Polymer Property : Linear Mold Shrinkage, Flow = 0.0039 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Flow	0.0039 cm/cm @Time 86400 sec	0.0039 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP STAT-KON DD0001 PC LNP STAT-KON* DD0001 is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant.
Linear Mold Shrinkage, Flow	0.0039 cm/cm @Time 86400 sec	0.0039 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP STAT-KON DD0001 PC (Asia Pacific) LNP STAT-KON* DD0001 is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0039 cm/cm @Time 86400 sec	0.0039 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP STAT-KON DD0001 PC (Europe-Africa-Middle East) LNP STAT-KON* DD0001 is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0039 - 0.0056 cm/cm @Time 86400 sec	0.0039 - 0.0056 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP STAT-KON WE002 PBT LNP STAT-KON* WE002 is a compound based on PBT resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0039 - 0.0056 cm/cm @Time 86400 sec	0.0039 - 0.0056 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP STAT-KON WE002 PBT (Asia Pacific) LNP STAT-KON* WE002 is a compound based on Polybutylene Terephalate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Flow	0.0039 cm/cm @Time 86400 sec	0.0039 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP Thermocomp RFZ349 PA 66 (Asia Pacific) LNP* Thermocomp* RFZ349 is a compound based on Nylon 66 resin containing Glass Fiber, Milled Glass. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP for t..
Linear Mold Shrinkage, Flow	0.0039 cm/cm @Time 86400 sec	0.0039 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP RFZ349XC PA 66 LNP THERMOCOMP* RFZ349XC is a compound based on Nylon 66 resin containing 20% Glass Fiber, 15% Milled Glass. Added features of this material include: Flame Retardant.
Linear Mold Shrinkage, Flow	0.0039 cm/cm @Time 86400 sec	0.0039 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP STAT-LOY WF306C PBT LNP* STAT-LOY* WF306C is a compound based on PBT resin containing 30% Glass Fiber. Added features of this material include: Antistat, Clean Compound System.
Linear Mold Shrinkage, Flow	0.0039 cm/cm @Time 86400 sec	0.0039 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP STAT-LOY WF306C PBT (Asia Pacific) LNP* Stat-loy* WF306C is a compound based on Polybutylene Terephalate resin containing Glass Fiber. Added features of this material include: Antistat, Clean Compounding System.
Linear Mold Shrinkage, Flow	0.0039 cm/cm @Time 86400 sec	0.0039 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP RFZ349XC PA 66 (Asia Pacific) LNP* THERMOCOMP* RFZ349XC is a compound based on Nylon 66 resin containing Glass Fiber, Milled Glass. Added features of this material include: Flame Retardant.