- Polymer Property : Modulus of Elasticity = 22500 ksi
Polymer Property : Modulus of Elasticity = 22500 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 155 GPa | 22500 ksi | |
| High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Bar, Hydrogen Annealed at 2150°F (1177°C) High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, 0% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, 10% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, 30% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, all-weld metal GTAW Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 537°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 0 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, 40% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Modulus of Elasticity | 155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||