Polymer Property : Melt Flow = 2.8 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	2.8 g/10 min @Load 3.80 kg, Temperature 230 °C	2.8 g/10 min @Load 8.38 lb, Temperature 446 °F	ASTM D-1238
Plaskolite West Optix® CA - 1000 I High Impact Acrylic Resin Optix® impact-modified grades exhibit 7 to 10 times the impact strength of general purpose grades and maintaining the superior optical properties. Each grade is offered in a grade(G) that resists g..
Melt Flow	2.8 g/10 min @Load 2.16 kg, Temperature 190 °C	2.8 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
SABIC 6318B Linear Low Density Polyethylene for Cast Film Product Description: 6318B is a hexene copolymer Linear Low Density Polyethylene grade designed to provide easy processability and specially formulated for optimum thermal stability at high process..
Melt Flow	2.8 g/10 min @Load 2.16 kg, Temperature 190 °C	2.8 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
SABIC 318CN Linear Low Density Polyethylene for Wire & Cable Product Description: 318CN is a Linear Low Density Polyethylene natural resin for wire and cable applications. It contains a low level of antioxidants and does not contain any slip or antiblock a..
Melt Flow	2.8 g/10 min @Load 5.00 kg, Temperature 200 °C	2.8 g/10 min @Load 11.0 lb, Temperature 392 °F
Total Lacqrene® 1250 Crystal Polystyrene (discontinued **) LACQRENE® 1250 is a very high molecular weight crystal polystyrene mainly for the injection molding industry. It is characterized by a very good compromise between molecular weight, heat resistanc..
Melt Flow	2.8 g/10 min @Load 2.16 kg, Temperature 230 °C	2.8 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
Ineos H03G-03 Polypropylene Homopolymer (discontinued **) Suggested fabrication methods: ExtrusionFeatures: Ease of processingTypical applications: Oriented filmComplies with FDA specification, Title 21, CFR 177.1520.Typical property data below from inject..
Melt Flow	2.8 g/10 min @Load 5.00 kg, Temperature 200 Â°C	2.8 g/10 min @Load 11.0 lb, Temperature 392 Â°F	Condition G; ASTM D1238
Global 121-PC-Blue Acrylonitrile Styrene, General Purpose Grade Description-transparent, blue, medium impact resistance, high hardness, good stiffness, high heat resistance, good chemical resistanceApplications-automotive, electrical parts, household goodsInform..
Melt Flow	2.8 g/10 min @Load 5.00 kg, Temperature 200 Â°C	2.8 g/10 min @Load 11.0 lb, Temperature 392 Â°F	ASTM D1238
Ineos Styrenics Polystyrene 486N (NAFTA) High-impact grade of polystyrene with excellent ESCR.Information provided by BASF.Ineos Styrenics purchased this product line from BASF in 2005.
Melt Flow	2.8 g/10 min @Load 5.00 kg, Temperature 200 Â°C	2.8 g/10 min @Load 11.0 lb, Temperature 392 Â°F	ASTM D1238
IRPC Polimaxx Polene 121PC Styrene Acrylonitrile APPLICATIONS: INJECTION MOLDING, HOUSEHOLD PRODUCTS : SANITARY WARE, AUTOPART APPLICATION : LAMP ELECTRICAL APPLIANCES : ELECTRICAL FAN
Melt Flow	2.8 g/10 min	2.8 g/10 min
KratonÂ® D1102 + PP blend (10/90) Unmodified polypropylene has high rigidity and good heat resistance, but poor impact resistance, especially at low temperatures. Blending KRATON D and G polymers with PP significantly improves the ..
Melt Flow	2.8 g/10 min @Load 5.00 kg, Temperature 200 Â°C	2.8 g/10 min @Load 11.0 lb, Temperature 392 Â°F	ASTM D1238
IRPC Polimaxx Polene 320PC Styrene Acrylonitrile APPLICATIONS: INJECTION MOLDING, HOUSEHOLD PRODUCTS : SANITARY WARE, AUTOPART APPLICATION : LAMP ELECTRICAL APPLIANCES : ELECTRICAL FAN
Melt Flow	2.8 g/10 min @Load 2.16 kg, Temperature 230 °C	2.8 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Borealis Borcoat™ MA115E Syntactic Polypropylene for Steel Pipe Coating Borcoat™ MA115E is a highly filled polypropylene compound and is self colored. Applications: Borcoat™ MA115E is recommended as heavy weight coating for special applications used in steel pipe coa..
Melt Flow	2.8 g/10 min @Load 2.16 kg, Temperature 230 °C	2.8 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Borealis Bormod™ HC905TF Polypropylene Homopolymer for Thermoforming Bormod HC905TF is a low melt flow rate polypropylene homopolymer intended for thermoformed packaging applications. This homopolymer is produced using the Borealis Controlled Crystallinity Polypropy..
Melt Flow	2.8 g/10 min @Load 2.16 kg, Temperature 230 °C	2.8 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Borealis HC207TF Polypropylene Homopolymer HC207TF is a special nucleated polypropylene homopolymer intended for thermoforming packaging. Applications: HC207TF is recommended for in-line and off line thermoforming, high transparent trays, c..
Melt Flow	2.8 g/10 min @Load 2.16 kg, Temperature 230 °C	2.8 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Borealis HC600TF Polypropylene HC600TF is a polypropylene homopolymer intended for thermoformed packaging applications. Its very good organoleptic properties allows this grade to be used with any masterbatch without discoloring ..
