Polymer Property : Melt Index of Compound = 45 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Index of Compound 45 g/10 min

@Load 5.00 kg,
Temperature 190 °C
45 g/10 min

@Load 11.0 lb,
Temperature 374 °F
cm<sup>3</sup>/10 min
Huntsman IROGRAN® A 70 H 4673 M Polyester-Based TPU-Injection Molding Grade
Introduction: IROGRAN A 70 H 4673 M is a soft polyester based thermoplastic polyurethane intended for injection molding applications. IROGRAN A 70 H 4673 M is part of the HUNTSMAN injection molding ..
Melt Index of Compound 45 g/10 min

@Load 21.6 kg,
Temperature 215 °C
45 g/10 min

@Load 47.6 lb,
Temperature 419 °F
Huntsman IROGRAN® A 95 E 4861 Polyester-Based TPU-Injection Extrusion Grade
Introduction: IROGRAN A95 4861 is a high performance polyester based thermoplastic polyurethane intended for extrusion applications. IROGRAN A95E 4861 is part of the HUNTSMAN technical extrusion pro..
Melt Index of Compound 45 g/10 min

@Load 2.16 kg,
Temperature 190 °C
45 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
LG Chemical LUCEL N145-02 General Purpose POM, Unreinforced, Externally Lubricated, Ultra High Flow
LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Melt Index of Compound 45 g/10 min

@Load 2.16 kg,
Temperature 190 °C
45 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
LG Chemical LUCEL N145-AS Antistatic POM, Unreinforced, Internally Lubricated, Ultra High Flow
LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Melt Index of Compound 45 g/10 min

@Load 2.16 kg,
Temperature 250 °C
45 g/10 min

@Load 4.76 lb,
Temperature 482 °F
MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Valox® HX3061HP PBT
PBT for compounding/fibers only. Not intended for injection molding. Biocompatible. Melt viscosity: 250C at 21.6 kgf is 1450-1850 poise. Available in Natural color (1001) only.
Melt Index of Compound 45 g/10 min

@Load 1.20 kg,
Temperature 224 °C
45 g/10 min

@Load 2.65 lb,
Temperature 435 °F
ASTM D1238
Dow PELLETHANE® 2101-85A Polyurethane Elastomer (Ether-Ether Hybrid)  (discontinued **)
Description: PELLETHANE® 2101-85A offers good low temperature properties, fast cycle time, and good hydrolytic stability. Applications include: seals, gaskets, animal tags, molding applications, ho..