Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage, Flow | 0.0036 cm/cm | 0.0036 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 |
Lanxess Durethan® AKV 40 H3.0 000000 Nylon 66, Glass Fiber Reinforced PA 66, 40% glass fibers, injection molding, heat-aging stabilizedInformation provided by LANXESS. |
|||
Linear Mold Shrinkage, Flow | 0.0036 - 0.0108 cm/cm | 0.0036 - 0.0108 in/in | ISO 294-4 |
Solvay Technyl® A218GV33-BK 33% Glass Filled, Heat Stabilized, Hydrolysis Resistant, Black Nylon 66 Information provided by Rhodia; Rhodia has been acquired by Solvay. |
|||
Linear Mold Shrinkage, Flow | 0.0036 cm/cm | 0.0036 in/in | SABIC Method |
SABIC Innovative Plastics LNP LUBRICOMP ZX89743 PPE+PS (Europe-Africa-Middle East) LNP* LUBRICOMP* ZX89743 is a compound based on PPE+PS Blend resin containing Glass Fiber, Glass Beads and a Proprietary Lubricant. Added features include : Internally Lubricated. |
|||
Linear Mold Shrinkage, Flow | 0.0036 cm/cm | 0.0036 in/in | ISO 204-4 |
DSM Akulon® Ultraflow K-FPG8 PA6-I-GF40 Glass Reinforced, High flow |
|||
Linear Mold Shrinkage, Flow | 0.0036 cm/cm | 0.0036 in/in | 60x60x2mm; ISO 294 |
BASF Ultradur B 4300 G6 High Speed Unc. 30% Glass Filled PBT Ultradur B 4300 G6 High Speed Unc. is a high flow, fast cycling with low warpage, 30% glass filled, pigmented black, injection molding PBT for industrial parts, rigid tough and dimensional stable ap.. |
|||
Linear Mold Shrinkage, Flow | 0.0036 cm/cm | 0.0036 in/in | TM=320°C, TW=100°C |
BASF Ultramid® KR 4357 G6 BK 00564 30% Glass Filled PA6/6T (Conditioned) Description: 30% glass-fiber reinforced, impact-modified product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechan.. |
|||
Linear Mold Shrinkage, Flow | 0.0036 cm/cm | 0.0036 in/in | TM=320°C, TW=100°C |
BASF Ultramid® KR 4357 G6 BK 00564 30% Glass Filled PA6/6T (Dry) Description: 30% glass-fiber reinforced, impact-modified product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechan.. |
|||
Linear Mold Shrinkage, Flow | 0.0036 cm/cm | 0.0036 in/in | ISO 2577, 294-4 |
BASF Ultrason® E 2010 G4 MR SW 15102 20% Glass Filled PESU Information provided by BASF |
|||
Linear Mold Shrinkage, Flow | 0.0036 cm/cm | 0.0036 in/in | ISO Data |
BASF Ultrason E 2010 G4 20% Glass Filled PES Ultrason E 2010 G4 is a 20% glass reinforced, medium viscosity injection molding PES grade with high rigidity and strength. |