Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 12.0 - 14.0 GPa | 1740 - 2030 ksi | Compression; ISO 527 |
Raschig Group 4552 Silicone Glass fiber reinforced silicone molding compound. Excellent thermal stability - up to +/- 300°C continuously, excellent electrical properties, good mechanical strength, very good dimensional stabi.. |
|||
Modulus of Elasticity | 10.0 - 14.0 GPa | 1450 - 2030 ksi | Injection; ISO 527 |
Raschig Group 5562 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
Modulus of Elasticity | 10.0 - 14.0 GPa | 1450 - 2030 ksi | Injection; ISO 527 |
Raschig Group 5563 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
Modulus of Elasticity | 2.60 - 14.0 GPa | 377 - 2030 ksi | Average value: 6.52 GPa Grade Count:156 |
Overview of materials for Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled". Specific grades with glass content between 15.. |
|||
Modulus of Elasticity | 0.00159 - 14.0 GPa | 0.230 - 2030 ksi | Average value: 2.19 GPa Grade Count:16 |
Overview of materials for Silicone, Molded, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Silicone, Molded, Glass Fiber Filled". Each property range of values reported is minimum and maximum val.. |
|||
Modulus of Elasticity | 5.40 - 14.0 GPa @Temperature 60.0 - 150 °C |
783 - 2030 ksi @Temperature 140 - 302 °F |
Average value: 9.23 GPa Grade Count:1 |
Overview of materials for Nylon 66, 20% Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Carbon Fiber Filled". Specific grades with carbon fiber content between 15% and 24% are in.. |
|||
Modulus of Elasticity | 3.20 - 14.0 GPa | 464 - 2030 ksi | Average value: 5.74 GPa Grade Count:13 |
Overview of materials for Polyphenylene Sulfide (PPS), Unreinforced, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), Unreinforced, Extruded". Each property range of values reported is minimum .. |