Polymer Property : Linear Mold Shrinkage = 0.016 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Linear Mold Shrinkage 0.014 - 0.016 cm/cm

@Thickness 6.35 mm
0.014 - 0.016 in/in

@Thickness 0.250 in
ASTM D955
Fiberfil® PP-61/CC/20 Polypropylene Copolymer, 20% Calcium Carbonate
Information provided by FIBERFIL Engineered Plastics
Linear Mold Shrinkage 0.014 - 0.016 cm/cm

@Thickness 6.35 mm
0.014 - 0.016 in/in

@Thickness 0.250 in
ASTM D955
Fiberfil® PP-62/CC/20/UV Polypropylene Copolymer, 20% Calcium Carbonate, UV Stabilized
Information provided by FIBERFIL Engineered Plastics
Linear Mold Shrinkage 0.013 - 0.016 cm/cm

@Thickness 6.35 mm
0.013 - 0.016 in/in

@Thickness 0.250 in
ASTM D955
Fiberfil® PP-62/MI/25 Polypropylene Copolymer, 25% Mica Reinforced
Information provided by FIBERFIL Engineered Plastics
Linear Mold Shrinkage 0.0080 - 0.016 cm/cm

@Thickness 1.60 mm
0.0080 - 0.016 in/in

@Thickness 0.0630 in
horizontal; ASTM D955
Gromax PBT 2100-104B
Product Description: PBT unreinforced flame-retarded injection molding grade. Characteristics:Excellent electrical property Excellent mechanic and chemical property Excellent weatherability Excellen..
Linear Mold Shrinkage 0.011 - 0.016 cm/cm

@Thickness 3.20 mm
0.011 - 0.016 in/in

@Thickness 0.126 in
48 hr, at 121°C; ASTM D955
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound
Information provided by A. Schulman.
Linear Mold Shrinkage 0.011 - 0.016 cm/cm

@Thickness 3.20 mm
0.011 - 0.016 in/in

@Thickness 0.126 in
48 hr, at 121°C; ASTM D955
A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass)
Information provided by A. Schulman.
Linear Mold Shrinkage 0.011 - 0.016 cm/cm

@Thickness 3.20 mm
0.011 - 0.016 in/in

@Thickness 0.126 in
48 hr, at 121°C; ASTM D955
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound
Information provided by A. Schulman.
Linear Mold Shrinkage 0.011 - 0.016 cm/cm

@Thickness 3.20 mm
0.011 - 0.016 in/in

@Thickness 0.126 in
48 hr, at 121°C; ASTM D955
A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass)
Information provided by A. Schulman.
Linear Mold Shrinkage 0.011 - 0.016 cm/cm

@Thickness 3.20 mm
0.011 - 0.016 in/in

@Thickness 0.126 in
48 hr, at 121°C; ASTM D955
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound
Information provided by A. Schulman.
Linear Mold Shrinkage 0.011 - 0.016 cm/cm

@Thickness 3.20 mm
0.011 - 0.016 in/in

@Thickness 0.126 in
48 hr, at 121°C; ASTM D955
A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass)
Information provided by A. Schulman.
Linear Mold Shrinkage 0.012 - 0.016 cm/cm

@Thickness 3.20 mm
0.012 - 0.016 in/in

@Thickness 0.126 in
aged 48 hrs at 121°C; ISO 294
A. Schulman FORMION™ FI 341 Ionomer
Information provided by A. Schulman.
Linear Mold Shrinkage 0.011 - 0.016 cm/cm

@Thickness 3.20 mm
0.011 - 0.016 in/in

@Thickness 0.126 in
48 hr, at 121°C; ASTM D955
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound
Information provided by A. Schulman.
Linear Mold Shrinkage 0.011 - 0.016 cm/cm

@Thickness 3.20 mm
0.011 - 0.016 in/in

@Thickness 0.126 in
48 hr, at 121°C; ASTM D955
A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass)
Information provided by A. Schulman.
Linear Mold Shrinkage 0.012 - 0.016 cm/cm

@Thickness 3.20 mm
0.012 - 0.016 in/in

@Thickness 0.126 in
aged 48 hrs at 121°C; ISO 294
A. Schulman FORMION™ FI 341 Ionomer
Information provided by A. Schulman.
Linear Mold Shrinkage 0.011 - 0.016 cm/cm

@Thickness 3.20 mm
0.011 - 0.016 in/in

@Thickness 0.126 in
48 hr, at 121°C; ASTM D955
A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass)
Information provided by A. Schulman.
Linear Mold Shrinkage 0.012 - 0.016 cm/cm

@Thickness 3.20 mm
0.012 - 0.016 in/in

@Thickness 0.126 in
aged 48 hrs at 121°C; ISO 294
A. Schulman FORMION™ FI 341 Ionomer
Information provided by A. Schulman.
Linear Mold Shrinkage 0.012 - 0.016 cm/cm

@Thickness 3.20 mm
0.012 - 0.016 in/in

@Thickness 0.126 in
aged 48 hrs at 121°C; ISO 294
A. Schulman FORMION™ FI 341 Ionomer
Information provided by A. Schulman.
Linear Mold Shrinkage 0.011 - 0.016 cm/cm

@Thickness 3.20 mm
0.011 - 0.016 in/in

@Thickness 0.126 in
48 hr, at 121°C; ASTM D955
A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass)
Information provided by A. Schulman.
Linear Mold Shrinkage 0.012 - 0.016 cm/cm

@Thickness 3.20 mm
0.012 - 0.016 in/in

@Thickness 0.126 in
aged 48 hrs at 121°C; ISO 294
A. Schulman FORMION™ FI 341 Ionomer
Information provided by A. Schulman.
Linear Mold Shrinkage 0.012 - 0.016 cm/cm

@Thickness 3.20 mm
0.012 - 0.016 in/in

@Thickness 0.126 in
aged 48 hrs at 121°C; ISO 294
A. Schulman FORMION™ FI 341 Ionomer
Information provided by A. Schulman.
Linear Mold Shrinkage 0.012 - 0.016 cm/cm

@Thickness 3.00 mm
0.012 - 0.016 in/in

@Thickness 0.118 in
Absolute Drying
Toyobo GLAMIDE® NB-5550 Nylon/Olefin
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Linear Mold Shrinkage 0.011 - 0.016 cm/cm

@Thickness 3.20 mm
0.011 - 0.016 in/in

@Thickness 0.126 in
48 hr, at 121°C; ASTM D955
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound
Information provided by A. Schulman.
Linear Mold Shrinkage 0.010 - 0.016 cm/cm

@Thickness 1.60 mm
0.010 - 0.016 in/in

@Thickness 0.0630 in
vertical; ASTM D955
Gromax CCP PBT 3010-104 10% Glass Fiber Filled
Product Description: PBT glass fiber 10% reinforced injection molding grade.Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature Excellent..
Linear Mold Shrinkage 0.011 - 0.016 cm/cm

@Thickness 3.20 mm
0.011 - 0.016 in/in

@Thickness 0.126 in
48 hr, at 121°C; ASTM D955
A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound
Information provided by A. Schulman.