- Polymer Property : Compressive Strength = 21800 psi
Polymer Property : Compressive Strength = 21800 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Compressive Strength | 150 MPa | 21800 psi | ASTM D695 |
| Owens Corning Glass Fiber Reinforced Polyester (Spray-up/Lay-up), 30 wt.% glass Data provided by the manufacturer, Owens Corning. |
|||
| Compressive Strength | 150 - 200 MPa | 21800 - 29000 psi | ISO 604 |
| Raschig Group 5553 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
| Compressive Strength | 150 - 200 MPa | 21800 - 29000 psi | ISO 604 |
| Raschig Group 5563 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
| Compressive Strength | 150 - 200 MPa | 21800 - 29000 psi | ISO 604 |
| Raschig Group 6501 DAIP Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi.. |
|||
| Compressive Strength | 150 - 200 MPa | 21800 - 29000 psi | ISO 604 |
| Raschig Group 6502 DAIP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi.. |
|||
| Compressive Strength | 150 - 200 MPa | 21800 - 29000 psi | ISO 604 |
| Raschig Group 6551 DAIP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi.. |
|||
| Compressive Strength | 150 - 200 MPa | 21800 - 29000 psi | ISO 604 |
| Raschig Group AMPLA® 2000 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Low post-shrinkage, very good electrical values, high heat resistance, very good sliding behavior, ve.. |
|||
| Compressive Strength | 150 - 200 MPa | 21800 - 29000 psi | ISO 604 |
| Raschig Group AMPLA® 7250 melamine-modified polyester Cellulose reinforced melamine-modified Polyester molding compound. Very good electrical values, excellent heat resistance, excellent surface quality, low post shrinkage. This product meets the allow.. |
|||
| Compressive Strength | 150 - 200 MPa | 21800 - 29000 psi | ISO 604 |
| Raschig Group AMPLA® 7500 melamine-modified polyester Organically and inorganically filled melamine modified Polyester molding compound. Low post-shrinkage, very good electrical values, excellent heat resistance, very good sliding behavior and wear sta.. |
|||
| Compressive Strength | 150 - 200 MPa | 21800 - 29000 psi | ISO 604 |
| Raschig Group RALUPOL® 2100 UP Polyester Organically and inorganically filled polyester molding compound. Low post-shrinkage, very good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy meta.. |
|||
| Compressive Strength | 150 - 200 MPa | 21800 - 29000 psi | ISO 604 |
| Raschig Group RALUPOL® 4385 UP Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very high arc resistance, very high mechanical values. This product meets the allowed upper limits for heavy.. |
|||
| Compressive Strength | 150 - 200 MPa | 21800 - 29000 psi | ISO 604 |
| Raschig Group RALUPOL® 4566 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u.. |
|||
| Compressive Strength | 150 - 200 MPa | 21800 - 29000 psi | ISO 604 |
| Raschig Group RALUPOL® 4802 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u.. |
|||
| Compressive Strength | 150 - 200 MPa | 21800 - 29000 psi | ISO 604 |
| Raschig Group RALUPOL® 5000 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, excellent heat resistance, good mechanical strength. This product meets the all.. |
|||
| Compressive Strength | 150 MPa | 21800 psi | ASTM D695 |
| Resinoid 2002-4 Phenolic Molding, Fabric Reinforced Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance |
|||
| Compressive Strength | 150 MPa | 21800 psi | |
| Poco Graphite HPD Semiconductor Grade Graphite Although it is impossible to identify differences between various grades of graphite by looking at them, each grade has a special set of characteristics and physical properties that determine their .. |
|||
| Compressive Strength | 150 - 200 MPa | 21800 - 29000 psi | ISO 604 |
