Polymer Property : Compressive Strength = 13800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Compressive Strength 95.0 MPa
13800 psi
Type B, 5mm/min; ISO 604:2002
Nylacast Oilon Cast Nylon 6, Lubricated (Lubricant Oil Filled)
This exceptional oil-loaded nylon features a complex blended oil lubrication system, uniformly distributed throughout the product, that guarantees constant performance over the whole service life. E..
Compressive Strength 95.0 MPa
13800 psi
Type B, 5mm/min; ISO 604:2002
Nylacast PA6C Cast Nylon 6
Natural PA6 is the base to the other grades of material offered by Nylacast. It is available in Natural (off white) or Black colour. It is made by ionic polymerisation of e-caprolactam under anhydri..
Compressive Strength 95.0 MPa
13800 psi
Sample Type B, 5 mm/min; ISO 604:2002
Global EPP PA 6C Cast Polyamide 6
Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of ..
Compressive Strength 95.0 MPa
13800 psi
Sample Type B, 5 mm/min; ISO 604:2002
Global EPP PA 6C HS BLUE Cast Polyamide 6 + UV and Heat Stabilizers
Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of ..
Compressive Strength 95.0 MPa
13800 psi
Sample Type B, 5 mm/min; ISO 604:2002
Global EPP PA 6C OFN Cast Polyamide 6 + Blended Liquid Lubricant
Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of ..
Compressive Strength 95.0 MPa
13800 psi
Sample Type B, 5 mm/min; ISO 604:2002
Global EPP PA 6C WFN Cast Polyamide 6 + Wax
Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of ..
Compressive Strength 95.0 MPa
13800 psi
20% pressing; EN ISO 604
Schwartz Technical Plastics LAMIGAMID® 314 Cast Polyamide 6, MoS2 Filled, Heat Stabilized, Dry
Application: sheaves, wheels, gear-rods, gears, sliding linersInformation provided by Schwartz Technical Plastics GmbH
Compressive Strength 95.0 MPa
13800 psi
20% pressing; EN ISO 604
Schwartz Technical Plastics LAMIGAMID® 314 Cast Polyamide 6, MoS2, Heat Stabilized, Conditioned
Application: sheaves, wheels, gear-rods, gears, sliding linersInformation provided by Schwartz Technical Plastics GmbH
Compressive Strength 95.0 MPa
13800 psi
20% pressing; EN ISO 604
Schwartz Technical Plastics LAMIGAMID® 510 Polyethylene Terephthalate
Application: friction bearings, wear linersInformation provided by Schwartz Technical Plastics GmbH
Compressive Strength 95.0 MPa

@Strain 3.50 %
13800 psi

@Strain 3.50 %
DIN EN ISO 604
Wolf Kunststoff ZEDEX® ZX-324VMT A3B PEEK, Fiber Reinforced
Main Characteristics: Maximum rigidity; Very good wear resistance; Low stick-slip tendency; Stress resistantApplications: Shipbuilding; Chemical Engineering; Automitve Technology; Machine ToolsInfor..
Compressive Strength 95.0 MPa

@Time 360000 sec
13800 psi

@Time 100 hour
Wolf Kunststoff ZEDEX® ZX-750V5KF 055 Polymer Alloy. Fiber Reinforced
Main Characteristics: Stiff; High elongation and yield stress; Low thermal expansion; Impact resistantApplications: Textile Machinery; Compressors; Hinges; Handling; Machine Tools; Automitve Technol..
Compressive Strength 95.0 MPa
13800 psi
Elastic Limit
Wolf Kunststoff ZEDEX® ZX-750V5T A9T Polymer Alloy
Main Characteristics: Hard; Stiff; Tough; High dimensional stability; High fatigue strength; High weather resistance; Good fire behavior; Suitable for vacuum; Good machinability; Contains PTFE; Stre..
Compressive Strength >= 95.0 MPa
>= 13800 psi
Ambient
China-Yixing Longly Refractories Plate Corundum-Mullite
Products with high-purity fused alumina and fused mullite for raw materials, the use of high-tonnage press repression, from ultra-high-temperature sintering; high-purity, the main phase (or corundum..
Compressive Strength >= 95.0 MPa
>= 13800 psi
Ambient
China-Yixing Longly Refractories Seggar Corundum-Mullite
Our company's production of a variety of corundum mullite push slab (moved plate), corundum-mullite seggar, corundum mullite corrugated board and other kinds of the kiln furniture, high refractorine..
Compressive Strength 95.1 MPa
13800 psi
BCC Products BC 6004 Epoxy Surface Coat
BC 6004 is a white thixotropic epoxy surface coat that has the ability to cure and bond to freshly poured wet plaster. This formulated resin compound can be applied with a brush or troweled to a thi..
Compressive Strength 95.1 - 123 MPa
13800 - 17800 psi
Bulk Molding Compounds BMC T60-6009 Compression Grade Wear Resistant Molding Compound
BMC T60-6009 is a compression grade wear resistant molding compound. This material was specifically formulated for applications that require excellent abrasion resistance. Due to its low specific ..