Polymer Property : Compressive Strength = 13100 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Compressive Strength 90.0 - 147 MPa
13100 - 21300 psi
Type B, 5mm/min; ISO 604:2002
Nylacast H.S. Blue Cast Nylon 6, Heat Stabilized
HS Blue is a heat Stabilised Cast Nylon 6. Its mechanical properties are maintained when operating at higher temperature and improves mechanical properties. This helps to reduce the stress distortio..
Compressive Strength 90.0 MPa
13100 psi
ASTM D695
IDI Composites 46-3 Thermoset Polyester, Molding
Superior electrical performance with low pressure molding for V-O flammability in encapsulation applications.Data provided by the manufacturer.
Compressive Strength 90.0 MPa
13100 psi
Sample Type B, 5 mm/min; ISO 604:2002
Global EPP PA 66E Extruded Polyamide 66
Polyamides, commonly referred to as nylons, are macromolecular, partially crystalline thermoplastics. Their physical properties are mainly determined by the composition and structure of their molecu..
Compressive Strength 90.0 MPa
13100 psi
Sample Type B, 5 mm/min; ISO 604:2002
Global EPP PA 6C IMPACT Cast Polyamide 6 + Plasticizer
Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of ..
Compressive Strength 90.0 MPa
13100 psi
Sample Type B, 5 mm/min; ISO 604:2002
Global EPP PA 6E Extruded Polyamide 6
Polyamides, commonly referred to as nylons, are macromolecular, partially crystalline thermoplastics. Their physical properties are mainly determined by the composition and structure of their molecu..
Compressive Strength 90.0 MPa
13100 psi
Cold Crushing Strength
Gouda Vuurvast AK 60 AP Dense Refractory Brick
Description: This phosphate bonded brick combines a very good thermal shock resistance with high slag resistance and low creep. Application: frit melting furnaces, incinerators, burner blocks, lime ..
Compressive Strength 90.0 MPa
13100 psi
Haysite 14100 Polyester BMC, 15% Glass Reinforced
The 14100 series bulk molding compound is an electrical grade material that can be compression, transfer, or injection molded. Offering good mechanical strength and excellent electrical properties, ..
Compressive Strength 90.0 MPa
13100 psi
Haysite 20000 Polyester BMC, 15% Glass Reinforced
The 20000 series bulk molding compound is an electrical grade that can be compression, transfer, or injection molded. Offering good arc/track properties and mechanical strength, this grade is also r..
Compressive Strength 90.0 MPa
13100 psi
Sample Type B, 5 mm/min; ISO 604:2002
Global EPP PA 612 Copolymer Cast Polyamide 612
Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of ..
Compressive Strength 90.0 MPa
13100 psi
Cold Crushing Strength
Gouda Vuurvast AK 85 KM Dense Refractory Brick
Description: This brick based on mullite and corundum, is characterized by a very low porosity, high slag resistance, low creep and very good thermal shock resistance.Remarks: This data represents a..
Compressive Strength 90.0 MPa
13100 psi
20% pressing; EN ISO 604
Schwartz Technical Plastics LAMIGAMID® 310 Cast Polyamide 6, Conditioned
Application: sheaves, wheels, rollers, mandrell segments, coupling parts, vibrator parts etc.Information provided by Schwartz Technical Plastics GmbH
Compressive Strength 90.0 MPa
13100 psi
20% pressing; EN ISO 604
Schwartz Technical Plastics LAMIGAMID® 310 Cast Polyamide 6, Dry
Application: sheaves, wheels, rollers, mandrell segments, coupling parts, vibrator parts etc.Information provided by Schwartz Technical Plastics GmbH
Compressive Strength 90.0 MPa
13100 psi
Absolute Drying; ASTM-D695
Toyobo GLAMIDE® T-662 Nylon-66
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Compressive Strength 90.0 MPa
13100 psi
Absolute Drying; ASTM-D695
Toyobo GLAMIDE® TY-835TC Nylon-66
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Compressive Strength 90.0 MPa

@Temperature 23.0 °C
13100 psi

@Temperature 73.4 °F
ASTM D695
Toyobo T-661 Nylon 66, Standard Grade (DAM)
Features: Non-reinforced, Standard GradeInformation provided by Toyobo.
Compressive Strength 90.3 MPa
13100 psi
ASTM D695
Chesterton ARC SD4i High temperature ceramic reinforced erosion resistant coating
Description: An advanced ceramic composite for resurfacing and protection of metal surfaces in immersion service. It is normally applied in a thickness range of 250-370 microns (10-15 mils) per coat..
Compressive Strength 90.3 MPa
13100 psi
ASTM D695
Chesterton MRS SD4i Metal Rebuilding System
An advanced ceramic composite for resurfacing and protection of metal surfaces in immersion service. It is normally applied in a thickness range of 250-370 microns (10 – 15 mils) per coat. Non-shri..
Compressive Strength 90.0 MPa
13100 psi
ISO 604
Chevron Phillips Xtel® XE3035BL Polyphenylene Sulfide Alloy
Xtel® XE3035BL is a high performance, glass fiber reinforced, PPS based alloy developed to provide exceptionally high ductility and impact resistance along with good thermal stability.Information p..
Compressive Strength 90.0 MPa
13100 psi
ISO 604
Chevron Phillips Xtel® XE3035NA Polyphenylene Sulfide Alloy
Xtel® XE3035NA is a high performance, glass fiber reinforced, PPS based alloy developed to provide exceptionally high ductility and impact resistance along with good thermal stability.Information p..
Compressive Strength >= 90.0 MPa
>= 13100 psi
Perpendicular to laminations; IEC 1212-2 5.3
Hippe MF CC 201 Woven Cotton Cloth Reinforced Melamine Resin - Sheet
Used in mechanical and electrical applications (coarse weave: >130 g/m2, =30 threads/cm). Arc and tracking resistant.Information provided by Hippe.
Compressive Strength >= 90.0 MPa
>= 13100 psi
Axial; IEC 1212-2 4.2
Hippe PF CC 41 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod
Used in mechanical and electrical applications. Fine weave (more than 30 threads per cm).Information provided by Hippe.
Compressive Strength 90.3 MPa
13100 psi
ASTM D695
Chesterton ARC MX2 High Wear Fine Particle Wear Compound
Description: An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion and chemical attack. It is applied at a thickness of 3 mm (1/8”..
Compressive Strength 90.0 - 105 MPa
13100 - 15200 psi
GB/T 1040
Beijing Evergrow Resources MoS2 Filled Nylon
Information provided by Beijing Evergrow Resources.
Compressive Strength 90.3 MPa
13100 psi
Abatron AboCast 8103-13 One-Component Epoxy
AboCast 8103-13 is the low-viscosity one-component clear epoxy system with deep impregnation that offers high performance at relatively high temperatures. It is best for thin-wall casting. Suggested..
Compressive Strength 90.3 MPa
13100 psi
BCC Products BC 6005 Epoxy Surface Coat
BC 6005 is a snow white thixotropic epoxy resin designed specifically for quality reproduction of a variety of surfaces. A room temperature cure system that offers ample working time yet affords qui..