- Polymer Property : Modulus of Elasticity = 196 GPa
Polymer Property : Modulus of Elasticity = 196 GPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 196 GPa | 28400 ksi | RT |
| Outokumpu 4828 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and .. |
|||
| Modulus of Elasticity | 196 GPa | 28400 ksi | RT |
| Outokumpu 4833 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and .. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 300 °C |
28400 ksi @Temperature 572 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 300 °C |
28400 ksi @Temperature 572 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 300 °C |
28400 ksi @Temperature 572 °F |
|
| Haynes 230® alloy, 30% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 300 °C |
28400 ksi @Temperature 572 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 204 °C |
28400 ksi @Temperature 399 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, mill annealed HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 300 °C |
28400 ksi @Temperature 572 °F |
|
| Haynes 230® alloy, plate, 8000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 204 °C |
28400 ksi @Temperature 399 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, 0% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 204 °C |
28400 ksi @Temperature 399 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, 12.7-50.8 mm thick bar, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 204 °C |
28400 ksi @Temperature 399 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, 40% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 204 °C |
28400 ksi @Temperature 399 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, SMAW weld, 316L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 204 °C |
28400 ksi @Temperature 399 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, transverse, GMAW spray weldment, 23.4 mm thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 204 °C |
28400 ksi @Temperature 399 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 50% cold rolled and 1 hour at 500°C, air cooled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 196 GPa | 28400 ksi | |
| Carlson 904L Austenitic Stainless Steel General Description904L is an austenitic nickel-chromium stainless steel with molybdenum and copper additions. The elevated nickel and chromium content of 904L make it resistant to corrosion in a w.. |
|||
| Modulus of Elasticity | 196 GPa | 28400 ksi | typical of UNS N08800 |
| ATI Allegheny Ludlum Type 332 Stainless Steel, UNS N08800 Type 332 is a nickel and chromium austenitic stainless steel designed to resist oxidation and carburization at elevated temperatures. The nickel content, 32%, makes the alloy highly resistant both .. |
|||
| Modulus of Elasticity | 196 GPa | 28400 ksi | stress relieved |
| ATI Allegheny Ludlum Stainless Steel Type 301, Full Hard (UNS S30100) Allegheny Ludlum Type 301 is a high strength grade of steel available in six conditions or tempers, its resistance to atmosphere corrosion and its bright, attractive surface make it an excellent cho.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 300 °C |
28400 ksi @Temperature 572 °F |
|
| Haynes 230® alloy, hot rolled and 1232°C solution annealed plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 300 °C |
28400 ksi @Temperature 572 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 204 °C |
28400 ksi @Temperature 399 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, all-weld metal, SMAW HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 204 °C |
28400 ksi @Temperature 399 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, GMAW, as welded, unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 204 °C |
28400 ksi @Temperature 399 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, GTAW weld, 904L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 204 °C |
28400 ksi @Temperature 399 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, transverse, GTAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 204 °C |
28400 ksi @Temperature 399 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, transverse, GTAW spray weldment, 12.7 mm (1/2 in.) thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 204 °C |
28400 ksi @Temperature 399 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 0.71 mm thick sheet HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 300 °C |
28400 ksi @Temperature 572 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 300 °C |
28400 ksi @Temperature 572 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 204 °C |
28400 ksi @Temperature 399 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Modulus of Elasticity | 196 GPa @Temperature 204 °C |
28400 ksi @Temperature 399 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||