Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 35.0 MPa | 5080 psi | ASTM D638 |
Premix Premi-Glas® 1200H-15 Polyester SMC Premi-Glas® 1200H-15 is a 15% fiberglass-reinforced, thermoset, Sheet Molding Compound designed for applications where good arc resistance and dielectric strength are required and UL 94 HB flame re.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ASTM D638 |
Premix Premi-Glas® 1201-15 Polyester SMC Premi-Glas® 1201-15 is a 15% glass reinforced thermoset Sheet Molding Compound designed for sinks, shower stall bases and wall applications. Key features and benefits are:Supports ANSI 124.2 and CS.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ASTM D638 |
Premix Premi-Glas® 1240-15 Fiberglass Reinforced Thermoset Thick Molding Compound Premi-Glas® 1240-15 is a fiberglass reinforced thermoset Thick Molding Compound for general purpose applications requiring thermal stability and stiffness.Key features and benefits are:Excellent st.. |
|||
Tensile Strength | 35.0 - 140 MPa | 5080 - 20300 psi | MD; ISO 527 / PA_098 |
Quadrant Plastic Composites GMT Glass-Mat-Reinforced Thermoplastic This semi-finished product in panel form was developed primarily as a substitute for metals (steel, aluminum etc.) and its main purchasers can be found in the automotive industry. This is where it i.. |
|||
Tensile Strength | 35.0 - 60.0 MPa | 5080 - 8700 psi | Compression; ISO 527 |
Raschig Group RALUPOL® 4802 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u.. |
|||
Tensile Strength | 35.0 - 60.0 MPa | 5080 - 8700 psi | Compression; ISO 527 |
Raschig Group RALUPOL® 5000 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, excellent heat resistance, good mechanical strength. This product meets the all.. |
|||
Tensile Strength | 35.0 - 60.0 MPa | 5080 - 8700 psi | Compression; ISO 527 |
Raschig Group RALUPOL® 802 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength, good heat resistance. This product meets the allowed up.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ASTM D412 |
GRECO ISOTHANE 1190A Poly(adipate)ester TPUÂ Resin ISOTHANE 1100 series products are transparent grade, polyester poly(adipate)ester based thermoplastic polyurethanes. They exhibit good toughness, solvent resistance, easy processing, and high transp.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | Measured on films cast from solution in toluene; ISO 37 |
Kraton® G1650 E (SEBS) Linear Triblock Copolymer Description: Kraton G1650 E is a clear linear triblock copolymer based on styrene and ethylene/butylene, S-E/B-S, with bound styrene of 29.2% mass. It is supplied from Europe in the physical forms i.. |
|||
Tensile Strength | 35.03 MPa | 5080 psi | ISO 527-2/5A/500 |
Lubrizol Advanced Materials Pearlthane® D91T80 Thermoplastic Polyurethane Type : Pearlthane® D91T80 is a aliphatic-based thermoplastic polyurethane.Main Application : Injection MouldingSpecial Features : Low density, fast processing and excellent elasticity properties... |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ASTM D412 |
Wanhua Chemical Wanthane® WHT-7185 Polycaprolactone Based TPU Higher mechanical strength, good hydrolytic stability & chemical resistance, weather resistance, heat & fungus resistanceInformation provided by Wanhua Chemical Group Co., Ltd. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ASTM D412 |
Wanhua Chemical Wanthane® WHT-1495B Polyester Based TPU Good extrusion stability, high transparency, excellent mechanical propertiesInformation provided by Wanhua Chemical Group Co., Ltd. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ISO 527 |
Ecomass® 2150TU96 Tungsten Powder Filled Polyamide (PA6/6), Injection Molding Grade Tungsten Powder Filled Polyamide (PA6/6), Good Toughness, Product Form - PelletsProcessing Method: Injection MoldingNontoxic alternative to Lead, weighting, balancing and radiation shielding applic.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | DIN 53 455 |
Hippe PA 12 Nylon 12 Maintenance-free bearing and gear components under water, insulated components, seals, gear wheels. Parts for pumps and household units. Application in the electrical sector - less water absorptio.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ISO 37 |
BASF Elastollan 1085 A TPUR Description: Thermoplastic Polyurethane Elastomers with excellent mechanical properties, outstanding wear resistance, high tear and tensile strength, good damping characteristics and a high resilien.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | after storage in water at 80°C for 42 days; ISO 37 |
BASF Elastollan 1198 A TPUR Description: Thermoplastic Polyether Polyurethane Elastomers with outstanding hydrolysis resistance, low temperature flexibility and resistance to micro-organisms.Typical Applications: Cable sheathi.. |
|||
Tensile Strength | 35.0 MPa @Strain 300 % |
5080 psi @Strain 300 % |
ISO 37 |
BASF Elastollan B 64 D TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties, outstanding wear resistance, high tensile strength, good damping and resilience performance and sup.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | after storage in water at 80°C for 42 days; ISO 37 |
BASF Elastollan C 75 A HPM TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and chemical resistance, outstanding wear resistance, high tear and tensile strength, good damping c.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ISO 37 |
BASF Elastollan S 50 A SPF TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and wear resistance, good damping characteristics and a high resilience performance.Typical Applicat.. |
|||
Tensile Strength | >= 35.0 MPa | >= 5080 psi | ISO 37 |
Austin Novel Materials Texalan® 282A Polyester-based TPU Description: Good abrasion resistance, tensile strength, oil resistance and transparency which can meet different demands in various industryInformation from Dawnentech |
|||
Tensile Strength | 35.0 - 45.0 MPa | 5080 - 6530 psi | ISO 527 |
Bulk Molding Compounds tetra-DUR N 4303 Bulk Molding Compound Mechanical high grade standard product.Typical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipation (explosion p.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ISO 37 |
BASF Elastollan 1185 A WM TPUR Description: Thermoplastic Polyether Polyurethane Elastomers with outstanding hydrolysis resistance, low temperature flexibility and resistance to micro-organisms.Typical Applications: Cable sheathi.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ISO 37 |
BASF Elastollan 670 AWHU TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and wear resistance, good damping characteristics and a high resilience performance.Typical Applicat.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | after storage in water at 80°C for 42 days; ISO 37 |
BASF Elastollan C 75 A TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and chemical resistance, outstanding wear resistance, high tear and tensile strength, good damping c.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | after storage in water at 80°C for 42 days; ISO 37 |
BASF Elastollan C 85 A HPM TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and chemical resistance, outstanding wear resistance, high tear and tensile strength, good damping c.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ASTM D412 |
Wanhua Chemical Wanthane® WHT-1595 Polyester Based TPU Low cost, good mechanical properties, good processabilityInformation provided by Wanhua Chemical Group Co., Ltd. |
|||
Tensile Strength | 35.0 - 60.0 MPa | 5080 - 8700 psi | Compression; ISO 527 |
Raschig Group 5567 DAP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl phthalate molding compound free from halogens. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exc.. |
|||
Tensile Strength | 35.0 - 44.0 MPa | 5080 - 6380 psi | ISO 527 |
BASF Ecoflex® C1200 F Blend Biodegradable Polyester Description: Ecovio® F Blend C2332 is our biodegradable, statistical, aliphatic-aromatic copolyester based on the monomers 1,4-butanediol, adipic acid and terephathalic acid in the polymer chain. E.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ISO 37 |
BASF Elastollan B 60 A WHA TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties, outstanding wear resistance, high tensile strength, good damping and resilience performance and sup.. |