Polymer Property : Melt Index of Compound = 1.3 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Index of Compound 1.3 g/10 min

@Load 2.16 kg,
Temperature 230 °C
1.3 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
3M Dyneon™ PVDF 6020/1001 Polyvinylidene Fluoride  (discontinued **)
Ultra-high molecular weight grade PVDFPowder gradeExcellent chemical resistance to a wide variety of aggressive fluids and solventsGood permeation resistanceExcellent strength and dimensional stabil..
Melt Index of Compound 1.3 g/10 min

@Load 3.80 kg,
Temperature 230 °C
1.3 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
Lendell Parapet GR-00100 PMMA, High Impact
Melt Index of Compound 1.3 g/10 min
1.3 g/10 min
Lushan PA6+30% GF Nylon Toughener/PA Impact Modifier
Nylon toughener/PA impact modifier Lushan series is a maleic anhydride grafted polyolefin elastomer, with a very low residual maleic anhydride monomer, no irritating odor when using. Nylon toughener..
Melt Index of Compound 1.3 - 2.5 g/10 min
1.3 - 2.5 g/10 min
Sibur ABS 2802 Extrusion Grade ABS Plastic
With high deformation properties and impact strength for production of sheets with following pneumatic and vacuum forming of products of technical purpose.
Melt Index of Compound 1.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D-1238
Chevron Phillips MarFlex® 2121 Polyethylene; LDPE
Low density polyethylene. This LDPE is tailored for cast film applications that require: Good processabilityGood drawdownEdge tear resistanceLow neck-in Applications: Typical cast film applicatio..
Melt Index of Compound 1.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Dow FLEXOMER™ DFDA-1095 NT Very Low Density Polyethylene (VLDPE) Resin
FLEXOMER™ DFDA-1095 NT is an ethylene-butene copolymer with a unique olefinic composition for improved process-ability and material handling. This product is produced via gas phase polymerization ..