- Polymer Property : Flexural Strength = 21500 psi
Polymer Property : Flexural Strength = 21500 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 148 MPa | 21500 psi | |
| Plastcom SLOVAMID 6 GF 20 GB 10 PA6, 20% glass fibre, 10% glass beads FeaturesPA 6 for injection moulding, chemically strengthened with 20% glass fibre and 10% glass beads. Application: impacted mouldings and mouldings with high strength applied in automotive, electri.. |
|||
| Flexural Strength | 148 MPa | 21500 psi | ASTM D790 |
| Niche Polymer PPHG40BK Homopolymer PP, 40% Glass Fiber Filled Information provided by Niche Polymer |
|||
| Flexural Strength | 148 MPa @Thickness 3.17 mm |
21500 psi @Thickness 0.125 in |
ASTM D790 |
| PTS 15GFR-BK PBT- Flame Retardant, 15% Glass Filled PBT Black Resin Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Flexural Strength | 148 MPa | 21500 psi | ASTM D790 |
| Solvay Specialty Polymers Amodel® AP-9240 NL Polyphthalamide (PPA) Resin, 40% Mineral Filled, Dry as Molded
( AMODEL AP-9240 NL resin is a 40% mineral-filled, impact-modified polyphthalamide (PPA). It was designed to provide a smooth molded surface suitable for many decorative applications. This resin offer.. |
|||
| Flexural Strength | 148 MPa | 21500 psi | ASTM D790 |
| Solvay Specialty Polymers Udel® GF-120 Polysulfone (PSU)
(Unverified Data**) Udel GF-120, resin is a 20% glass fiber reinforced polysulfone compound. Glass fiber substantially increases the rigidity, tensile strength, creep resistance, dimensional stability and chemical resi.. |
|||
| Flexural Strength | 148 MPa @Temperature 23.0 °C |
21500 psi @Temperature 73.4 °F |
DAM; ASTM D790 |
| DuPont Performance Polymers Minlon® 10B40HS1 BK061 Nylon 66
(Unverified Data**) Minlon® 10B40HS1 BK061 is a 40% mineral reinforced, heat stabilized, black polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
| Flexural Strength | 148 MPa | 21500 psi | ASTM D790 |
| MRC Polymers NAXALOYâ„¢ 770 GF16 ABS+PC Alloy, 16% Glass Fiber Filled Can be UV StabilizedInternal and external lubricant can be addedInformation provided by MRC Polymers Inc. |
|||
| Flexural Strength | 148 MPa | 21500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1520A PC (Asia Pacific) 20% glass reinforced/15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances. |
|||
| Flexural Strength | 148 MPa | 21500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1520A PC (Europe-Africa-Middle East) LNP* Lubricomp* Lexan_FL1520 compound is a 20% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances. |
|||
| Flexural Strength | 148 MPa | 21500 psi | ASTM D790 |
| Techmer ES Electrablend® PA6/6 GF13 SS10 BK 13/10% Glass/Stainless Steel Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber/Stainless Steel Reinforcement, 13/10% Filler by WeightFeatures: Electromagnetic Shielding (EMI)Appearance: BlackInformation.. |
|||
| Flexural Strength | 148 MPa | 21500 psi | ASTM D790 |
| Solvay Specialty Polymers Udel® GF-120 Polysulfone (PSU), Glass Fiber Udel® GF-120, resin is a 20% glass fiber reinforced polysulfone compound. Glass fiber substantially increases the rigidity, tensile strength, creep resistance, dimensional stability and chemical .. |
|||
| Flexural Strength | 148 MPa | 21500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON Noryl_NC2525 PPE+HIPS (Europe-Africa-Middle East) LNP* Stat-kon* Noryl_NC2525 compound is a 25% CFR PPE+PS. Highly conductive. High heat. May be added to similar material/regrind to add some conductivity to the blend. |
|||
| Flexural Strength | 148 MPa | 21500 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP STAT-KON RFD03 PA 66 (Asia Pacific) LNP* STATKON* RFD03 is a compound based on PA 66 resin contaning Carbon Powder, Glass Fiber. Added features include: Electrically Conductive. |
|||
| Flexural Strength | 148 MPa | 21500 psi | Method I (3 point load), 2.0 mm/min; ISO 178; ASTM D790 |
| Styron CALIBREâ„¢ 5201-12 Polycarbonate Resin Overview: CALIBREâ„¢ 5201-12 polycarbonate resin is 20% glass reinforced containing mold release for optimal processing. This resin exhibits high modulus and excellent dimensional stability. CALI.. |
|||
| Flexural Strength | 148 MPa | 21500 psi | Method I (3 point load), 2.0 mm/min; ISO 178; ASTM D790 |
| Styron CALIBREâ„¢ 5201-8 Polycarbonate Resin Overview: CALIBREâ„¢ 5201-8 polycarbonate resin is 20% glass reinforced containing mold release for optimal processing. This resin exhibits high modulus and excellent dimensional stability. CALIB.. |
|||
| Flexural Strength | 148 MPa @Temperature -40.0 °C |
21500 psi @Temperature -40.0 °F |
ASTM Test |
| BASF Ultramid® 8253 HS PA6 (Dry) Ultramid 8253 HS is a heat stabilized, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications requiring improved dry as molded toughness and increased.. |
|||
| Flexural Strength | 148 MPa @Temperature -40.0 °C |
21500 psi @Temperature -40.0 °F |
ASTM Test |
| BASF Ultramid® 8253 PA6 (Dry) Ultramid 8253 is an unfilled, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Ultramid 8253 HS) and/o.. |
|||
| Flexural Strength | 148 MPa | 21500 psi | ASTM D790 |
| Applied Composites 8072 Polyester SMC Industry Application: TransportationProduct Application: AutomotiveDistinct Features: Zero Shrink, Superior Class A Finish, Improved Impact, Accepts Mold CoatingInformation provided by Applied Compo.. |
|||
| Flexural Strength | 148 MPa | 21500 psi | ASTM D790 |
| A. Schulman ComAlloy Hiloy® 515 Polycarbonate, Carbon Fiber Reinforced Data provided by the manufacturer, ComAlloy International Company.10% Carbon Fiber Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Flexural Strength | 148 MPa | 21500 psi | ASTM D790 |
| Applied Composites 120 Polyester SMC Industry Application: ElectricalProduct Application: Transmission ProductDistinct Features: Pigmentable UL 94 V-5, Stable @ 600 Hour QUV Accelerated Weather Testing, Passed 6 Mos. AZ Outdoor Weather.. |
|||
| Flexural Strength | 148 MPa | 21500 psi | ISO 178 |
| SABIC Innovative Plastics LNP STAT-KON OE002 PPS - LINEAR LNP* STAT-KON* OE002 is a compound based on PPS - Linear resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive. |
|||
| Flexural Strength | 148 MPa | 21500 psi | ASTM D790 |
| SABIC Innovative Plastics NORYL PX2934 PPE+PS (Asia Pacific) PPE+PS GF20% High Heat Non-FR |
|||
| Flexural Strength | 148 MPa | 21500 psi | ASTM D 790 |
| SABIC Innovative Plastics Valox® VC108 PBT (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Flexural Strength | 148 MPa | 21500 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP JF004L PES LNP* THERMOCOMP* JF004L is a compound is based on Polyethersulfone containing 20% Glass Fiber. Characteristics of this grade is: Low Extractible |
|||