Polymer Property : Modulus of Elasticity = 197 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Modulus of Elasticity 197 GPa

@Temperature 400 °C
28600 ksi

@Temperature 752 °F
Dynamic
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Bar, Hot Rolled and Solution Annealed
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Modulus of Elasticity 197 GPa

@Temperature 400 °C
28600 ksi

@Temperature 752 °F
Dynamic
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Modulus of Elasticity 197 GPa

@Temperature 200 °C
28600 ksi

@Temperature 392 °F
Haynes Hastelloy® X alloy, sheet
Solid-solution-strengthened with very good high-temperature strength and very good resistance to oxidizing environments up to about 1095°C, and good carburization resistance. Applications includ..
Modulus of Elasticity 197 GPa

@Temperature 427 °C
28600 ksi

@Temperature 801 °F
(heat treated at 1121°C (2050°F), water quenched plate)
Haynes Ultimet® alloy, 1.6 mm sheet
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Modulus of Elasticity 197 GPa

@Temperature 427 °C
28600 ksi

@Temperature 801 °F
(heat treated at 1121°C (2050°F), water quenched plate)
Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Modulus of Elasticity 197 GPa

@Temperature 427 °C
28600 ksi

@Temperature 801 °F
(heat treated at 1121°C (2050°F), water quenched plate)
Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Modulus of Elasticity 197 GPa

@Temperature 427 °C
28600 ksi

@Temperature 801 °F
(heat treated at 1121°C (2050°F), water quenched plate)
Haynes Ultimet® alloy, 12.7-50.8 mm bar
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Modulus of Elasticity 197 GPa

@Temperature 427 °C
28600 ksi

@Temperature 801 °F
(heat treated at 1121°C (2050°F), water quenched plate)
Haynes Ultimet® alloy, 6.3-38.1 mm plate
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Modulus of Elasticity 197 GPa

@Temperature 427 °C
28600 ksi

@Temperature 801 °F
(heat treated at 1121°C (2050°F), water quenched plate)
Haynes Ultimet® alloy, aged 1000 hours at 204°C (400°F)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Modulus of Elasticity 197 GPa

@Temperature 427 °C
28600 ksi

@Temperature 801 °F
(heat treated at 1121°C (2050°F), water quenched plate)
Haynes Ultimet® alloy, aged 1000 hours at 316°C
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Modulus of Elasticity 197 GPa

@Temperature 427 °C
28600 ksi

@Temperature 801 °F
(heat treated at 1121°C (2050°F), water quenched plate)
Haynes Ultimet® alloy, aged 1000 hours at 427°C (800°F)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Modulus of Elasticity 197 GPa

@Temperature 427 °C
28600 ksi

@Temperature 801 °F
(heat treated at 1121°C (2050°F), water quenched plate)
Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Modulus of Elasticity 197 GPa

@Temperature 427 °C
28600 ksi

@Temperature 801 °F
(heat treated at 1121°C (2050°F), water quenched plate)
Haynes Ultimet® alloy, aged 1000 hours at 649°C (1200°F)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Modulus of Elasticity 197 GPa

@Temperature 427 °C
28600 ksi

@Temperature 801 °F
(heat treated at 1121°C (2050°F), water quenched plate)
Haynes Ultimet® alloy, aged 1000 hours at 871°C (1600°F)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Modulus of Elasticity 197 GPa

@Temperature 427 °C
28600 ksi

@Temperature 801 °F
(heat treated at 1121°C (2050°F), water quenched plate)
Haynes Ultimet® alloy, aged 1000 hours at 982°C
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Modulus of Elasticity 197 GPa

@Temperature 427 °C
28600 ksi

@Temperature 801 °F
(heat treated at 1121°C (2050°F), water quenched plate)
Haynes Ultimet® alloy, all-weld metal, GMAW weld (short)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Modulus of Elasticity 197 GPa

@Temperature 427 °C
28600 ksi

@Temperature 801 °F
(heat treated at 1121°C (2050°F), water quenched plate)
Haynes Ultimet® alloy, all-weld metal, GMAW weld (spray)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Modulus of Elasticity 197 GPa

@Temperature 427 °C
28600 ksi

@Temperature 801 °F
(heat treated at 1121°C (2050°F), water quenched plate)
Haynes Ultimet® alloy, all-weld metal, GTAW weld
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Modulus of Elasticity 197 GPa

@Temperature 427 °C
28600 ksi

@Temperature 801 °F
(heat treated at 1121°C (2050°F), water quenched plate)
Haynes Ultimet® alloy, all-weld metal, SMAW weld
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Modulus of Elasticity 197 GPa

@Temperature 427 °C
28600 ksi

@Temperature 801 °F
(heat treated at 1121°C (2050°F), water quenched plate)
Haynes Ultimet® alloy, mill annealed
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Modulus of Elasticity 197 GPa

@Temperature 427 °C
28600 ksi

@Temperature 801 °F
(heat treated at 1121°C (2050°F), water quenched plate)
Haynes Ultimet® alloy, plate, GMAW weld (spray)
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Modulus of Elasticity 197 GPa

@Temperature 400 °C
28600 ksi

@Temperature 752 °F
Dynamic
Haynes 75 Nickel Alloy Sheet, Annealed at 1925°F (1050°C)
Haynes alloy 75 is a solution-strengthened nickel-chromium alloy with moderate strength to 1200°F (650°C). It is principally used in low stress elevated temperature applications requiring reas..
Modulus of Elasticity 197 GPa

@Temperature 400 °C
28600 ksi

@Temperature 752 °F
Dynamic
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Modulus of Elasticity 197 GPa

@Temperature 400 °C
28600 ksi

@Temperature 752 °F
Dynamic
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Sheet, Cold Rolled and Solution Annealed
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Modulus of Elasticity 197 GPa

@Temperature 400 °C
28600 ksi

@Temperature 752 °F
Dynamic
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing..
Modulus of Elasticity 197 GPa

@Temperature 20.0 °C
28600 ksi

@Temperature 68.0 °F
EDRO #7 Shock Resistant S7 Tool Steel
EDRO #7™ is a chromium-molybdenum steel characterized by: high toughness, good wear resistance, high impact resistance, good through hardening properties, good machinability, and good dimensional s..
Modulus of Elasticity 197 GPa

@Temperature 20.0 °C
28500 ksi

@Temperature 68.0 °F
EDRO UltraChem® #15 Precipitation Hardening Stainless Mold Steel
Ultrachem® is a chromium-nickel precipitation-hardening stainless steel, a modified PH alloy grade, which is characterized by: exceptional corrosion resistance, uniform hardness in all dimensions, ..
Modulus of Elasticity 197 GPa

@Temperature 20.0 °C
28500 ksi

@Temperature 68.0 °F
EDRO UltraChem® ESR #16 Precipitation Hardening Stainless Mold Steel
Ultrachem ESR® is a chromium-nickel precipitation-hardening stainless steel, a modified PH alloy grade, which is characterized by exceptional polishability, exceptional corrosion resistance, unifor..
Modulus of Elasticity 197 GPa

@Temperature 400 °C
28600 ksi

@Temperature 752 °F
Dynamic
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Plate, Hot Rolled and Solution Annealed
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing spe..
Modulus of Elasticity 197 GPa

@Temperature 400 °C
28600 ksi

@Temperature 752 °F
Dynamic
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate
HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing spe..