Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
RheTech Products T30P200-01BG 30% Talc Reinforced Polypropylene Copolymer, Black, Blow Molding Grade Applications: HVAC ductsSeat backsFlipper panelsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
SABIC 726 Series Linear Low Density Polyethylene for Blown Film Product Description: 726 series resins are fractional index Linear Low Density Polyethylene grades suitable for blown film applications. Films produced using these resins give a relatively higher .. |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Polimeri Europa Greenflex® FF 45 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion Greenflex FF 45 is an ethylene vinyl acetate copolymer (EVA) for blown film extrusion. Films produced with Greenflex FF 45 show high toughness.Main Applications: Greenflex FF 45 is recommended for.. |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Polimeri Europa Riblene® FF 39 Low Density Polyethylene - Blown Film Extrusion Riblene FF 39 is a high molecular weight low density polyethylene (LDPE), suitable for blown film extrusion. Riblene FF 39 is characterized by a good melt strength leading to a good bubble stabilit.. |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
Condition E; ASTM D1238 |
Formosa Plastics Formolene® FORMAX® L91507A Film (Hexene Grade) LLDPE
(discontinued **) Superior Performance Linear Low Density Polyethylene for Film Extrusion Formolene FORMAX® L9 is a superior strength linear low density hexene copolymer polyethylene made using a gas-phase process. .. |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
Condition E; ASTM D1238 |
Formosa Plastics Formolene® FORMAX® L91507H Film (Hexene Grade) LLDPE
(discontinued **) Superior Performance Linear Low Density Polyethylene for Film Extrusion Formolene FORMAX® L9 is a superior strength linear low density hexene copolymer polyethylene made using a gas-phase process. .. |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
LyondellBasell Lupolex FA LLDPE Description: Lupolex 25G FA is a linear low density polyethylene (LLDPE) used for blending, film, packaging, and bagsFeatures: AntioxidantGood Puncture ResistanceHigh RigidityHigh ClarityGood Heat S.. |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Ineos H00G-00 Polypropylene Homopolymer A polypropylene homopolymer produced by Ineos utilizing catalyst technology. This material meets the Food and Drug Administration requirements of 21CFR 177.1520. Homopolymer H00G-00 meets certain .. |
|||
Melt Flow | 0.70 - 0.90 g/10 min @Load 2.61 kg, Temperature 190 °C |
0.70 - 0.90 g/10 min @Load 5.75 lb, Temperature 374 °F |
ASTM D1238 |
LG Chemical SEETEC EF320 Ethylene Vinyl Acetate Characteristics: Good Mechanical Properties and Good Optical PropertiesApplications: Agricultural FilmCAS No. 24937-78-8Information provided by LG Chemical |
|||
Melt Flow | 0.70 - 0.85 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 - 0.85 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
LG Chemical SEETEC PM360 HDPE Features: Characteristics: Excellent processability, Good tenacity & knot strengthAdditives: Anti-oxidants, LubricantsApplication: Tarpaulin, Woven bags (Inflation)CAS No. 25213-02-9Information prov.. |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Iran Petrochemical (PCC) 235F7 Linear Low Density Polyethylene 235F7 is a LLDPE blown film grade designed for general purpose film application. This resin is particularly suited for blending with LDPE, giving better strength and downgauging possibility.Informat.. |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Borealis HE4872 High Density Polyethylene HE4872 is a HDPE compound for solid insulation of symmetric data cable at high extrusion speed. Applications: high frequency data transmission cables, outer skin of foam-skin constructions. Specif.. |
|||
Melt Flow | 0.70 g/10 min | 0.70 g/10 min | Condition not noted.; ASTM D1238 |
DuPont Elvax® 3165 Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion, Blown Film 18 wt% Vinyl Acetate.Elvax® 3165 is an extrudable ethylene-vinyl acetate copolymer resin available in pellet form for use in conventional extrusion equipment designed to process polyethylene resins.. |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Total Lumicene® mPE M 4707 EP Metallocene Polyethylene, Blown Film This product is a Total Ecosolutions grade.Lumicene® mPE M 4707 EP is a second generation metallocene based High Density Polyethylene with hexene as comonomer.Lumicene® mPE M 4707 EP can be proces.. |
|||
Melt Flow | 0.70 - 2.0 g/10 min | 0.70 - 2.0 g/10 min | ASTM D1238 |
A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman. |
|||
Melt Flow | 0.70 - 2.0 g/10 min | 0.70 - 2.0 g/10 min | ASTM D1238 |
A. Schulman POLYFLAM™ E-14526-31 30% Glass Reinforced Chemically Coupled Polypropylene DescriptionPolyfort® E-14526-31 is a 30% glass reinforced chemically coupled polypropylene black. Information provided by A. Schulman. |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
condition E; ASTM D1238 |
DuPont™ Surlyn® 9910 Ionomer Resin, Zinc Surlyn® 9910 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr.. |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil LDPE LD 071.LQ Low Density Polyethylene Resin Product Description: LD 071 Series case wrap film resins combine good processability with excellent strength and good film optics for bundling applications requiring proper shrink performance, tough.. |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil LLDPE LL 1201KG Linear Low Density Polyethylene Resin (European Grade) Product Description: LL 1201 series are LLDPE grades, offering excellent combination of stiffness and optical properties (when blended with 10-20% LDPE) Availability: Africa & Middle East, Asia Paci.. |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Entec Hypel® PEHD.7/.962 HDPE Available in North America Features: Food Contact Acceptable and High DensityAgency Ratings: FDA 21 CFR 177.1520RoHS Compliant Form: Pellets Information provided by Entec |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Braskem EB861 Blown Film Extrusion Low Density Polyethylene Medium-resistance films for general use; Mulching films; Shrink films; Coextrusion.Information provided by Braskem. |
|||
Melt Flow | 0.70 g/10 min | 0.70 g/10 min | ASTM D1238 |
Aclo Accutech ABS ABS831G30L Glass Reinforced |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Braskem LF 0720/20 AF LLDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 40mm extruder, with blow up ratio 2, 2:1Applications: Heavy duty bags; "liners"; general purpose; HDPE and LDPE blends. Information provided by Braskem |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Braskem LF0720/21AF Blown Film Extrusion Linear Low Density Polyethylene Description: LF0720/21AF is a LLDPE Butene copolymer produced using Unipol® process technology. It shows low haze and high clarity associated with good balance of mechanical properties, processing .. |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Bapolene® 0760 Polyethylene, Blow Molding Grade This resin is a high density polyethylene homopolymer for blow molding applications. It is recommended for applications that require high top load strength and good stiffness. This product meets 2.. |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Bapolene® 152F Polyethylene Film Grade Bapolene 152F is a hexene linear low density polyethylene with a combination of superior impact strength and HSIT. Product is designed to exhibit performance similar to that of metallocene products... |
|||
Melt Flow | 0.70 g/10 min @Load 21.6 kg, Temperature 190 °C |
0.70 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
Braskem Idealis 500 High Molecular Weight Polyethylene Powder Braskem Idealis 500 is the only High Molecular Weight Polyethylene resin in powder form specially designed for the compression molding process; Applications range from food handling cutting boards a.. |
|||
Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238, ISO 1183 |
DuPont™ Surlyn® 1706 Zinc Ionomer Surlyn® 1706 is available for use in conventional blown, cast film, and sheet extrusion equipment. It is also used in coextrusion equipment designed to process polyethylene and ethylene copolymer t.. |