Polymer Property : Melt Index of Compound = 3.8 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Index of Compound 3.8 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.8 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
ICO Polymers ICORENEâ„¢ 150-1050 HDPE Rotational Molding Resin
Description: ICORENE 150-1050 polyethylene developed for use in rotational molding. It has very high stiffness, toughness, and scratch resistance combined with good processability. This product is..
Melt Index of Compound 3.8 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.8 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
ICO Polymers ICORENEâ„¢ 150-1497 HDPE Rotational Molding Resin
Description: ICORENE 150-1497 polyethylene developed for use in rotational molding. It has very high stiffness, toughness, and scratch resistance combined with good processability. Applications: Th..
Melt Index of Compound 3.8 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.8 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
ICO Polymers ICORENEâ„¢ 150-1500 HDPE Rotational Molding Resin
Description: ICORENE 150-1500 polyethylene developed for use in rotational molding. It has very high stiffness, toughness, and scratch resistance combined with good processability. This product is ..
Melt Index of Compound 3.8 g/10 min
3.8 g/10 min
ASTM D1238
Lushan L-5R (HC) Polyethylene Copolymer Adhesive for Steel Pipe Coating
Copolymer adhesive resin Lushan L-5R series is maleic anhydride grafted polyethylene which could be in granule or powder form. It was developed by Lushan with independent patent technologies and pro..
Melt Index of Compound 3.8 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.8 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Arkema Group OREVAC® 18350 Grafted Maleic Anhydride Polyethylene
OREVAC 18350 is a maleic anhydride grafted polyethylene used in the manufacturing of three layer MDPE and HDPE coating for steel pipeline. It is mainly used in pipe coating to have good adhesion per..
Melt Index of Compound 3.8 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.8 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Arkema Group OREVAC® 18350P Grafted Maleic Anhydride Polyethylene
OREVAC 18350P is a maleic anhydride grafted polyethylene used in the manufacturing of three layer MDPE and HDPE coating for steel pipeline. It is mainly used in pipe coating to have good adhesion pe..
Melt Index of Compound 3.8 g/10 min

@Temperature 230 °C
3.8 g/10 min

@Temperature 446 °F
ASTM D1238
Amco PRIMATOP PP HOMO 038X Fiber Grade Polypropylene
PP HOMO 038X features low water carryover. Applications include woven fabric and bags, rope and cordage, woven carpet backing, and woven geotextile fabrics.Former A-Top Polymers product; part of Amc..
Melt Index of Compound 3.8 g/10 min

@Load 2.16 kg,
Temperature 210 °C
3.8 g/10 min

@Load 4.76 lb,
Temperature 410 °F
ISO 1133
Arkema Group OREVAC® 18760 Grafted Maleic Anhydride Polypropylene
OREVAC 18760 is a maleic anhydride grafted polypropylene used in the manufacturing of three layer PP coating for steel pipeline. OREVAC 18760 is also used in multilayer EVOH – PP structures. OREVAC..