Polymer Property : Modulus of Elasticity = 204 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Modulus of Elasticity 204 GPa

@Temperature 200 °C
29600 ksi

@Temperature 392 °F
Haynes 214® alloy, 20% cold reduction, 980°C (1800°F) for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity 204 GPa

@Temperature 200 °C
29600 ksi

@Temperature 392 °F
Haynes 214® alloy, 40% cold reduction
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity 204 GPa

@Temperature 200 °C
29600 ksi

@Temperature 392 °F
Haynes 214® alloy, 40% cold reduction, 1095°C (2000°F) for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity 204 GPa

@Temperature 200 °C
29600 ksi

@Temperature 392 °F
Haynes 214® alloy, 50% cold reduction, 1095°C (2000°F) for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity 204 GPa

@Temperature 200 °C
29600 ksi

@Temperature 392 °F
Haynes 214® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity 204 GPa

@Temperature 200 °C
29600 ksi

@Temperature 392 °F
Haynes 214® alloy, sheet, 1000 hours exposure at 760°C (1400°F)
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity 204 GPa

@Temperature 200 °C
29600 ksi

@Temperature 392 °F
Haynes 214® alloy, sheet, 1000 hours exposure at 980°C (1800°F)
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity 204 GPa

@Temperature 300 °C
29600 ksi

@Temperature 572 °F
Haynes 25 alloy, cold worked sheet, 20 % cold reduction
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 204 GPa

@Temperature 300 °C
29600 ksi

@Temperature 572 °F
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 370°C (700°F) for 1 hour
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 204 GPa

@Temperature 300 °C
29600 ksi

@Temperature 572 °F
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 595°C (1100°F) for 2 hours
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 204 GPa

@Temperature 150 °C
29600 ksi

@Temperature 302 °F
Haynes HR-160® alloy plate, aged 1000 hours at 649°C (1200°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Modulus of Elasticity 204 GPa

@Temperature 150 °C
29600 ksi

@Temperature 302 °F
Haynes HR-160® alloy plate, aged 4000 hours at 649°C (1200°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Modulus of Elasticity 204 GPa

@Temperature 150 °C
29600 ksi

@Temperature 302 °F
Haynes HR-160® alloy, annealed plate
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Modulus of Elasticity 204 GPa

@Temperature 150 °C
29600 ksi

@Temperature 302 °F
Haynes HR-160® alloy, plate, aged 8000 hours at 871°C (1600°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Modulus of Elasticity 204 GPa

@Temperature 150 °C
29600 ksi

@Temperature 302 °F
Haynes HR-160® alloy, solution annealed sheet
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Modulus of Elasticity 204 GPa

@Temperature 300 °C
29600 ksi

@Temperature 572 °F
Haynes 25 alloy, cold rolled and 1205°C (2200°F) solution annealed sheet
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 204 GPa

@Temperature 300 °C
29600 ksi

@Temperature 572 °F
Haynes 25 alloy, room temperature after 25% cold reduction, 1065°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 204 GPa

@Temperature 300 °C
29600 ksi

@Temperature 572 °F
Haynes 25 alloy, room temperature after 25% cold reduction, 1120°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 204 GPa

@Temperature 300 °C
29600 ksi

@Temperature 572 °F
Haynes 25 alloy, room temperature sheet after 1000 hours of 650°C exposure
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 204 GPa

@Temperature 300 °C
29600 ksi

@Temperature 572 °F
Haynes 25 alloy, room temperature sheet after 1000 hours of 870°C exposure
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 204 GPa

@Temperature 300 °C
29600 ksi

@Temperature 572 °F
Haynes 25 alloy, room temperature sheet after 500 hours of 650°C exposure
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 204 GPa

@Temperature 300 °C
29600 ksi

@Temperature 572 °F
Haynes 25 alloy, room temperature sheet after 500 hours of 870°C exposure
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Modulus of Elasticity 204 GPa
29600 ksi
Special Metals INCONEL® 725 Nickel Superalloy (UNS N07725), Age Hardened Round
Tensile strength (ultimate and yield), hardness, impact, and elongation values reported here are typical for Age Hardened Round samples. Other property values are typical of INCONEL® alloy 725.D..
Modulus of Elasticity 204 GPa
29600 ksi
Carpenter Pyrowear® 675 Stainless Steel, Tempered 316°C, Longitudinal Properties
Data provided by Carpenter Technology Corporation.This is a carburizing, corrosion resistant steel designed to provide a case hardness in excess of HRC 60 combined with a tough, ductile core. The c..
Modulus of Elasticity 204 GPa

@Temperature 300 °C
29600 ksi

@Temperature 572 °F
Haynes 25 alloy, room temperature after 0% cold reduction
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity 204 GPa

@Temperature 300 °C
29600 ksi

@Temperature 572 °F
Haynes 25 alloy, room temperature after 10% cold reduction, 1175°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity 204 GPa

@Temperature 300 °C
29600 ksi

@Temperature 572 °F
Haynes 25 alloy, room temperature after 20% cold reduction
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity 204 GPa

@Temperature 300 °C
29600 ksi

@Temperature 572 °F
Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity 204 GPa

@Temperature 300 °C
29600 ksi

@Temperature 572 °F
Haynes 25 alloy, room temperature after 20% cold reduction, 1120°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Modulus of Elasticity 204 GPa

@Temperature 300 °C
29600 ksi

@Temperature 572 °F
Haynes 25 alloy, room temperature after 15% cold reduction, 1065°C anneal for 5 minutes
Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..