Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 21 g/10 min @Load 5.00 kg, Temperature 300 °C |
21 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
PTS PPE-LXS 314-10 PPE-HIPS, 10% Glass Filled Typical Applications: Water industrial partsInformation provided by PTS LLC. |
|||
Melt Flow | 21 g/10 min @Load 1.20 kg, Temperature 300 °C |
21 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
SABIC Innovative Plastics Lexan® FXD124R PC (Europe-Africa-Middle East) LEXAN FXD124R is a transparent/translucent low viscosity grade for light diffusion special effects. FDA compliant. Color package may affect performance.This data was supplied by SABIC-IP for the Eu.. |
|||
Melt Flow | 21 g/10 min @Load 5.00 kg, Temperature 200 °C |
21 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
PolyOne Dynaflex™ G7670-1 (Natural) Thermoplastic Elastomer (TPE) Dynaflex™ G7670-1 (Natural) is an easy processing, general purpose TPE designed for a wide variety of applications, including those where FDA compliance is required. - Overmold Adhesion to Polyprop.. |
|||
Melt Flow | 21 g/10 min | 21 g/10 min | ISO 1133 |
Solvay Engineered Polymers SEQUEL® 1440LS TPO
(discontinued **) Description: SEQUEL® 1440LS engineered polyolefin material is designed for large automotive exterior applications that require ductile impact properties at low temperatures, excellent processabilit.. |
|||
Melt Flow | 21 g/10 min @Load 10.0 kg, Temperature 250 °C |
21 g/10 min @Load 22.0 lb, Temperature 482 °F |
|
Lehmann & Voss LUVOCOM® 1850/CF/10/GF/10/GK/10/GS/5/FR PBT, with carbon fiber, glass fiber, glass spheres and glass flakes, fire protection Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance r.. |
|||
Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 250 °C |
21 g/10 min @Load 4.76 lb, Temperature 482 °F |
|
Lehmann & Voss LUVOCOM® 1850-7942/RD PBT, with PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
Melt Flow | 21 g/10 min | 21 g/10 min | ASTM D1238 |
LyondellBasell Petrothene® GA564189 Linear Low Density Polyethylene, Injection Molding Grade PETROTHENE GA564189 exhibits good stiffness and low temperature toughness. Typical applications include trash cans, industrial containers, housewares and toys. Regulatory Status: GA564189 meets the .. |
|||
Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 280 °C |
21 g/10 min @Load 4.76 lb, Temperature 536 °F |
ISO 1133-1 |
Lanxess Pocan® DP T 7140 LDS 000000 PET + PBT, 42% Glass Fiber/Mineral PET + PBT, 44% glass fibers/mineral, injection molding, LDS, high thermal dimensional stabilityInformation provided by LANXESS. |
|||
Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 230 °C |
21 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
LG Chemical LUPOL MC4352 PP+Rubber+MF Description: Injection Molding, PP+Rubber+MF, Good Dimensional Stability, Scratch resistance, Good Weatherability, High ImpactApplication: Automotive Exterior (Sill Side Molding, Door Garnish)CAS: 9.. |
|||
Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 265 °C |
21 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
SABIC Innovative Plastics XYLEX X7300 PC+POLYESTER PC+POLYESTER unreinforced alloy. High flow, chemically resistant with excellent optical quality. UV-stabilized. |
|||
Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 265 °C |
21 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
SABIC Innovative Plastics XYLEX X7300 PC+POLYESTER (Europe-Africa-Middle East) PC+POLYESTER unreinforced alloy. High flow, chemically resistant with excellent optical quality. UV-stabilized. |
|||
Melt Flow | 21 g/10 min @Load 5.00 kg, Temperature 260 °C |
21 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
Samsung Cheil Industries Infino® AE-2130 PC/PET, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Melt Flow | 21 g/10 min @Load 10.0 kg, Temperature 220 °C |
21 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
Samsung Cheil Industries Starex® LX-0981 ABS, Unreinforced Metallic-Look Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries. |
|||
Melt Flow | 21 g/10 min | 21 g/10 min | ASTM D1238 |
Samyang Trimma® FT6125 I[R] PMMA, Transparent High transparency and high scratch resistance. Stable against weak acids, strong acids, weak alkalis and inorganic salts.Information provided by Samyang. |
|||
Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 260 °C |
21 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
