Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 130 - 150 MPa | 18900 - 21800 psi | Injection; ISO 178 |
Raschig Group 2557 AMC Polyester Glass fiber reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, exceptional processability with short cycle time and low .. |
|||
Flexural Strength | 120 - 150 MPa | 17400 - 21800 psi | Injection; ISO 178 |
Raschig Group 6552 DAIP Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi.. |
|||
Flexural Strength | 130 - 150 MPa | 18900 - 21800 psi | At Rupture; ISO 178 |
Vyncolit X681 Novolac Phenolic Glass fiber filled phenolic molding compound with excellent mechanical properties and a low coefficient of friction. Tribological compound with PTFE additive.USES: Water pump seals and self-lubrica.. |
|||
Flexural Strength | 90.0 - 150 MPa | 13100 - 21800 psi | |
Alliance S-26B Samarium Cobalt Magnetic Material |
|||
Flexural Strength | 90.0 - 150 MPa | 13100 - 21800 psi | |
Alliance S-28A Samarium Cobalt Magnetic Material |
|||
Flexural Strength | 90.0 - 150 MPa | 13100 - 21800 psi | |
Alliance S-28B Samarium Cobalt Magnetic Material |
|||
Flexural Strength | 90.0 - 150 MPa | 13100 - 21800 psi | |
Alliance S-30A Samarium Cobalt Magnetic Material |
|||
Flexural Strength | 90.0 - 150 MPa | 13100 - 21800 psi | |
Alliance S-30B Samarium Cobalt Magnetic Material |
|||
Flexural Strength | 90.0 - 150 MPa | 13100 - 21800 psi | |
Alliance S-28H Samarium Cobalt Magnetic Material |
|||
Flexural Strength | 90.0 - 150 MPa | 13100 - 21800 psi | |
Alliance S-32 Samarium Cobalt Magnetic Material |
|||
Flexural Strength | 90.0 - 150 MPa | 13100 - 21800 psi | |
Alliance S-26H Samarium Cobalt Magnetic Material |