Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
PolyOne LubriOne™ PC-20GF/15T Polycarbonate (PC) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
Flexural Strength | 145 MPa | 21000 psi | Resin |
Renegade Materials Corporation RM-3000 Bismaleimide (BMI) 6781 S2 Glass Fabric Developed using state-of-the-art formulating technologies, RM-3000 One Part BMI RTM Resin delivers superior hot/wet performance in airframe, missile and
propulsion applications at service temperatu.. |
|||
Flexural Strength | 145 MPa | 21000 psi | Resin |
Renegade Materials Corporation RM-3002 Bismaleimide (BMI) Resin Developed using state-of-the-art formulating technologies, RM-3002 BMI prepreg products deliver superior hot/wet performance in airframe, missile and propulsion applications at service temperatures .. |
|||
Flexural Strength | 145 MPa | 21000 psi | Resin |
Renegade Materials Corporation RM-3002 Bismaleimide (BMI) Resin 4581 Astroquartz III Developed using state-of-the-art formulating technologies, RM-3002 BMI prepreg products deliver superior hot/wet performance in airframe, missile and propulsion applications at service temperatures .. |
|||
Flexural Strength | 145 MPa | 21000 psi | |
Plastcom SLOVAMID 6 NG GF 15 HI PA6, 15% glass fibre, improved strength FeaturesPA 6 for injection moulding, chemically strengthened with 15% glass fibre. Application: impacted mouldings and mouldings with high strength applied in automotive, electrical, engineering and.. |
|||
Flexural Strength | 145 MPa | 21000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP DFL34EH PC LNP* LUBRICOMP* DFL34EH is a compound based on Polycarbonate containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Easy Molding, Healthcare, Wear Resistant. |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
Rostone Rosite® C200BS ESD SMC, Conductive Thermoset Polyester, 10% Glass Reinforced
(discontinued **) Key Features: Electrostatic DissipativeRosite Conductive C used in applications such as molded paper guides in printers and plotters. Conductive C is the UL recognition.Information provided by Onei.. |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
IDI Composites 44-10 HGM Thermoset Polyester, Molding Same as 44-10 HG with Mil Spec MAI-60.Data provided by the manufacturer. |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
IDI Composites M-104 Thermoset Polyester, Molding Mechanical grade materials in a range of strengths with excellent moldability and molded part appearance.Data provided by the manufacturer. |
|||
Flexural Strength | 145 MPa | 21000 psi | 2.0 in/min; ASTM D790 |
LTL Color Compounds ColorFast® FRPBT150 PBT, 13% Glass-Filled, Flame Retarded 13% glass-filled V-0 rated PBTAll information provided by LTL Color Compounders, Inc. |
|||
Flexural Strength | 145 MPa | 21000 psi | ISO 178 |
Mitsubishi Xantar® G4F 23 R Polycarbonate-20% Glass Reinforced Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Flexural Strength | 145 MPa @Temperature 22.0 °C |
21000 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
Menzolit Menzolit® SMC 2500 Unsaturated Polyester UP SMC 2500 is a special SMC for high voltage isolating applications. The glass level has been selected to combine good mouldability with good strength and stiffness properties. Even without a specific.. |
|||
Flexural Strength | 145 MPa | 21000 psi | ISO 178 |
Mitsubishi Xantar® MX 1082 Polycarbonate-20% Glass Reinforced Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Flexural Strength | 145 MPa | 21000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® 815 PBT (Europe-Africa-Middle East) VALOX 815 is a 15% glass reinforced PBT+PET blend with excellent surface finish. Applications: hot air gun housings assemblies, industrial glue guns, appliance housings and handles. |
|||
Flexural Strength | 145 MPa | 21000 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC202M PPE+HIPS (Europe-Africa-Middle East) DATA ON BK1005 ONLY. |
|||
Flexural Strength | 145 MPa | 21000 psi | ISO 178 |
SABIC Innovative Plastics LNP Stat-kon NX03602 PC+ABS LNP STAT-KON* NX03602 is a compound based on PC+ABS Blend resin containing Carbon Fiber, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supplied by .. |
|||
Flexural Strength | 145 MPa | 21000 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Stat-kon NX03602 PC+ABS LNP STAT-KON* NX03602 is a compound based on PC+ABS Blend resin containing Carbon Fiber, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supplied by .. |
|||
Flexural Strength | 145 MPa | 21000 psi | at rupture; ASTM D790 |
Sumitomo Bakelite North America E 2748-9641D Short Glass Fiber Reinforced Epoxy E 2748-9641D is a mineral and short fiberglass filled epoxy molding compound.Information provided by Sumitomo Bak North America, Inc. |
|||
Flexural Strength | 145 MPa | 21000 psi | 20 x 40 mm |
CeramTec 665 Steatite, MgO•SiO2 Steatites used in place of aluminas are a cost-effective way to meet performance requirements. They are easier to form and fire at lower temperatures. 665 L533C has low dielectric loss. It makes exc.. |
|||
Flexural Strength | 145 MPa | 21000 psi | ISO 178-93 |
Wellman Wellamid® MRGF30/10 42H-NBK1 Nylon 6, 30% Mineral and 10% Glass Reinforced All information provided by Wellman Engineered Resins. |
|||
Flexural Strength | 145 MPa | 21000 psi | ISO 178 |
Polyram Polytron P30N03 Polypropylene, 30% Long Glass Fibers A chemically coupled 30% long glass fibers reinforced natural polypropylene, heat stabilized, for injection molding applications. These products have significantly improved impact performance chara.. |
|||
Flexural Strength | 145 MPa | 21000 psi | |
Plastcom SLOVALEN PH 69 GF 40 PP, 40% glass fibre, mod. of mech. properties FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 40% glass fibre, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP... |