SABIC Innovative Plastics NORYL N802 PPE+HIPS (Asia Pacific) PPE/PS 80oC V2 FR high flow |
|||
Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 230 °C |
21 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Borealis HF700SA Polypropylene HF700SA is a polypropylene homopolymer intended for injection molding. This material has excellent balanced mechanical properties and is easy to process. Applications: household applications.Infor.. |
|||
Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 190 °C |
21 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
A. Schulman POLYBATCH™ Red 5500 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 5500 is a red color concentrate based in polyethylene. This concentrate was designed to provide color in polyolefin film and molding applications. POLYBATCH® 5500 is heavy .. |
|||
Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 190 °C |
21 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
A. Schulman POLYBATCH™ Cedar 10310U Concentrate Based In LLDPE DescriptionPOLYBATCH® Cedar 10310U is a cedar color concentrate containing an optimized blend of color and UV stabilizer based in LLDPE. This concentrate was designed to provide color and UV stabi.. |
|||
Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 190 °C |
21 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
A. Schulman POLYBATCH™ Red 5500 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 5500 is a red color concentrate based in polyethylene. This concentrate was designed to provide color in polyolefin film and molding applications. POLYBATCH® 5500 is heavy .. |
|||
Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 190 °C |
21 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
A. Schulman POLYBATCH™ Red 5500 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 5500 is a red color concentrate based in polyethylene. This concentrate was designed to provide color in polyolefin film and molding applications. POLYBATCH® 5500 is heavy .. |
|||
Melt Flow | 21 g/10 min @Load 5.00 kg, Temperature 260 °C |
21 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
Goodfellow TPX® RT31 Injection Molding Grade Polymethylpentene This grade is highly recommended for injection molding; also for film and fiber extrusion.TPX® is semi-crystalline, transparent, very light and - for a polyolefin - expensive. It has good release c.. |
|||
Melt Flow | 21 g/10 min @Load 1.20 kg, Temperature 300 °C |
21 g/10 min @Load 2.65 lb, Temperature 572 °F |
estimated from MVR using room temperature density; ISO 1133 |
Covestro Makrolon® GF8001* Polycarbonate, 20% Glass Filled ISO 7391-PC,MR,(,,)-18-3,GF20Developmental productFormerly Makrolon DP1-1951MVR (300 °C/1.2 kg) 16 cm3/10 min20 % Glass fiber reinforcedLow viscosityEasy releaseInjection molding - Melt temperature.. |
|||
Melt Flow | 21 g/10 min | 21 g/10 min | ASTM D1238 |
Aclo Accutech Polypropylene Homopolymer HP0339C40L Calcium Reinforced |
|||
Melt Flow | 21 g/10 min | 21 g/10 min | ASTM D1238 |
Aclo Accutech Polypropylene Homopolymer HP0339W40L Wollastonite Reinforced |
|||
Melt Flow | 21 g/10 min | 21 g/10 min | ASTM D1238 |
Aclo Accutech Polypropylene Homopolymer HP0339W40L1 Wollastonite Reinforced |
|||
Melt Flow | 21 g/10 min @Load 5.00 kg, Temperature 300 °C |
21 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
BLUESTAR LXS 314 G10 PPE-HIPS, 10% Glass Filled Typical Applications: Water industrial partsInformation provided by Polymer Technology and Services, LLC (PTS). |
|||
Melt Flow | 21 g/10 min | 21 g/10 min | ASTM D1238 |
Aclo Accutech Polypropylene Homopolymer HP0339T40L Talc Reinforced |
|||
Melt Flow | 21 g/10 min | 21 g/10 min | ASTM D1238 |
Aclo Accutech Polypropylene Homopolymer HP0339W30L Wollastonite Reinforced |
|||
Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 230 °C |
21 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene DescriptionPolyfort® FPP 1876 is a 22% mineral filled copolymer UV Inhibited Polypropylene. It is high flow. Information provided by A. Schulman. |
|||
Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 190 °C |
21 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
A. Schulman POLYBATCH™ Red 5500 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 5500 is a red color concentrate based in polyethylene. This concentrate was designed to provide color in polyolefin film and molding applications. POLYBATCH® 5500 is heavy .. |