Polymer Property : Modulus of Elasticity = 10.3 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	10.3 GPa @Thickness 1.57 mm	1500 ksi @Thickness 0.0620 in	CW; ASTM D229
Industrial Laminates/Norplex NP310 Cotton Fabric Description: Canvas machining grade for structural and mechanical applications. Better impact strength than phenolic paper grades. MIL-I-24768/16. Thickness Tested: 0.062, 0.125", and 0.500".
Modulus of Elasticity	10.3 GPa @Thickness 1.57 mm	1500 ksi @Thickness 0.0620 in	CW; ASTM D229
Industrial Laminates/Norplex NP310E Cotton Fabric Description: Manufactured with a domestic cotton fabric and phenolic resin. Similar to NP310 with improved moisture resistance and electrical properties. Mechanical properties equivalent to NP310. M..
Modulus of Elasticity	10.3 GPa @Thickness 1.57 mm	1500 ksi @Thickness 0.0620 in	LW; ASTM D229
Industrial Laminates/Norplex NP320U Cotton Fabric Description: Utility version of NP320E. Meets most, but not all, NEMA properties for L and LE, and is not certifiable as a NEMA Grade.Thickness Tested: 0.062", 0.125", and 0.500"
Modulus of Elasticity	10.3 GPa @Thickness 1.57 mm	1500 ksi @Thickness 0.0620 in	LW; ASTM D229
Industrial Laminates/Norplex NP322 Cotton Fabric Description: Linen phenolic laminate with molybdenum disulfide. Provides the same lubricity as NP313, but has better machining qualities. Mechanical strength similar to, but slightly less than NP320..
Modulus of Elasticity	10.3 GPa @Thickness 1.57 mm	1500 ksi @Thickness 0.0620 in	LW; ASTM D229
Industrial Laminates/Norplex NP325 Cotton Fabric Description: Linen phenolic laminate with graphite added as a solid lubricant. Linen substrate provides better machining and wear resistance than NP315.Thickness Tested: 0.062", 0.125" and 0.500".
Modulus of Elasticity	10.3 GPa @Thickness 1.57 mm	1500 ksi @Thickness 0.0620 in	LW; ASTM D229
Industrial Laminates/Norplex NP344 Cotton Fabric Description: Fine weave canvas laminate with high temperature phenolic resin and molybdenum disulfide lubricant. Good machining properties and low coefficient of thermal expansion. Better machining ..
Modulus of Elasticity	10.3 GPa @Thickness 1.57 mm	1500 ksi @Thickness 0.0620 in	LW; ASTM D229
Industrial Laminates/Norplex NP347 Cotton Fabric Description: Bleached canvas with high temperature phenolic resin with molybdenum disulfide lubricant. Low moisture absorption. Capable of 150Â°C continuous operation.Thickness Tested: 0.062", 0.1..
Modulus of Elasticity	10.3 GPa @Thickness 1.57 mm	1500 ksi @Thickness 0.0620 in	CW; ASTM D229
Industrial Laminates/Norplex NP634 Laminate Description: Warm punching, composite grade with woven glass covers for improved flexural, tensile and impact strength. Electrical properties comparable to NP611.Thickness Tested: 0.062", 0.125" and..
Modulus of Elasticity	10.3 GPa @Thickness 1.57 mm	1500 ksi @Thickness 0.0620 in	LW; ASTM D229
Industrial Laminates/Norplex NP639 Paper Base Laminate Description: Economical paper reinforced laminate developed with capacity to withstand temperatures to 150Â° C without blistering. High compressive strength and low moisture absorption.Thickness T..