Polymer Property : Tensile Strength = 12300 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength 85.0 MPa
12300 psi
at Yield; ISO 527-1/-2
Quadrant EPP Ertalon® 66 GF30 PA 66, 30% glass filled, extruded (ISO Data)
Compared with virgin PA 66, this 30 % glass fibre reinforced and heat stabilised nylon grade offers increased strength, stiffness, creep resistance and dimensional stability whilst retaining an exce..
Tensile Strength 85.0 MPa

@Temperature 23.0 °C
12300 psi

@Temperature 73.4 °F
DAM; ASTM D638
DuPont Performance Polymers Minlon® 11C40 BKB086 Nylon 66  (Unverified Data**)
Minlon® 11C40 BKB086 is a 40% mineral reinforced, heat stabilized, black polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers
Tensile Strength 85.0 MPa
12300 psi
ASTM D638
Kolon KOPA® KN333HRBL Heat Resistant Nylon 66
Middle viscosity, BLACKApplications A variety of reservoir tanks and housingsInformation provided by API-Kolon.
Tensile Strength 85.0 MPa
12300 psi
ISO 527
Lucite International Diakon® CMH454 Acrylic Polymer
Information provided by Lucite International
Tensile Strength 85.0 MPa
12300 psi
ISO 527
Lucite International Diakon® CMH454L Acrylic Polymer
Information provided by Lucite International
Tensile Strength 85.0 MPa
12300 psi
ISO 527
Lucite International Diakon® MH254 Acrylic Bead Polymer, High Transparency
PMMA beads offer an exceptional transmission level of 92.5%, an increase of +0.5% in light transmission vs. granular grades - ideal for medical diagnostic devices.Information provided by Lucite Inte..
Tensile Strength 85.0 MPa
12300 psi
ASTM D638
Solvay Specialty Polymers Ryton® QC200N Polyphenylene Sulfide (PPS)
Ryton® PPS Fiber Grade Resins are high molecular weight polyphenylene sulfide polymers suitable for monofilament and/or multifilament fiber extrusion. They exhibit excellent thermal stability and..
Tensile Strength 85.0 MPa
12300 psi
ASTM D638
Solvay Specialty Polymers Ryton® QC200P Polyphenylene Sulfide (PPS)
Ryton® PPS Fiber Grade Resins are high molecular weight polyphenylene sulfide polymers suitable for monofilament and/or multifilament fiber extrusion. They exhibit excellent thermal stability and..
Tensile Strength 85.0 MPa
12300 psi
ASTM D638
Solvay Specialty Polymers Ryton® QC220N Polyphenylene Sulfide (PPS)
Ryton® PPS Fiber Grade Resins are high molecular weight polyphenylene sulfide polymers suitable for monofilament and/or multifilament fiber extrusion. They exhibit excellent thermal stability and..
Tensile Strength 85.0 MPa
12300 psi
ASTM D638
Solvay Specialty Polymers Ryton® QC220P Polyphenylene Sulfide (PPS)
Ryton® PPS Fiber Grade Resins are high molecular weight polyphenylene sulfide polymers suitable for monofilament and/or multifilament fiber extrusion. They exhibit excellent thermal stability and..
Tensile Strength 85.0 MPa
12300 psi
50 mm/min; ISO 527-1
Sax Polymers SAXAMID 226 Nylon 6.6
SAXAMID 226 is a general purpose polyamide 6.6 injection-molding-grade. Benefits are short cycle times and good release properties.Information provided by SAX Polymers
Tensile Strength 85.0 MPa
12300 psi
5 mm/min; ISO 527-1
Sax Polymers SAXALEN PPH305G30 Polypropylene Homopolymer, 30% Glass Filled
SAXALEN PPH305G30 is a 30% glass filled Polypropylene - Homopolymer injection molding grade with high stiffness, low creep under load and good flow properties.Information provided by SAX Polymers
Tensile Strength 85.0 MPa

@Thickness >=1.50 mm
12300 psi

@Thickness >=0.0591 in
24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6
Elektro-Isola Etronax MFP G Phenolic, Cotton/synthetic Fabric Reinforcement, Black, Sheets
Description: Exclusively for mechanical applications. The combination of cotton/synthetic reinforcement and a graphite-modified resin results in a material with low friction and especially high wear..
Tensile Strength 84.8 MPa
12300 psi
ASTM D638
Ensinger Tecapeek® XP-115 Compression Molded PEEK Compound, Static Dissipative
Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in..
Tensile Strength 84.8 MPa
12300 psi
ASTM D638
Ensinger Tecapeek® XP-181 Compression Molded PPEK Compound, EWS Filled and Carbon Fiber Reinforced
Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in..
Tensile Strength 84.8 MPa
12300 psi
ASTM D638
Ensinger Tecapeek® XP-91BHT Compression Molded PEEK HT Compound, 30% Fiberglass, Black Pigmented
Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in..
Tensile Strength 84.8 MPa
12300 psi
ASTM D638
Ensinger Tecapeek® XP-99 Compression Molded PEEK Compound, Bearing Grade Material with 7% Graphite, 8% PTFE, and 15% Carbon Fiber
Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in..
Tensile Strength >= 85.0 MPa
>= 12300 psi
IEC 1212-2 5.7
Hippe PF CC 203 Woven Cotton Cloth Reinforced Phenolic Resin - Sheet
Used in mechanical applications (fine weave: =130 g/m2, >30 threads/cm). Recommended for small parts. Better mechanical properties and poorer electrical properties than type PF CC 204.Information ..
Tensile Strength 85.0 MPa
12300 psi
dry; DIN 53 455
Hippe PA 6 G
Thick-wall pre-forms, heavy semi-finished products. Transfusion of inserts (rolls, cores) and all types of large preforms.Information provided by Hippe.
Tensile Strength 85.0 MPa
12300 psi
DIN 53 455
Hippe PEI
A material with very high mechanical strength and high thermoforming stability which can be used at high temperatures. Distinguished by constant dielectric properties, a wide range of frequency and ..
Tensile Strength 85.0 MPa
12300 psi
cond.; ISO 527
Azoty Tarnow™ Tarnamid® T-27 GF20 FRV0 Polyamide 6 - Flame Retarded, Reinforced
Flame retarded grades, flammability class V0, reinforced with 20% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning..
Tensile Strength 85.0 MPa

@Strain 15.0 %,
Temperature 0.000 °C
12300 psi

@Strain 15.0 %,
Temperature 32.0 °F
50 mm/min; ISO 527-2
BASF Elastollan R 2000 20% Glass Filled TPUR
Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan..