Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 145 MPa | 21000 psi | Resin |
Renegade Materials Corporation RM-3002 Bismaleimide (BMI) Resin Developed using state-of-the-art formulating technologies, RM-3002 BMI prepreg products deliver superior hot/wet performance in airframe, missile and propulsion applications at service temperatures .. |
|||
Flexural Strength | 145 MPa | 21000 psi | Resin |
Renegade Materials Corporation RM-3002 Bismaleimide (BMI) Resin 4581 Astroquartz III Developed using state-of-the-art formulating technologies, RM-3002 BMI prepreg products deliver superior hot/wet performance in airframe, missile and propulsion applications at service temperatures .. |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
LNP Lubricomp® PDX-E-00548 CCS Polyetherimide, Aramid Fiber Reinforced, PTFE Lubricant
(discontinued **) Features: Lubricated, Low to None Ion ContentForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however man.. |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
Ravago Manufacturing Americas Hylon® N1033STL Nylon 6/6 (Cond)
(discontinued **) Information provided by Ravago. |
|||
Flexural Strength | 145 MPa | 21000 psi | |
Lehmann & Voss LUVOCOM® 50-8076 Polycarbonate, with carbon fiber Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High dimensionally stable precision parts with low warpage and.. |
|||
Flexural Strength | 145 MPa | 21000 psi | |
Lehmann & Voss LUVOCOM® 80-7713 Polyacetal-copolymer, with carbon fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Electrically conductive, suita.. |
|||
Flexural Strength | 145 MPa | 21100 psi | ASTM D790 |
Greene Tweed Arlon® 1330 PEEK Arlon® is a tough, high-temperature, semi-crystalline, thermoplastic presenting a unique combination of mechanical, thermal, chemical and electrical properties. Greene, Tweed uses several proprie.. |
|||
Flexural Strength | 145 MPa | 21000 psi | |
Lehmann & Voss LUVOCOM® 1105-7106 PEEK, with carbon fiber, PTFE, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts,.. |
|||
Flexural Strength | 145 MPa | 21000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® 815 PBT (Europe-Africa-Middle East) VALOX 815 is a 15% glass reinforced PBT+PET blend with excellent surface finish. Applications: hot air gun housings assemblies, industrial glue guns, appliance housings and handles. |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
Techmer ES HiFill® PA6 GB36 IM1 BK 36% Glass Bead Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 36% Filler by WeightAdditive: Lubricant Features: LubricatedAppearance: BlackInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 145 MPa | 21000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC202M PPE+PS DATA ON BK1005 ONLY. |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Stat-kon NX03602 PC+ABS LNP STAT-KON* NX03602 is a compound based on PC+ABS Blend resin containing Carbon Fiber, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supplied by .. |
|||
Flexural Strength | 145 MPa | 21000 psi | 20 x 40 mm |
CeramTec 665 Steatite, MgO•SiO2 Steatites used in place of aluminas are a cost-effective way to meet performance requirements. They are easier to form and fire at lower temperatures. 665 L533C has low dielectric loss. It makes exc.. |
|||
Flexural Strength | 145 MPa | 21000 psi | ISO 178-93 |
Wellman Wellamid® MRGF30/10 42H-NBK1 Nylon 6, 30% Mineral and 10% Glass Reinforced All information provided by Wellman Engineered Resins. |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
Toyobo VYLOPET® EMC310 Injection Molding Polyester Resin Applications: Coiled bobbinsMouthpiecesFeatures: High cyclesInformation provided by Toyobo. |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
Ensinger Tecapeek® XP-91 Compression Molded PEEK Compound, 30% Fiberglass Ensinger Special Polymers offers over twenty different VICTREX® PEEK blends to choose from and has the capability to blend custom compounds for specific applications. Compression molding results in.. |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
A. Schulman ComAlloy Hiloy® 638 Nylon 6/6, Mineral Reinforced, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company.35% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
Beijing Ranger Chem PBT-201-G10 211 Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
Techmer ES HiFill FR® PA6 GF15 FR-N 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Flame Retardant, Heat Stabilized, Halog.. |