| Raschig Group 3572 Epoxy Glass-fiber reinforced epoxy molding compound. Good mechanical strength and electrical strength, enhanced elasticity for ensuring good sealing under extreme heat and/or humidity, good chemical resis.. |
|||
| Compressive Strength | 150 - 200 MPa | 21800 - 29000 psi | ISO 604 |
| Raschig Group RALUPOL® 802 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength, good heat resistance. This product meets the allowed up.. |
|||
| Compressive Strength | 150 - 200 MPa | 21800 - 29000 psi | ISO 604 |
| Raschig Group RALUPOL® 804 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy m.. |
|||
| Compressive Strength | 150 - 200 MPa | 21800 - 29000 psi | ISO 604 |
| Raschig Group RALUPOL® 8602 UP Glass-fiber reinforced polyester molding compound. Mold shrinkage similar to phenolic molding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical streng.. |
|||
| Compressive Strength | 150 MPa | 21800 psi | ASTM D695 |
| Sumitomo Bakelite North America RX® 1-520/RX® 1310 Short-Glass Reinforced Diallyl Phthalate Short glass fiber reinforced, non-flame retardant, diallyl ortho-phthalate molding compound which meets the requirements of ASTM D5948 Type SDG.Information provided by Vyncolit, a Sumitomo Bak Group.. |
|||
| Compressive Strength | 150 MPa | 21800 psi | break; DIN EN ISO 604 |
| Wolf Kunststoff ZEDEX® ZX-530EL3 066 Polymer Alloy, Carbon Fiber Reinforced Main Characteristics: Low thermal expansion; High rigidity; High yield stress; High wear resistance; Low friction; Stress ResistantApplications: Chemical Engineering; Laboratory Technology; Automitv.. |
|||
| Compressive Strength | 150 MPa | 21800 psi | DIN EN ISO 604 |
| Wolf Kunststoff ZEDEX® ZX-530EL3 066 Polymer Alloy, Carbon Fiber Reinforced Main Characteristics: Low thermal expansion; High rigidity; High yield stress; High wear resistance; Low friction; Stress ResistantApplications: Chemical Engineering; Laboratory Technology; Automitv.. |
|||
| Compressive Strength | 150 MPa | 21800 psi | Absolute Drying; ASTM-D695 |
| Toyobo GLAMIDE® TY-791GT 6T-Nylon GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a.. |
|||
| Compressive Strength | 150 - 170 MPa | 21800 - 24700 psi | ISO 604 |
| Bulk Molding Compounds tetra-DUR N 4303 Bulk Molding Compound Mechanical high grade standard product.Typical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipation (explosion p.. |
|||
| Compressive Strength | 150 - 200 MPa | 21800 - 29000 psi | ISO 604 |
| Raschig Group 5567 DAP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl phthalate molding compound free from halogens. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exc.. |
|||
| Compressive Strength | 150 - 200 MPa | 21800 - 29000 psi | ISO 604 |
| Raschig Group RALUPOL® 8605 UP Polyester Glass fiber reinforced polyester molding compound. Resistant to hydrolysis. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU dire.. |
|||
| Compressive Strength | 150 MPa | 21800 psi | Cold Crushing Strength |
| Gouda Vuurvast SiC 70 Dense Refractory Brick Description: This type of brick, based on silicon carbide, is because of a very good thermal shock resistance, abrasion resistance and a high thermal conductivity very well suited for waste incinera.. |
|||
| Compressive Strength | 150 MPa | 21800 psi | Test specimen flat tested; ISO 604 |
| Hexion Bakelite™ PF 7595 Phenolic Formaldehyde Resin, Low Coefficient of Friction, Galvanized, Conductive
(di Phenolic molding compound, inorganically/organically filled, modified with graphite, good heat conductivity, good sliding properties, conductive in electrical properties.Application areas: Bearers f.. |
|||
| Compressive Strength | 150 MPa | 21800 psi | |
| Henkel SynCore HC 9875 Syntactic Film High crush strength, low density syntactic core material, co-curable with a variety of 350°F / 177°C curing epoxy prepregs. |
|||