| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 163 GPa @Temperature 500 °C |
23600 ksi @Temperature 932 °F |
|
| Outokumpu 253MA® High Temperature Austenitic Stainless Steel Variant of 1.4828 with increased nitrogen content and has been microalloyed with rare earth metals (REM). The most suitable temperature range is 850-1100°C, because structural changes when used be.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 705 °C |
23600 ksi @Temperature 1300 °F |
|
| Haynes HR-160® alloy plate, aged 4000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 900 °C |
23600 ksi @Temperature 1650 °F |
|
| Haynes 242® alloy, after 1000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 900 °C |
23600 ksi @Temperature 1650 °F |
|
| Haynes 242® alloy, after 8000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 900 °C |
23600 ksi @Temperature 1650 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and 40% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 900 °C |
23600 ksi @Temperature 1650 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed, 40% cold work, aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 800 °C |
23600 ksi @Temperature 1470 °F |
|
| Haynes 25 alloy, room temperature sheet after 2500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 700 °C |
23600 ksi @Temperature 1290 °F |
|
| Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 700 °C |
23600 ksi @Temperature 1290 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 700 °C |
23600 ksi @Temperature 1290 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 700 °C |
23600 ksi @Temperature 1290 °F |
|
| Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 760 °C |
23600 ksi @Temperature 1400 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, 20% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 760 °C |
23600 ksi @Temperature 1400 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, 60% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 760 °C |
23600 ksi @Temperature 1400 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, GTAW, aged 4000 hours at 450°C (800°F), unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 760 °C |
23600 ksi @Temperature 1400 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, SMAW weld, 316L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Modulus of Elasticity | 163 - 170 GPa | 23600 - 24700 ksi | |
| CLAL-MSX ARCAP Anticorrosion AP1 0 Annealed, Rolled Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin.. |
|||
| Modulus of Elasticity | 163 - 170 GPa | 23600 - 24700 ksi | |
| CLAL-MSX ARCAP Anticorrosion AP1 H12 1/2 hard, Drawn Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin.. |
|||
| Modulus of Elasticity | 163 - 170 GPa | 23600 - 24700 ksi | |
| CLAL-MSX ARCAP Anticorrosion AP1C H14 4/4 hard, Drawn Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un.. |
|||
| Modulus of Elasticity | 163 - 170 GPa | 23600 - 24700 ksi | |
| CLAL-MSX ARCAP Anticorrosion AP1 H15 Spring, Drawn Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin.. |
|||
| Modulus of Elasticity | 163 - 170 GPa | 23600 - 24700 ksi | |
| CLAL-MSX ARCAP Anticorrosion AP1C 0 Annealed, Rolled Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un.. |
|||
| Modulus of Elasticity | 163 - 170 GPa | 23600 - 24700 ksi | |
| CLAL-MSX ARCAP Anticorrosion AP1D H14 4/4 hard, Drawn Copper Alloy, Wire and rod, 2.5< diameter< 5 High Corrosion Resistance: ARCAP alloys are very corrosion resistant to the majority of chemical and physical environments. CLAL can provide data for the corrosion resistance of ARCAP alloys. In par.. |
|||
| Modulus of Elasticity | 163 - 170 GPa | 23600 - 24700 ksi | |
| CLAL-MSX ARCAP Anticorrosion AP1D H14 4/4 hard, Drawn Copper Alloy, Wire and rod, diameter High Corrosion Resistance: ARCAP alloys are very corrosion resistant to the majority of chemical and physical environments. CLAL can provide data for the corrosion resistance of ARCAP alloys. In par.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 800 °C |
23600 ksi @Temperature 1470 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 800 °C |
23600 ksi @Temperature 1470 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 800 °C |
23600 ksi @Temperature 1470 °F |
|
| Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 800 °C |
23600 ksi @Temperature 1470 °F |
|
| Haynes 25 alloy, room temperature after 20% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 760 °C |
23600 ksi @Temperature 1400 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, GMAW, as welded, unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 700 °C |
23600 ksi @Temperature 1290 °F |
|
| Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 760 °C |
23600 ksi @Temperature 1400 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, 0% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Modulus of Elasticity | 163 GPa @Temperature 760 °C |
23600 ksi @Temperature 1400 °F |
heat-treated at 1121°C (2050°F), rapid quenched, plate |
| Haynes Hastelloy® C-22® alloy, 6.4-19.1 mm thick plate, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||