Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 80.0 MPa | 11600 psi | ISO 527-1 |
Murtfeldt Murlubric® [FS] Oil Modified Nylon 6 Murlubric® is a modified cast polyamide that mineral oil is integrated into during polymerization. As a result, the material has self lubricating properties and retains its excellent characteristi.. |
|||
Tensile Strength | 80.0 MPa | 11600 psi | ASTM D638 |
Premix Premi-Glas® 2200-30 CR-SX Fiberglass Reinforced SMC Description: Premi-Glas® 2200-30 CR-SX is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal .. |
|||
Tensile Strength | 80.0 MPa | 11600 psi | ASTM D638 |
Premix Premi-Glas® 2203-30 CR-SX Fiberglass Reinforced SMC Description: Premi-Glas® 2203-30 CR-SX is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal .. |
|||
Tensile Strength | 80.0 MPa | 11600 psi | ASTM D638 |
Premix Premi-Glas® 2204-30 CR-SX Fiberglass Reinforced SMC Description: Premi-Glas® 2204-30 CR-SX is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal .. |
|||
Tensile Strength | 80.0 MPa | 11600 psi | ASTM D638 |
Premix Premi-Glas® 2205-30 CR-SX Fiberglass Reinforced SMC Description: Premi-Glas® 2205-30 CR-SX is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal .. |
|||
Tensile Strength | 80.0 MPa | 11600 psi | ASTM D638 |
Premix Premi-Glas® 3200-30 Fiberglass Reinforced SMC Description: Premi-Glas® 3200-30 is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal and di.. |
|||
Tensile Strength | 80.0 MPa | 11600 psi | at Yield; ISO 527-1/-2 |
Quadrant EPP Ertalon® 6 SA PA 6, extruded (ISO Data) This material offers an optimal combination of mechanical strength, stiffness, toughness, mechanical damping properties and wear resistance. These properties, together with good electrical insulatin.. |
|||
Tensile Strength | 80.0 MPa | 11600 psi | at Yield; ISO 527-1/-2 |
Quadrant EPP Nylatron® NSM PA 6 + internal lubricant, cast (ISO Data) Nylatron NSM is a proprietary cast nylon 6 formulation containing solid lubricant additives which grant this materials self-lubricity, excellent frictional behaviour, superior wear resistance and ou.. |
|||
Tensile Strength | 80.0 MPa | 11600 psi | DIN 53455 |
Isoflon PA 6.6 Polyamide 6.6 General use for mechanical partsGood heat resistanceEasy to useHigh moisture regainInformation provided by Isoflon. |
|||
Tensile Strength | 80.0 MPa | 11600 psi | DIN 53455 |
Isoflon PETP Polyethylene terephthalate Good optical propertiesHigh UV resistanceAbsorbs little moistureInformation provided by Isoflon. |
|||
Tensile Strength | 80.0 MPa | 11600 psi | ISO 527 |
Lucite International Diakon® CLG902 Acrylic Polymer Information provided by Lucite International |
|||
Tensile Strength | 80.0 MPa | 11600 psi | ISO 527 |
Lucite International Diakon® CLG902LX Acrylic Polymer Information provided by Lucite International |
|||
Tensile Strength | 80.0 MPa | 11600 psi | ISO 527 |
Lucite International Diakon® CMG302 Acrylic Polymer Information provided by Lucite International |
|||
Tensile Strength | 80.0 MPa | 11600 psi | ISO 527 |
Lucite International Diakon® Frost 902 51 Acrylic Polymer Information provided by Lucite International |
|||
Tensile Strength | 80.0 MPa | 11600 psi | ISO 527 |
Lucite International Diakon® LG702 Acrylic Bead Polymer, High Transparency PMMA beads offer an exceptional transmission level of 92.5%, an increase of +0.5% in light transmission vs. granular grades - ideal for medical diagnostic devices.Information provided by Lucite Inte.. |
|||
Tensile Strength | 80.0 MPa | 11600 psi | ISO 527 |
Lucite International Diakon® MG100 Acrylic Bead Polymer, High Transparency PMMA beads offer an exceptional transmission level of 92.5%, an increase of +0.5% in light transmission vs. granular grades - ideal for medical diagnostic devices.Information provided by Lucite Inte.. |
|||
Tensile Strength | 80.0 MPa | 11600 psi | ISO 527 |
Solvay Technyl® C50H2 Nylon 6, Flame Retardant, Heat Stabilized Information provided by Rhodia; Rhodia has been acquired by Solvay. |
|||
Tensile Strength | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527-1 |
Sax Polymers SAXAMID 136F4Q32 Nylon 6, 20% Glass Fiber SAXAMID 136F4Q32 is a high impact-modified polyamide 6 injection-molding-grade reinforced with 20% glass fibers.Information provided by SAX Polymers |
|||
Tensile Strength | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527-1 |
Sax Polymers SAXAMID 226K6 Nylon 6.6, 30% Glass Beads SAXAMID 226K6 is a polyamide 6.6 injection-molding-grade filled with 30% glass beads. It is characterized by optimized shrinkage properties.Information provided by SAX Polymers |
|||
Tensile Strength | 80.0 MPa @Thickness >=1.50 mm |
11600 psi @Thickness >=0.0591 in |
24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6 |
Elektro-Isola Etronax MF Phenolic, Cotton Fabric Reinforcement, Brown, Sheets Description: Exclusively for mechanical applications. Impact-resistant, resistant to mechanical wear, noise-reducing, low friction. Well suited for parts where there are high mechanical load and wea.. |
|||
Tensile Strength | >= 80.0 MPa | >= 11600 psi | IEC 1212-2 5.7 |
Hippe PF CC 204 Woven Cotton Cloth Reinforced Phenolic Resin - Sheet Used in mechanical and electrical applications (fine weave: =130 g/m2, >30 threads/cm). Recommended for small parts.Information provided by Hippe. |
|||
Tensile Strength | >= 80.0 MPa | >= 11600 psi | IEC 1212-2 5.7 |
Hippe PF CC 201 Woven Cotton Cloth Reinforced Phenolic Resin - Sheet Used in mechanical applications (coarse weave: >130 g/m2, =30 threads/cm). Better mechanical properties and poorer electrical properties than type PF CC 202.Information provided by Hippe. |
|||
Tensile Strength | 80.0 MPa | 11600 psi | ISO 527 |
Azoty Tarnow™ Tarnamid® T-27 MCS V2 Polyamide 6 - Flame Retarded, Unreinforced Flame retarded (class V2), bromine and red phosphorus free, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has th.. |
|||
Tensile Strength | 80.0 MPa | 11600 psi | ISO 527 |
Azoty Tarnow™ Tarnamid® T-27 GF20 FRV2 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grade, flammability class V2, reinforced with 20% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning... |
|||
Tensile Strength | 80.0 MPa | 11600 psi | ISO 527 |
Azoty Tarnow™ Tarnamid® T-27 MCS 850 Polyamide 6 - Flame Retarded, Unreinforced Glow wire resistance 850°C, bromine and red phosphorus free, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has .. |
|||
Tensile Strength | 80.0 MPa | 11600 psi | at Yield; ISO 527-1/-2 |
Quadrant EPP Ketron® GF30 PEEK + glassfibres, extruded (ISO Data) This 30 % glass fibre reinforced grade offers a higher stiffness and creep resistance than Ketron PEEK-1000 and has a much better dimensional stability. This grade is very appropriate for structural.. |