Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 50.0 - 100 MPa | 7250 - 14500 psi | 1.5mm/min; ISO 178:2001 |
Nylacast Aquanyl Nylon 612 Copolymer Aquanyl is a copolymer of Nylon 6 and Nylon 12 produced via the anionic polymerization process using the monomer's Caprolactam and Laurinlactam. It has reduced water absorption, improved stability a.. |
|||
Flexural Strength | 80.0 - 100 MPa | 11600 - 14500 psi | Compression; ISO 178 |
Raschig Group 2567 AMC Glass fiber-reinforced and inorganically filled polyester molding compound (UP) in various colors. Outstanding mechanical strength similar to BMC/SMC, very good electrical isolation properties and .. |
|||
Flexural Strength | 80.0 - 100 MPa | 11600 - 14500 psi | Compression; ISO 178 |
Raschig Group 2568 AMC Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s.. |
|||
Flexural Strength | 80.0 - 100 MPa | 11600 - 14500 psi | Compression; ISO 178 |
Raschig Group DECAL® 572R Phenolic Glass-fiber reinforced phenolic molding compound. Exceptional heat resistance with regard to maintaining surface finish and mechanical properties, outstanding mechanical properties, excellent rotati.. |
|||
Flexural Strength | 70.0 - 100 MPa | 10200 - 14500 psi | Injection and Compression; ISO 178 |
Raschig Group EPOXIDUR® 3580 EP Epoxy Glass-fiber reinforced and mineral filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties even with thin wall thicknesses and high temperatures. This prod.. |
|||
Flexural Strength | 70.0 - 100 MPa | 10200 - 14500 psi | Compression; ISO 178 |
Raschig Group MELOPLAS® 150 MF Wood flour-reinforced MF molding compound in dark colors. High surface hardness, high mechanical strength, good electrical properties. Self-extinguishing (V-O/1,6 according to UL 94), UL-listed. Fr.. |
|||
Flexural Strength | 80.0 - 100 MPa | 11600 - 14500 psi | Compression; ISO 178 |
Raschig Group MELOPLAS® 182 MF Wood flour-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in dark colors. Improved dimensional stability and electrical properties as compared with MP 180, high surf.. |
|||
Flexural Strength | 70.0 - 100 MPa | 10200 - 14500 psi | Compression; ISO 178 |
Raschig Group MELOPLAS® 183 MF Cellulose-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in white and colored shades. Improved dimensional stability and electrical properties as compared with MP 18.. |
|||
Flexural Strength | 80.0 - 100 MPa | 11600 - 14500 psi | Compression; ISO 178 |
Raschig Group MELOPLAS® 3025 MF Cellulose-reinforced and inorganically filled MF molding compound in white and colored shades. High surface hardness, good UV and heat stability, very good resistance to chemicals - also to foodstu.. |
|||
Flexural Strength | 80.0 - 100 MPa | 11600 - 14500 psi | Compression; ISO 178 |
Raschig Group RALUPOL® 4385 UP Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very high arc resistance, very high mechanical values. This product meets the allowed upper limits for heavy.. |
|||
Flexural Strength | 80.0 - 100 MPa | 11600 - 14500 psi | Compression; ISO 178 |
Raschig Group RALUPOL® 4802 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u.. |
|||
Flexural Strength | 70.0 - 100 MPa | 10200 - 14500 psi | Compression; ISO 178 |
Raschig Group RALUPOL® 4806 UP Glass-fiber reinforced polyester molding compound. Very low mold shrinkage and post-shrinkage, very good mechanical strength, very good electrical values, better performance values compared to UP 80.. |
|||
Flexural Strength | 80.0 - 100 MPa | 11600 - 14500 psi | Compression; ISO 178 |
Raschig Group RALUPOL® 802 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength, good heat resistance. This product meets the allowed up.. |
|||
Flexural Strength | 80.0 - 100 MPa | 11600 - 14500 psi | Compression; ISO 178 |
Raschig Group RALUPOL® 804 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy m.. |
|||
Flexural Strength | 80.0 - 100 MPa | 11600 - 14500 psi | Compression; ISO 178 |
Raschig Group SURAPLAST 54 UPA Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for.. |
|||
Flexural Strength | 80.0 - 100 MPa | 11600 - 14500 psi | DIN 54352 |
Schwartz Technical Plastics LAMINEX® 2000 Cotton Fabric, Phenolic Resin Impregnated, Coarse Application: rollneck-bearings, coverts for friction rollsInformation provided by Schwartz Technical Plastics GmbH |
|||
Flexural Strength | 80.0 - 100 MPa | 11600 - 14500 psi | DIN 54352 |
Schwartz Technical Plastics LAMINEX® 2040 Cotton Fabric, Phenolic Resin Impregnated, MoS2 Filled Application: slippers, gear-rods, bushesInformation provided by Schwartz Technical Plastics GmbH |
|||
Flexural Strength | 90.0 - 100 MPa | 13100 - 14500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP ZX08309 PPE+HIPS (Asia Pacific) This material is mineral filled PPO grade with high dielectric constant and low loss tangent |
|||
Flexural Strength | 80.0 - 100 MPa | 11600 - 14500 psi | At Rupture; ISO 178 |
Vyncolit X658 Novolac Phenolic Glass fiber and mineral filled phenolic molding compound with excellent mechanical and thermal properties and a very good dimensional stability.USES: Complex precision parts.Information provided by .. |
|||
Flexural Strength | 80.0 - 100 MPa | 11600 - 14500 psi | At Rupture; ISO 178 |
Vyncolit 2530 W Novolac Phenolic Mineral and organic filled phenolic molding compound with excellent thermal properties.USES: Lamp sockets, special lamp holders, pan handles and knobs.Information provided by Vyncolit, a Sumitomo Ba.. |
|||
Flexural Strength | 80.0 - 100 MPa | 11600 - 14500 psi | At Rupture; ISO 178 |
Vyncolit 2920 W Novolac Phenolic Mineral and organic filled molding compound with good dimensional stability and heat resistance.USES: Carburettor and intake manifold thermal insulator.Information provided by Vyncolit, a Sumitomo B.. |
|||
Flexural Strength | 50.0 - 100 MPa | 7250 - 14500 psi | |
Alliance BIF-11 Bonded (Composite) Magnetic Material |
|||
Flexural Strength | 50.0 - 100 MPa | 7250 - 14500 psi | |
Alliance BIF-17 Bonded (Composite) Magnetic Material |
|||
Flexural Strength | 50.0 - 100 MPa | 7250 - 14500 psi | |
Alliance BIF-19 Bonded (Composite) Magnetic Material |
|||
Flexural Strength | 50.0 - 100 MPa | 7250 - 14500 psi | |
Alliance BIF-2 Bonded (Composite) Magnetic Material |
|||
Flexural Strength | 50.0 - 100 MPa | 7250 - 14500 psi | |
Alliance BIF-16 Bonded (Composite) Magnetic Material |
|||
Flexural Strength | 80.0 - 100 MPa | 11600 - 14500 psi | Compression; ISO 178 |
Raschig Group 5567 DAP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl phthalate molding compound free from halogens. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exc.. |