Polymer Property : Flexural Strength = 167 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	167 MPa	24200 psi
Quadrant EPP Duratron® PEI U1000 PEI, unfilled, extruded (ISO Data) Duratron U1000 PEI is an amber translucent (non-optical quality) amorphous thermoplastic material, offering high strength and heat resistance. It performs continuously to 170 °C, making it ideal fo..
Flexural Strength	167 MPa @Temperature 150 °C	24200 psi @Temperature 302 °F	ASTM D790
Mitsui AURUM® JGN6230 Thermoplastic Polyimide Resin, Amorphous (discontinued **) AURUM® is an easy melt, processable and recyclable thermoplastic polyimide resin that provides continuous service temperatures to 465° F in its amorphous state and up to 550° F when annealed to i..
Flexural Strength	167 MPa	24200 psi	ASTM D790
LG Chemical LUCON SE-4200H Electrically Conductive Thermoplastic LG Chemicals has formulated a diverse range of LUCON thermoplastic compounds containing conductive additives, such as carbon powder, (nickel coated) carbon fiber, or stainless steel fiber for solvin..
Flexural Strength	167 MPa	24200 psi	ASTM D790
Kolon SPESINÂ® KP212G15V0BM G/F Reinforced & Flame Retardant PBT Compound Resin Flame retardant, paintabilityApplications: A variety of cases and connectorsInformation provided by API-Kolon.
Flexural Strength	167 MPa	24200 psi	ASTM D790
Kolon SPESINÂ® KP213G15BL Glass Fiber Reinforced PBT Compound Resin b>Characteristics: G/F 15% reinforced, BLACKApplications: Impeller housingsInformation provided by API-Kolon.
Flexural Strength	167 MPa	24200 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP PDX-U-05314 PPA (Asia Pacific) LNP* Lubricomp* PDX-U-05314 is a compound based on Polyphthalamide resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated.
Flexural Strength	167 MPa	24200 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RX94033 PA6.6 (Europe-Africa-Middle East) LNP* LUBRICOMP* RX94033 is a compound based on PA 66 resin containing Aramide Fiber, Glass Fiber, PTFE. Added features include: Internally Lubricated.
Flexural Strength	167 MPa	24200 psi	ISO 178
SABIC Innovative Plastics LNP LUBRILOY RF206 PA 66 LNP LUBRILOY* RF206 is a compound based on Nylon 66 resin containing 30% Glass Fiber, Proprietary Lubricant, Added features of this material includes: Wear Resistant.
Flexural Strength	167 MPa	24200 psi	ISO 178
SABIC Innovative Plastics LNP LUBRILOY RF206AXH PA 66 LNP LUBRILOY* RF206AXH is a compound based on Nylon 66 resin containing 30% Glass Fiber, Proprietary Lubricant, Added features of this material include: Wear Resistant, Healthcare.
Flexural Strength	167 MPa	24200 psi	ASTM D790
Techmer ES HiFillÂ® PES GF20 TL15 LE 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightPTFE LubricantFeatures: Low Extractables and LubricatedInformation provided by TP Compos..
Flexural Strength	167 MPa	24200 psi	ASTM D790
Techmer ES LuriblendÂ® PA6/6 GF13 ML2 13% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 13% Filler by WeightAdditive: Heat Stabilizer and Molybdenum Disulfide Lubricant(2%)Features: Lubricated and Heat Stabiliz..
Flexural Strength	167 MPa	24200 psi	ISO 178
SABIC Innovative Plastics LNP STAT-KON DEI13F PC LNP* STAT-KON* DEI13F is a compound based on Polycarbonate resin containing 15% Carbon Fiber, 2% Silicone. Added features of this material include: Electrically Conductive, Superior Molding, Wear R..
Flexural Strength	167 MPa	24200 psi	ASTM D790
Chase Plastics CP Pryme® N130GL (COND, 50% RH) Nylon 6, 30% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics.
Flexural Strength	167 MPa	24200 psi	Dry; ASTM D790
Asahi Kasei Leona® 14G15 15% Glass Filled Nylon 66 15% Glass Fiber Reinforced. Enhanced strength and stiffnessApplications:Heater tanks, fuel injectors, ABS sensors, and other under-the-hood automotive parts Information provided by Asahi Kasei
Flexural Strength	167 MPa	24200 psi	2.8mm/min; ASTM D790
Asia International Enterprise (Hong Kong) 60G2-13GF Nylon 66, 13% Filled Information provided by Asia International Enterprise (Hong Kong) Ltd.
Flexural Strength	167 MPa	24200 psi	ASTM D790
Beijing Chemical Industry KAIFA® 304-G30 PBT Resin 30% glass fiber reinforced, flame retardant, low bleeding, UV-resistantInformation provided by Beijing Chemical Industry Research Institute (Group)
Flexural Strength	167 MPa	24200 psi	2.8mm/min; ASTM D790
Asia International Enterprise (Hong Kong) ST60G3 Nylon 66, 15% Filled Information provided by Asia International Enterprise (Hong Kong) Ltd.