- Polymer Property : Melt Index of Compound = 6.0 g/10 min
Polymer Property : Melt Index of Compound = 6.0 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Index of Compound | 6.0 g/10 min @Load 5.00 kg, Temperature 190 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| Polykemi AB POLYelast TPE Z600 Thermoplastic Elastomer, SEBS-based Information provided by Polykemi AB |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Polykemi AB POLYfill PP CIP6015F Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Polykemi AB POLYfill PP CIP6020F Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics Lexan® 103 PC (Europe-Africa-Middle East) LEXAN 103 is a high viscosity U.V. stabilized multi purpose grade. LEXAN 103 is available in transparent, translucent and opaque colours. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics Lexan® EXL4016H PC Copolymer (Europe-Africa-Middle East) 6% GF reinforced opaque polycarbonate-siloxane copolymer with good impact strength, stiffness and hydrolytic stability. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics Lexan® FXD103R PC (Asia Pacific) FXD103R is a Light Diffusion effect, which is part of the VisualFX family. These effects have been developed to meet increasing Aesthetic demands in the Marketplace. Color Package may affect propert.. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 5.00 kg, Temperature 220 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics Lexan® FXD104R PC FXD104R is a Light Diffusion effect, which is part of the VisualFX family. Color Package may affect properties. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics Lexan® HP6REU PC (Europe-Africa-Middle East) Low/med flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains mold .. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics Lexan® OQ4820 PC (Europe-Africa-Middle East) LEXAN OQ4820 is a high viscosity grade with a UV cut-off up to 400 nm and a greater optical purity than standard resins. Fields of application for this material are optical lenses, f.i. in sun glass.. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics Lexan® PC0700 PC (Europe-Africa-Middle East) PC0700 resin is a low flow (MFR = 7 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release. It.. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics Lexan® 950 PC (Europe-Africa-Middle East) LEXAN 950 is a high viscosity flame retardant grade, especially suitable for electrical applications. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| ICO Polymers ICOFLOâ„¢ 510-5053 500 Micron LDPE Powder Description: ICOFLO 510-5053 is a premium polyethylene powder specifically designed to be used in the preparation of masterbatch (concentrate). By utilizing a free flowing powder as a carrier in ma.. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| ICO Polymers ICORENEâ„¢ 195-4060 LMDPE Rotational Molding Resin Description: ICORENE 195-4060 is a linear medium density polyethylene copolymer developed for rotational molding. It has a good balance of properties such as toughness, easy flow and stiffness. Key.. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics LNP LUBRICOMP DX98306H PC (Asia Pacific) LNP* Lubricomp* DX98306H is a compound based on Polycarbonate resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated, Low Extractible. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics PC0703 PC (Asia Pacific) PC0703 resin is a low flow (MFR = 7 at 300?C/1.2kg), heat and UV stabilized, polycarbonate product designed for use in the extrusion market. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 5.00 kg, Temperature 360 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics ULTEM 2300 PEI (Europe-Africa-Middle East) 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 and 5VA listing. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 5.00 kg, Temperature 360 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics ULTEM AR9300 PEI (Europe-Africa-Middle East) 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. |
|||
| Melt Index of Compound | 6.0 - 11 g/10 min | 6.0 - 11 g/10 min | |
| Sibur 21080 Superior Quality Polypropylene for Production of Syringe For production of syringe and products of complicated profile for technical and domestic purpose. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 10.0 kg, Temperature 280 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics NORYL NH8006 PPE+HIPS Noryl* NH8006 resin is a 30% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve a UL94 V0 flame rating (color specific) while offering an exceptio.. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP (Europe-Africa-Middle East) Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus .. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 2.16 kg, Temperature 300 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics NORYL PX0888 PPE+PS Unfilled, non-FR. Higher heat resistance than N110 (BOZ) and px0844 (USA). For automotive interiors. 250F (121C) DTUL. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 2.16 kg, Temperature 300 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| SABIC Innovative Plastics NORYL PX0888 PPE+PS (Asia Pacific) Unfilled, non-FR. Higher heat resistance than N110 (BOZ) and px0844 (USA). For automotive interiors. 250F (121C) DTUL. |
|||
| Melt Index of Compound | 6.0 g/10 min | 6.0 g/10 min | 2.16/190; ASTM D1238 |
| A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene DescriptionPolyaxis CP 624 is a stabilized high density polyethylene rotational molding compound with good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from.. |
|||
| Melt Index of Compound | 6.0 - 8.0 g/10 min | 6.0 - 8.0 g/10 min | 2.16/190; ASTM D1238 |
| A. Schulman POLYAXIS® LPA815 LPA 815EVA DescriptionPolyaxis LPA 815 is an EVA which is soft an pliable, even at low temperatures.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and ESCR .. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
Cond. E; ISO 1133 |
| A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer DescriptionFormion® FI 105 is a non-reinforced, transparent, injection molding grade Sodium Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and .. |
|||
| Melt Index of Compound | 6.0 - 8.0 g/10 min | 6.0 - 8.0 g/10 min | 2.16/190; ASTM D1238 |
| A. Schulman POLYAXIS® LPA815 LPA 815EVA DescriptionPolyaxis LPA 815 is an EVA which is soft an pliable, even at low temperatures.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and ESCR .. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 21.6 kg, Temperature 150 °C |
6.0 g/10 min @Load 47.6 lb, Temperature 302 °F |
Fainplast |
| Fainplast Compounds HAX HF 3622 Halogen Free PVC General purpose |
|||
| Melt Index of Compound | 6.0 - 10 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 - 10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Arkema Group OREVAC® 18732 Grafted Maleic Anhydride Polypropylene OREVAC 18732 and 18732P are maleic anhydride grafted polypropylene used in the manufacturing of multiplayer structures. These products are available in pellets or in powder. OREVAC 18732 and 18732P .. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Arkema Group LOTADER® 3430 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride LOTADER 3430 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized by high-pressure autoclave process. LOTADER 3430 is a versatile adhesive for extrusion coating or lam.. |
|||
| Melt Index of Compound | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
cm3/10 min; ISO 1133 |
| DuPont Performance Polymers Delrin® 300CP BK642 Acetal Homopolymer
(Unverified Data**) Delrin® 300CP is a medium-high viscosity acetal homopolymer with improved thermal stability and an outstanding balance of ease of processing and part performance. This black is formulated to mainta.. |
|||