Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 180 MPa | 26100 psi | Test specimen flat tested; ISO 604 |
Hexion Bakelite™ PF 6507 Phenolic Formaldehyde Resin, Elasticized, Low Shrinkage, Resistant to High Temperatures, High Mechanical Strength Phenolic molding compound, inorganically filled, glass fiber reinforced, elastomer modified, galvanizable, heat resistant, good media resistance, high dimensional stability at raised temperature, hi.. |
|||
Compressive Strength | 180 MPa | 26100 psi | ASTM D695 |
Sumitomo Bakelite North America Epiall® 1908B-1 Short Glass Fiber Reinforced Epoxy Epiall 1908B-1 is a short fiberglass reinforced epoxy molding compound, with excellent dimensional stability, good strength properties and good electrical insulation properties.Information provided .. |
|||
Compressive Strength | 180 - 220 MPa | 26100 - 31900 psi | ISO 604 |
Vyncolit G885 Novolac Phenolic Glass fiber and mineral filled phenolic molding compound with excellent mechanical and thermal properties. Information provided by Vyncolit, a Sumitomo Bak Group |
|||
Compressive Strength | 180 MPa | 26100 psi | Absolute Drying; ASTM-D695 |
Toyobo GLAMIDE® T-663G50A MXD66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a.. |
|||
Compressive Strength | 180 MPa | 26100 psi | ASTM D695 |
Plenco 3597 Phenolic, Granular, Injection Molded PLENCO 03597 is a mineral filled phenolic molding compound offering excellent flammability ratings even at thin cross sections, along with excellent arc and comparative track resistance values. UL r.. |
|||
Compressive Strength | 180 MPa | 26100 psi | ASTM D695 |
Plenco 6301 Phenolic, Granular, Injection Molded PLENCO 06301 is an inorganic reinforced phenolic molding compound, offering excellent heat resistance, dimensional stability, and processability as required for typical automotive applications. It i.. |
|||
Compressive Strength | 180 MPa @Temperature 23.0 °C, Time 86400 sec |
26100 psi @Temperature 73.4 °F, Time 24.0 hour |
50% RH, Axial; ISO 604; IEC/EN 61212-2 5.2 |
Elektro-Isola G-Etronax M Melamine, Glass Fabric Reinforcement, White, Tubes Description: Mechanical and electrical applications. Arc-resistant and tracking-resistant material. Good flame resistance. Self-extinguishing. Halogen-free. Lower high-voltage values and insulation .. |
|||
Compressive Strength | 180 MPa @Treatment Temp. 150 °C, Time 3600 sec |
26100 psi @Treatment Temp. 302 °F, Time 1.00 hour |
ISO 604; IEC/EN 60893-2 5.3 |
Elektro-Isola G-Etronax PM 953 Polyester, Glass Mat, Off White, Sheets Description: Good electrical properties such as high breakdown voltage in air and oil and highest arc resistance and tracking resistance. Self-extinguishing. Low smoke emission, halogen-free. Very m.. |
|||
Compressive Strength | 180 MPa @Treatment Temp. 200 °C, Time 3600 sec |
26100 psi @Treatment Temp. 392 °F, Time 1.00 hour |
ISO 604; IEC/EN 60893-2 5.3 |
Elektro-Isola G-Etronax PM H Polyester, Glass Mat, Creme, Sheets Description: A reasonably-priced alternative to other high-temperature types. Low thermal conductivity. Applications: Used as, among other things, thermal insulation plates where high strength prope.. |
|||
Compressive Strength | 180 MPa @Temperature 23.0 °C |
26100 psi @Temperature 73.4 °F |
EN ISO 604 |
Ensinger TECASINT 1031 Polyimide, 40% Graphite Filled (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel.. |
|||
Compressive Strength | 180 MPa @Temperature 23.0 °C |
26100 psi @Temperature 73.4 °F |
EN ISO 604 |
Ensinger TECASINT 3062 Polyimide, Shiny Black, 15% Graphite, 10% PTFE (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel.. |
|||
Compressive Strength | 180 MPa @Temperature 23.0 °C, Time 86400 sec |
26100 psi @Temperature 73.4 °F, Time 24.0 hour |
50% RH, Axial; ISO 604; IEC/EN 61212-2 5.2 |
Elektro-Isola Etronax MF G Phenolic, Cotton Fabric Reinforcement, Black, Tubes Description: Mechanical applications. Impact-resistant, noise-reducing, wear-resistant material. Well suited as a low-friction material. High wear resistance in aggressive and dust-filled environmen.. |
|||
Compressive Strength | >= 180 MPa | >= 26100 psi | ISO 604 |
Bulk Molding Compounds tetra-DUR F 4209 Bulk Molding Compound Highest Arc resistanceTypical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipation (explosion protection), therm.. |
|||
Compressive Strength | >= 180 MPa | >= 26100 psi | ISO 604 |
Bulk Molding Compounds tetra-DUR N 4203 Bulk Molding Compound Highest dimensional stability under temp. Low profile.Typical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipat.. |