Polymer Property : Flexural Strength = 212 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	212 MPa	30700 psi	ASTM D790
PolyOne Stat-Tech™ PI-05CF/000R Black Polyether Imide (PEI) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound..
Flexural Strength	212 MPa @Temperature 150 °C	30700 psi @Temperature 302 °F	ASTM D790
Mitsui AURUM® JCL3030 Thermoplastic Polyimide Resin, Amorphous, Wear/Friction Grade (discontinued **) AURUM® is an easy melt, processable and recyclable thermoplastic polyimide resin that provides continuous service temperatures to 465° F in its amorphous state and up to 550° F when annealed to i..
Flexural Strength	212 MPa	30700 psi	ASTM D790
Greene Tweed WRâ„¢ 300 PEEK, Carbon Filled WRÂ®300 is a carbon-fiber reinforced compression molded PEEK often selected by pump manufacturers and users for pump bushings and case or impeller wear rings. Maximum service life is achieved in ..
Flexural Strength	212 MPa	30700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP OCL13XXP PPS - LINEAR (Europe-Africa-Middle East) LNP* Stat-kon* OCL13XXP is a compound based on PPS - LINEAR resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive.
Flexural Strength	212 MPa	30700 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP QFP36 PA 6/10 LNP LUBRICOMP* QFP36 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of this material include: Wesr Resistant.
Flexural Strength	212 MPa	30700 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP QFP36 PA 6/10 (Asia Pacific) LNP LUBRICOMP* QFP36 is a compound based on Nylon 6/10 resin containing Silicone, PTFE, Glass Fiber. Added features of this material include: Internally Lubricated.
Flexural Strength	212 MPa	30700 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON DE0069F PC LNP* STAT-KON* DE0069F is a compound based on Polycarbonate resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Superior Molding.
Flexural Strength	212 MPa	30700 psi	ASTM D790
Techmer ES HiFillÂ® PA6 GF20 L 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by Weight Processing Method: Injection MoldingInformation provided by TP Composites, Inc.
Flexural Strength	212 MPa	30700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Stat-kon OCL13 PPS - LINEAR (Europe-Africa-Middle East) LNP* Stat-kon* OCL13 is a compound based on PPS - LINEAR resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for..
Flexural Strength	212 MPa	30700 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON OCL13XXP PPS - LINEAR (Europe-Africa-Middle East) LNP* Stat-kon* OCL13XXP is a compound based on PPS - LINEAR resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive.
Flexural Strength	212 MPa	30700 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Stat-kon WEF42 PET/PBT LNP Stat-Kon WCF-1006 is a compound based on PET/PBT resin containing carbon and glass fiber reinforcements.This data was supplied by SABIC-IP for the Americas region.
Flexural Strength	212 MPa	30700 psi	2 mm/min; ISO 178
Sax Polymers SAXAMID 126F3 Nylon 6, 15% Glass Fiber SAXAMID 126F3 is a polyamide 6 injection-molding-grade reinforced with 15% glass fibers.Information provided by SAX Polymers
Flexural Strength	212 MPa	30700 psi	ISO 178
Polyplastics Duranex® C5330 Polybutylene Terephthalate (PBT), Higher gloss, Better surface appearance, 30% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Flexural Strength	212 MPa	30700 psi	ISO 178
Polyplastics Duranex® CN5330 Polybutylene Terephthalate (PBT), Higher gloss, Better surface appearance, 30% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Flexural Strength	212 MPa	30700 psi	ISO Data
BASF Ultradur B 2300 G6 HR BK15116 30% Glass Filled PBT Ultradur B 2300 G6 HR BK15116 is a hydrolysis resistant, pigmented black 30% fiberglass reinforced PBT, exhibiting superior flow characteristics. Designed for improved latch strength in automotive..
Flexural Strength	212 MPa	30700 psi	ASTM Test
BASF Ultramid® 8234G HS 44% Glass Filled PA6 (Conditioned) Ultramid 8234G HS is a heat stabilized, 44% glass fiber reinforced polyamide 6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensio..
Flexural Strength	212 MPa	30700 psi	ISO 178
SABIC Innovative Plastics LNP THERMOTUF OF006I PPS - Linear LNP THERMOTUF* OF006I is a compound based on PPS - Linear resin containing Glass Fiber. Added features of this material include: High Impact.