LubricatedAppearance: BeigeInformation.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Thickness 3.17 mm |
0.0025 in/in @Thickness 0.125 in |
ASTM D955 |
Techmer ES HiFill® PA6 GF50 RM LE 50% Glass Filled (Conditioned) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAdditive: LubricantFeatures: Low Extractables, Low Moisture Absorption and LubricatedInf.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Thickness 3.17 mm |
0.0025 in/in @Thickness 0.125 in |
ASTM D955 |
Techmer ES HiFill® PA6 GF50 RM LE 50% Glass Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAdditive: LubricantFeatures: Low Extractables, Low Moisture Absorption and LubricatedInf.. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | GB/T 15585-1995 |
Sichuan Deyang Haton® hGR20 Polyphenylene Sulfide, Glass Fiber Reinforced Injection moldingInformation provided by Sichuan Deyang Chemical Co., LTD |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0025 - 0.0080 in/in @Thickness 0.126 in |
ASTM D955 |
Samsung Cheil Industries Infino® XP-2165MC PPS Information provided by Samsung Cheil Industries. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Time 86400 sec |
0.0025 in/in @Time 24.0 hour |
ASTM D955 |
SABIC Innovative Plastics LNP THERMOCOMP VC006 SUPER TOUGH NYLON LNP* THERMOTUF* VC006 is a compound based on Super Tough Nylon resin containing 30% Carbon Fiber. Added features of this material include: High Impact, Electrically Conductive. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0025 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics NORYL HM3020H PPE+PS (Asia Pacific) PPE+PS GF+MF 30% filled, FR V-1, high flow |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Thickness 3.20 mm |
0.0025 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics LNP THERMOCOMP Noryl_HM3020 PPE+HIPS (Europe-Africa-Middle East) LNP* Thermocomp* Noryl_HM3020 compound is a 30% Glass/Mineral filled, high modulus grade. DTUL 248F (120C). UL94 V-1/5VA rated in black and gray. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Time 86400 sec |
0.0025 in/in @Time 24.0 hour |
ISO 294 |
SABIC Innovative Plastics LNP THERMOCOMP UFW49S PPA (Asia Pacific) LNP* Thermocomp* UFW49S is a compound based on Polyphthalamide resin containing Glass Fiber, Mineral. Added features of this material include: Heat Stabilized, Low Warpage. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0055 cm/cm | 0.0025 - 0.0055 in/in | ISO DIS 294-4 |
Wellman Wellamid® GF1758-BK2 33% Glass Fiber Reinforced Nylon 66 Description: Glass Fiber Reinforced Nylon 66Information provided by Wellman. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0055 cm/cm | 0.0025 - 0.0055 in/in | ISO DIS 294-4 |
Wellman Wellamid® MRGF25/15 22H-NBK1 40% Mineral/Glass Reinforced Nylon 66 Description: Mineral/Glass Reinforced Nylon 66Information provided by Wellman. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0035 cm/cm | 0.0025 - 0.0035 in/in | on Tensile Bar; E2P method |
Eurostar Starflam AFR560B1 PA66, Mineral/Glass Fiber Reinforced, Flame Retardant, Injection Molding Starflam AFR560B1 is a Flame Retardant, Mineral Filled and Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | ISO 2577 |
BASF Ultramid® B3WG6 HP BK 23210 30% Glass Filled PA6 (Dry) Description: 30% Glass fiber reinforced and heat aging resistant injection molding grade with enhances flowability used e.g. for automobile manifold.Information provided by BASF |
|||
Linear Mold Shrinkage, Flow | 0.0025 cm/cm @Time 86400 sec |
0.0025 in/in @Time 24.0 hour |
ISO 294 |
SABIC Innovative Plastics LNP THERMOCOMP GX94043L PSU (Europe-Africa-Middle East) LNP* THERMOCOMP* GX94043L is a compound based on Polysulfone resin containing Mineral. |
|||
Linear Mold Shrinkage, Flow | 0.0025 - 0.0040 cm/cm | 0.0025 - 0.0040 in/in | |
LATI Latilub 80-17ST G/30 PPS, 30% Glass Fiber Reinforced, Silicone/PTFE Filled Self-lubricating product based on Polyphenylene Sulfide (PPS). Silicone / PTFE. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provid.. |