Melt Flow	2.8 g/10 min @Load 2.16 kg, Temperature 190 °C	2.8 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Borealis SuperCOPO™ LH4201R Polyethylene Insulation Compound, Crosslinkable SuperCOPO™ LH4201R is a crosslinkable natural polyethylene compound, specially designed for insulation applications. Applications: SuperCOPO™ LH4201R is intended for insulation of XLPE power cabl..
Melt Flow	2.8 g/10 min @Load 2.16 kg, Temperature 230 °C	2.8 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Polyram Bondyram® TL1306 Maleic Anhydride Modified Polypropylene Information provided by Polyram.
Melt Flow	2.8 g/10 min @Load 5.00 kg, Temperature 200 °C	2.8 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D1238
Total Impact Polystyrene 940E Super High Impact Polystyrene, Sheet Extrusion and Thermoforming Grade TOTAL Petrochemicals 940E is a super high impact polystyrene designed for high gloss sheet extrusion and thermoforming applications that require additional toughness.Applications: The combination o..
Melt Flow	2.8 g/10 min @Load 2.16 kg, Temperature 190 °C	2.8 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Polyram RamTal PMH2003 Polyacetal Homopolymer for Injection Molding General purpose polyacetal homopolymer for injection molding applications, MFI 3.Information provided by Polyram.
Melt Flow	2.8 g/10 min @Load 5.00 kg, Temperature 200 °C	2.8 g/10 min @Load 11.0 lb, Temperature 392 °F	ISO 1133 H
Total Polystyrene Impact 8260 Improved Environmental Stress Crack Resistance High Impact Polystyrene POLYSTYRENE IMPACT 8260 is a high impact polystyrene for extrusion and injection applications. This grade has an improved environmental stress crack resistance in comparison with standard high impa..
Melt Flow	2.8 g/10 min @Load 5.00 kg, Temperature 200 °C	2.8 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D1238
Total PSI 940E Impact Polystyrene Description: 940E is a super high impact polystyrene designed for high gloss sheet extrusion and thermoforming applications that require additional toughness.Applications: The combination of high gl..
Melt Flow	2.8 g/10 min @Load 2.16 kg, Temperature 190 °C	2.8 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
ExxonMobil LLDPE LL 1004YB Film Linear Low Density Polyethylene Resin (European Grade) Product Description: LL 1004YB is an LLDPE grade, offering excellent high temperature stability. Properties may be further enhanced by the combination with Exceed mLLDPE. Availability: Africa & Midd..
Melt Flow	2.8 g/10 min	2.8 g/10 min	ASTM D1238
Aclo Accucomp ABS ABS810L Medium Impact Grade
Melt Flow	2.8 g/10 min @Load 5.00 kg, Temperature 200 °C	2.8 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D1238
Americas Styrenics STYRON® 484 High Impact Polystyrene Product CharacteristicsToughnessHeat resistanceGood stiffnessFood Contact CompliantUL Classification 94HBTypical ApplicationsLidsAppliances/RefrigerationPackaging/disposablesHousewaresInformation pr..
Melt Flow	2.8 g/10 min @Load 5.00 kg, Temperature 200 °C	2.8 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D1238
Total PSI 975E Polystyrene Polystyrene 975E is a high impact polystyrene designed for extrusion/thermoforming applications. The food ESCR properties of 975E dictate its use for dairy applications that are subjected to high bu..
Melt Flow	2.8 g/10 min @Load 5.00 kg, Temperature 230 °C	2.8 g/10 min @Load 11.0 lb, Temperature 446 °F
Arkema Group Kynar® FLEX 2822 PVDF (discontinued **) Designation ISO 12086-VDF/HFP-K, EDN, N. ?E5.C.H.B.C,, ? (4-8)Kynar FLEX PVDF are fluorinated thermoplastic copolymers.Outstanding characteristics of Kynar FLEX: chemical resistance, imperviousness ..
Melt Flow	2.8 g/10 min	2.8 g/10 min
UBE A (High-Cis) HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %) Description: UBE high impact polystyrene (HIPS).Information provided by UBE.
Melt Flow	2.8 g/10 min	2.8 g/10 min
UBE UBEPOL BR15HB HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %) Description: UBEPOL-BR15HB is characterized by the highest branching of these 3 grades and is adapted by many PS manufacturers.Information provided by UBE.
Melt Flow	2.8 g/10 min @Load 3.80 kg, Temperature 230 °C	2.8 g/10 min @Load 8.38 lb, Temperature 446 °F	ASTM D-1238
Plaskolite West Optix® CP - 1000 I High Impact Acrylic Resin Optix® impact-modified grades exhibit 7 to 10 times the impact strength of general purpose grades and maintaining the superior optical properties. Each grade is offered in a grade(G) that resists g..
Melt Flow	2.8 g/10 min @Load 3.80 kg, Temperature 230 °C	2.8 g/10 min @Load 8.38 lb, Temperature 446 °F
Arkema Group Oroglas® SG 10 Acrylic, Gamma Radiation Resistant (discontinued **) OROGLAS SG 10 is special Gamma - radiation - resistant formulation designed for use in medical devises.OROGLAS SG 10 maintains exceptional clarity after 5 megarads of Gamma radiation with no advers..
Melt Flow	2.8 g/10 min	2.8 g/10 min	Exxon Method
ExxonMobil Iotek® 8030 Sodium Ionomer Molding/Extrusion Resin (discontinued **) Data provided by the manufacturer, Exxon Chemical.Excellent abrasion resistance, impact strength, hardness, and tensile strength. Iotek ionomers provide superb low temperature impact strength when ..