Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 9.00 - 11.0 GPa | 1310 - 1600 ksi | Injection; ISO 527 |
Raschig Group 2557 AMC Polyester Glass fiber reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, exceptional processability with short cycle time and low .. |
|||
Modulus of Elasticity | 9.00 - 11.0 GPa | 1310 - 1600 ksi | Compression and Injection; ISO 527 |
Raschig Group RALUPOL® 4385 UP Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very high arc resistance, very high mechanical values. This product meets the allowed upper limits for heavy.. |
|||
Modulus of Elasticity | 9.00 - 11.0 GPa | 1310 - 1600 ksi | Injection and Compression; ISO 527 |
Raschig Group RALUPOL® 4806 UP Glass-fiber reinforced polyester molding compound. Very low mold shrinkage and post-shrinkage, very good mechanical strength, very good electrical values, better performance values compared to UP 80.. |
|||
Modulus of Elasticity | 9.00 - 11.0 GPa | 1310 - 1600 ksi | Compression; ISO 527 |
Raschig Group RALUPOL® 5000 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, excellent heat resistance, good mechanical strength. This product meets the all.. |
|||
Modulus of Elasticity | 0.750 - 11.0 GPa | 109 - 1600 ksi | Average value: 3.95 GPa Grade Count:46 |
Overview of materials for Polybutylene Terephthalate (PBT), Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Flame Retardant". Each property range of values reported is minimum an.. |
|||
Modulus of Elasticity | 7.40 - 11.0 GPa | 1070 - 1600 ksi | Average value: 9.35 GPa Grade Count:15 |
Overview of materials for Polycyclohexylenedimethylene Terephthalate (PCT), 30% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PCT or PCTA, 30% Glass Reinforced".Specific grades with glass content between 25% and 34% are included. .. |
|||
Modulus of Elasticity | 3.45 - 11.0 GPa | 500 - 1600 ksi | Average value: 6.46 GPa Grade Count:25 |
Overview of materials for Acetal Homopolymer, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, Glass Fiber Reinforced". Each property range of values reported is minimum and maxim.. |
|||
Modulus of Elasticity | 5.30 - 11.0 GPa | 769 - 1600 ksi | Average value: 6.79 GPa Grade Count:5 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 40% Glass Fiber Filled". Specific grades with glass content betwe.. |
|||
Modulus of Elasticity | 9.00 - 11.0 GPa | 1310 - 1600 ksi | Injection and Compression; ISO 527 |
Raschig Group SURAPLAST 54 UPA Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for.. |
|||
Modulus of Elasticity | 2.34 - 11.0 GPa | 340 - 1600 ksi | Average value: 5.60 GPa Grade Count:7 |
Overview of materials for Polycarbonate/Polysulfone Alloy This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/Polysulfone Alloy". Each property range of values reported is minimum and maximum values o.. |
|||
Modulus of Elasticity | 4.48 - 11.0 GPa | 650 - 1600 ksi | Average value: 6.01 GPa Grade Count:13 |
Overview of materials for Polyetherimide (PEI), 10% Glass Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 10% Glass Fiber". Specific grades with glass content between 5% and 14% are included. Ea.. |
|||
Modulus of Elasticity | 9.00 - 11.0 GPa | 1310 - 1600 ksi | Average value: 10.1 GPa Grade Count:6 |
Overview of materials for Phenolic, Novolac, Mineral/Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral/Fiber Filled". Each property range of values reported is minimum and maximum .. |
|||
Modulus of Elasticity | 1.80 - 11.0 GPa | 261 - 1600 ksi | Average value: 7.95 GPa Grade Count:43 |
Overview of materials for Nylon 66/6, 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are incl.. |
|||
Modulus of Elasticity | 2.41 - 11.0 GPa | 350 - 1600 ksi | Average value: 4.79 GPa Grade Count:42 |
Overview of materials for Nylon 66, Aramid Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Aramid Fiber Filled". Each property range of values reported is minimum and maximum values of .. |
|||
Modulus of Elasticity | 2.45 - 11.0 GPa | 355 - 1600 ksi | Average value: 5.41 GPa Grade Count:8 |
Overview of materials for Nylon 66, Mineral Filled, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Mineral Filled, Impact Grade". Each property range of values reported is minimum and maximum v.. |
|||
Modulus of Elasticity | 2.34 - 11.0 GPa | 340 - 1600 ksi | Average value: 4.89 GPa Grade Count:22 |
Overview of materials for Nylon 66, Stainless Steel Filled; EMI Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Stainless Steel Filled; EMI Grade". Each property range of values reported is minimum and maxi.. |
|||
Modulus of Elasticity | 7.50 - 11.0 GPa | 1090 - 1600 ksi | Average value: 8.92 GPa Grade Count:6 |
Overview of materials for Nylon 63, 35% Glass-Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 63, 35% Glass-Filled". Each property range of values reported is minimum and maximum values of app.. |
|||
Modulus of Elasticity | 3.40 - 11.0 GPa @Temperature 120 - 200 °C |
493 - 1600 ksi @Temperature 248 - 392 °F |
Average value: 5.89 GPa Grade Count:7 |
Overview of materials for Nylon 46, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Glass Fiber Reinforced". Each property range of values reported is minimum and maximum values .. |
|||
Modulus of Elasticity | 4.10 - 11.0 GPa | 595 - 1600 ksi | Average value: 8.69 GPa Grade Count:7 |
Overview of materials for Nylon 46, Lubricated + Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Lubricated + Glass Fiber Reinforced". Each property range of values reported is minimum and ma.. |
|||
Modulus of Elasticity | 9.00 - 11.0 GPa | 1310 - 1600 ksi | Injection; ISO 527 |
Raschig Group 5567 DAP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl phthalate molding compound free from halogens. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exc.. |
|||
Modulus of Elasticity | 3.30 - 11.0 GPa @Temperature -40.0 - 100 °C |
479 - 1600 ksi @Temperature -40.0 - 212 °F |
Average value: 5.19 GPa Grade Count:27 |
Overview of materials for Polypropylene with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are i.. |
|||
Modulus of Elasticity | 8.27 - 11.0 GPa | 1200 - 1600 ksi | ASTM D638 |
Premix Premi-Glas® 1200-24 Polyester SMC
(discontinued **) Premi-Glas® 1200-24 is a 24% fiberglass-reinforced, thermoset, sheet molding compound designed for Class A Heavy Truck - Bus body panels and Marine cowls parts where smooth, flat, ripple free surfa.. |