Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Property : Tensile Strength = 7250 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength >= 50.0 MPa
>= 7250 psi
ASTM D882
OCTAL DPET™/PE Peelable Laminate Sheet
Clear direct-to-sheet amorphous PET sheet with a polyethylene laminate film. Approved for food contact packaging. Information provided by OCTAL Petrochemicals.
Tensile Strength 50.0 MPa
7250 psi
ASTM D638
Premix Premi-Glas® 1200H-20 Polyester SMC
Premi-Glas® 1200H-20 is a 20% fiberglass reinforced, thermoset, Sheet Molding Compound designed for applications where good arc resistance and dielectric strength are required and UL 94HB flame rec..
Tensile Strength 50.0 MPa
7250 psi
ASTM D638
Premix Premi-Glas® 1240-20 Fiberglass Reinforced Thermoset Thick Molding Compound
Premi-Glas® 1240-20 is a fiberglass reinforced thermoset Thick Molding Compound for general purpose applications requiring thermal stability and stiffness.Key features and benefits are:Excellent st..
Tensile Strength 50.0 MPa
7250 psi
ASTM D638
Premix Premi-Glas® 2203-20 CR-SX Fiberglass Reinforced Thermoset SMC
Premi-Glas® 2203-20 CR-SX is a fiberglass reinforced thermoset sheet molding compound for electrical and flame retardant applications.Key features and benefits are:Excellent stiffness to weight rat..
Tensile Strength 50.0 MPa
7250 psi
ASTM D638
Premix Premi-Glas® 2204-20 CR-SX Fiberglass Reinforced Thermoset SMC
Premi-Glas® 2204-20 CR-SX is a fiberglass reinforced thermoset sheet molding compound for electrical and flame retardant applications.Key features and benefits are:Good dimensional stability, inclu..
Tensile Strength 50.0 MPa
7250 psi
ASTM D638
Premix Premi-Glas® 2206-25 CR-SX Fiberglass Reinforced Thermoset SMC
Premi-Glas® 2206-25 CR-SX is a fiberglass reinforced thermoset sheet molding compound for electrical, flame retardant and HVAC applications.Key features and benefits are:Non-Halogen FR technology f..
Tensile Strength 50.0 - 70.0 MPa
7250 - 10200 psi
Injection; ISO 527
Raschig Group 6502 DAIP Diallyl Phthalate (DAP), Cast, Mineral Filler
Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi..
Tensile Strength 50.0 - 70.0 MPa
7250 - 10200 psi
Injection; ISO 527
Raschig Group DECAL® 1760 Phenolic
Glass-fiber reinforced phenolic molding compound. Very good electrical properties, good chemical resistance and mechanical properties. This product meets the allowed upper limits for heavy metals an..
Tensile Strength 50.0 - 70.0 MPa
7250 - 10200 psi
Compression; ISO 527
Raschig Group DECAL® 572R Phenolic
Glass-fiber reinforced phenolic molding compound. Exceptional heat resistance with regard to maintaining surface finish and mechanical properties, outstanding mechanical properties, excellent rotati..
Tensile Strength 50.0 - 90.0 MPa
7250 - 13100 psi
Injection; ISO 527
Raschig Group MELOPAS® 2010 MF Melamine
Organically and inorganically filled Melamine molding compound. Excellent surface hardness, good mechanical strength, good electrical properties. This product meets the allowed upper limits for heav..
Tensile Strength 50.0 - 70.0 MPa
7250 - 10200 psi
ISO 527
Raschig Group 3572 Epoxy
Glass-fiber reinforced epoxy molding compound. Good mechanical strength and electrical strength, enhanced elasticity for ensuring good sealing under extreme heat and/or humidity, good chemical resis..
