Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 8.30 GPa | 1200 ksi | ASTM D638 |
Owens Corning Glass Fiber Reinforced Polyester (PBT), 30 wt.% glass Thermoplastic Polyesters are resistant to most organic solvents, weak acids and alkalis. They are not recommended with strong acids and alkalis or for prolonged use in hot water. Data provided by t.. |
|||
Modulus of Elasticity | 8.27 - 20.7 GPa | 1200 - 3000 ksi | Average value: 10.9 GPa Grade Count:6 |
Overview of materials for PPE/PPO + Carbon Fiber This property data is a summary of similar materials in the MatWeb database for the category "PPE/PPO + Carbon Fiber". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Modulus of Elasticity | 8.27 - 26.2 GPa | 1200 - 3800 ksi | Average value: 17.4 GPa Grade Count:19 |
Overview of materials for Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler". Specific grades with carbon fiber content bet.. |
|||
Modulus of Elasticity | 8.30 GPa | 1200 ksi | |
Lehmann & Voss LUVOCOM® 50/CF/20 Polycarbonate, with carbon fiber, low-warpage Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Strong, stiff parts.Reduced moment of inertia compared with me.. |
|||
Modulus of Elasticity | 8.30 GPa | 1200 ksi | |
Lehmann & Voss Nylatron® MR 2007 Polyamide 6, with mineral filler Applications: Automotive industry, textile machinery, apparatus- and precision engineering.Low warpage.Isotropic shrinkage characteristics.Information provided by Lehmann & Voss & Co.KG |
|||
Modulus of Elasticity | 8.30 GPa | 1200 ksi | ISO 527-1/-2 |
BASF Ultramid® KR 4365 G5 35% Glass Filled PA6/6T FR (Dry) Description: Partially aromatic polyamide; flame retardant based on red phosphorus; low water absorption, high melting point (295°C); low tendency to form deposits on electrical contacts, very resi.. |
|||
Modulus of Elasticity | 8.30 GPa | 1200 ksi | ISO 178 |
Addiplast Addinyl PMD 20090 Nylon 6, 40% Glass Filled Glass fiber reinforced, high resistance to frictionInformation provided by Addiplast. |
|||
Modulus of Elasticity | 8.27 - 28.3 GPa | 1200 - 4100 ksi | Average value: 16.8 GPa Grade Count:3 |
Overview of materials for Polyphenylene Sulfide (PPS), NCG Fiber This property data is a summary of similar materials in the MatWeb database for the category "PPS + NGG". Each property range of values reported is minimum and maximum values of appropriate MatWeb e.. |