Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Property : Modulus of Elasticity = 181 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, cold worked sheet, 20 % cold reduction
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 370°C (700°F) for 1 hour
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 595°C (1100°F) for 2 hours
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, hot rolled and 1230°C solution annealed sheet
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, cold rolled and 1205°C (2200°F) solution annealed sheet
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, cold worked sheet, 10% cold reduction
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, cold worked sheet, 15 % cold reduction
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature after 20% cold reduction, 1175°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature after 25% cold reduction
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature after 25% cold reduction, 1120°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature after 25% cold reduction, 1175°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature sheet after 1000 hours of 650°C exposure
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature sheet after 1000 hours of 870°C exposure
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature sheet after 2500 hours of 650°C exposure
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature sheet after 500 hours of 650°C exposure
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature sheet after 500 hours of 870°C exposure
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, sheet
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 181 GPa
26200 ksi
Carlson Nitronic® 60® Austenitic Stainless Steel
General DescriptionNitronic 60 is an anti-galling and wear resistant austenitic stainless steel. It provides a significantly lower cost alternative to combat wear and galling when compared with cob..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature after 10% cold reduction
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature after 10% cold reduction, 1065°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature after 15% cold reduction
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature after 15% cold reduction, 1120°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature after 15% cold reduction, 1175°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature after 20% cold reduction
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature after 20% cold reduction, 1120°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity 181 GPa

@Temperature 600 °C
26300 ksi

@Temperature 1110 °F
Haynes 25 alloy, room temperature after 15% cold reduction, 1065°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..