Tensile Strength >= 50.0 MPa
>= 7250 psi
GB/T 1040.2-2006
Sichuan Deyang Haton® hb DL Polyphenylene Sulfide Resin
Extrusion, low chlorineInformation provided by Sichuan Deyang Chemical Co., LTD
Tensile Strength 50.0 MPa
7250 psi
ISO 527-1
Sax Polymers SAXLAC 310A Acrylonitrile Butadiene Styrene
Saxalac 310A is a medium viscosity, impact resistant ABS injection molding grade, characterized by good processability and high stiffness.Mechanical property data tested at 50% RH.Information provid..
Tensile Strength 50.0 MPa
7250 psi
Wolf Kunststoff ZEDEX® ZX-100A Polymer Alloy
Main Characteristics: Tough; Resilient; Soft; Low cost solutionApplications: Handling, Vessel and pump, Steel and Water, Chemical Engineering, Automitve Technology, Machine ToolsInformation provided..
Tensile Strength 50.0 MPa
7250 psi
DIN EN ISO 527
Wolf Kunststoff ZEDEX® ZX-530 A5D Polymer Alloy
Main Characteristics: Low Creep; Low moisture absorption; Flame retardant; Low impurity ions; Good machinability; FDA compliant LABS; Extremely low outgassing; Less expensive than PEEK; Stress resis..
Tensile Strength 50.0 MPa
7250 psi
ISO 37
BASF Elastollan 1198 A TPUR
Description: Thermoplastic Polyether Polyurethane Elastomers with outstanding hydrolysis resistance, low temperature flexibility and resistance to micro-organisms.Typical Applications: Cable sheathi..
Tensile Strength 50.0 MPa
7250 psi
ISO 37
BASF Elastollan 590 A TPUR
Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and a high abrasion resistance.Typical Applications: Heel top-pieces, castor tyres and parts requiri..
Tensile Strength 50.0 MPa
7250 psi
ISO 37
BASF Elastollan 685 AU TPUR
Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and wear resistance, good damping characteristics and a high resilience performance.Typical Applicat..
Tensile Strength 50.0 MPa
7250 psi
ISO 37
BASF Elastollan 690 AU TPUR
Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and wear resistance, good damping characteristics and a high resilience performance.Typical Applicat..
Tensile Strength 50.0 MPa
7250 psi
ISO 37
BASF Elastollan 695 AU TPUR
Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and wear resistance, good damping characteristics and a high resilience performance.Typical Applicat..
Tensile Strength 50.0 MPa
7250 psi
ISO 37
BASF Elastollan C 59 D TPUR
Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and chemical resistance, outstanding wear resistance, high tear and tensile strength, good damping c..
Tensile Strength 50.0 MPa
7250 psi
50 mm/min; ISO 37
BASF Elastollan R 1000 20% Glass Filled TPUR
Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan..
Tensile Strength 50.0 MPa
7250 psi
ISO 37
BASF Elastollan SP 852 TPUR
Description: Thermoplastic Polyurethane Elastomers with excellent mechanical properties, outstanding wear resistance, high tear and tensile strength, good damping characteristics and a high resilien..
Tensile Strength 50.0 MPa
7250 psi
ISO 37
BASF Elastollan C 85 A HPM TPUR
Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and chemical resistance, outstanding wear resistance, high tear and tensile strength, good damping c..
Tensile Strength 50.0 MPa

@Strain 10.0 %,
Temperature 40.0 °C
7250 psi

@Strain 10.0 %,
Temperature 104 °F
50 mm/min; ISO 527-2
BASF Elastollan R 2000 20% Glass Filled TPUR
Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan..
Tensile Strength >= 50.0 MPa
>= 7250 psi
ISO 37
Austin Novel Materials Texalan® 664D Polyester and Polyether based TPU
Description: A kind of custom-made products which use different raw materials to meet customers special requirementsInformation from Dawnentech
Tensile Strength 50.0 MPa
7250 psi
DIN 53 455
Hippe PVC-U Polyvinyl Chloride
Material at reasonable price, high strength. Used in machine construction as covers, pipes, section, façade elements.Information provided by Hippe.
Tensile Strength 50.0 MPa
7250 psi
ISO 37
BASF Elastollan 695 AU TPUR
Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and wear resistance, good damping characteristics and a high resilience performance.Typical Applicat..