Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Linear Mold Shrinkage, Flow 0.0013 - 0.0018 cm/cm

@Time 86400 sec
0.0013 - 0.0018 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP LUBRICOMP OFL36 PPS - Branched (Asia Pacific)
LNP LUBRICOMP* OFL36 is a compound based on PPS - Branched resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow 0.0013 - 0.0018 cm/cm

@Time 86400 sec
0.0013 - 0.0018 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP LUBRICOMP OFL36 PPS - Linear
LNP* LUBRICOMP* OFL36 is a compound based on PPS - Linear resin containing 30% Glass Fiber, 15% PTFE. Added features of this grade include: Wear Resistant.
Linear Mold Shrinkage, Flow 0.0013 - 0.0018 cm/cm

@Time 86400 sec
0.0013 - 0.0018 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP LUBRICOMP OFL36A PPS - Branched
LNP* LUBRICOMP* OFL36A is a compound based on PPS - Branched resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
Linear Mold Shrinkage, Flow 0.0013 - 0.0018 cm/cm

@Time 86400 sec
0.0013 - 0.0018 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP LUBRICOMP OFL36A PPS - Branched (Europe-Africa-Middle East)
LNP LUBRICOMP* OFL36 is a compound based on PPS - Branched resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow 0.0013 - 0.0018 cm/cm

@Time 86400 sec
0.0013 - 0.0018 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP LUBRICOMP OFL36A PPS (Asia Pacific)
LNP* Lubricomp* OFL36A is a compound based on Polyphenylene Sulfide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow 0.0013 - 0.0018 cm/cm

@Time 86400 sec
0.0013 - 0.0018 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP LUBRICOMP OFL36XXC PPS - Linear
LNP* LUBRICOMP* OFL36XXC is a compound based on PPS - Linear resin containing 30% Glass Fiber, 15% PTFE. Added features of this grade are: Wear Resistant.
Linear Mold Shrinkage, Flow 0.0016 - 0.0018 cm/cm

@Thickness 1.00 mm
0.0016 - 0.0018 in/in

@Thickness 0.0394 in
Solvay Specialty Polymers Amodel® FC-1140 Polyphthalamide (PPA), 40% Glass Fiber
Amodel® FC-1140 is an FDA-approved, 40% glass fiber reinforced resin designed for high strength and stiffness. This combines with its excellent thermal properties, low water absorption and good h..
Linear Mold Shrinkage, Flow 0.0015 - 0.0018 cm/cm

@Thickness 2.00 mm
0.0015 - 0.0018 in/in

@Thickness 0.0787 in
Solvay Specialty Polymers Amodel® FC-1150 Polyphthalamide (PPA), 50% Glass Fiber
Amodel® FC-1150 is an FDA-approved, 50% glass fiber reinforced resin designed for high strength and stiffness. This combines with its excellent thermal properties, low water absorption and good h..
Linear Mold Shrinkage, Flow 0.0017 - 0.0018 cm/cm

@Time 86400 sec
0.0017 - 0.0018 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP THERMOCOMP QF006 PA 6/10
LNP THERMOCOMP* QF006 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber.