Mechanical Properties Metric English Comments
Flexural Strength 211 MPa
30600 psi
ASTM D790
Solvay Specialty Polymers AvaSpire® AV-742 SL30 Polyaryletherketone (PAEK)  (Unverified Data**)
AV-742 SL30 is a wear resistant grade of AvaSpire polyaryletherketone (PAEK) designed to provide low wear rates in both non-lubricated and lubricated environments. In addition to outstanding wear re..
Flexural Strength 211 MPa
30600 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RFL36S PA 66
LNP* LUBRICOMP* RFL36S is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Heat Stabilized.
Flexural Strength 211 MPa
30600 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RFL36XXY PA 66
LNP* LUBRICOMP* RFL36XXY is a compound based on Nylon 66 containing 30% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant.
Flexural Strength 211 MPa
30600 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RFL36XXZ PA 66
LNP* LUBRICOMP* RFL36XXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant.
Flexural Strength 211 MPa
30600 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RFP36 PA 66 (Europe-Africa-Middle East)
LNP* Lubricomp* RFP36 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE, Silicone.
Flexural Strength 211 MPa

@Temperature 23.0 °C
30600 psi

@Temperature 73.4 °F
4; ISO 178
Solvay Specialty Polymers Amodel® A-1565 HS Polyphthalamide (PPA), 65% GlassMineral (Dry)
Amodel® A-1565 HS is a 65% glass and mineral-reinforced polyphthalamide (PPA) designed to be cost-effective in applications requiring high stiffness, good dimensional stability and good retention..
Flexural Strength 211 MPa
30600 psi
ISO 178
SABIC Innovative Plastics LNP LUBRILOY RF208 PA 66
LNP LUBRILOY* RF208 is a compound based on Nylon 66 resin containing 40% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant.
Flexural Strength 211 MPa
30600 psi
ISO 178
SABIC Innovative Plastics LNP LUBRILOY RF208 PA 66 (Asia Pacific)
LNP LUBRILOY* RF208 is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Flexural Strength 211 MPa
30600 psi
ASTM D790
Solvay Specialty Polymers AvaSpire® AV-742 SL30 Polyaryletherketone (PAEK)
AV-742 SL30 is a wear resistant grade of AvaSpire® polyaryletherketone (PAEK) designed to provide low wear rates in both non-lubricated and lubricated environments. In addition to outstanding wea..
Flexural Strength 211 MPa
30600 psi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP Stat-kon DEF13 PC
LNP* Stat-kon* DEF13 is a compound based on Polycarbonate resin containing Glass Fiber, Glass Fiber, Carbon Fiber. Added features of this material include: Electrically Conductive.This data was sup..
Flexural Strength 211 MPa
30600 psi
ASTM D790
SABIC Innovative Plastics LNP STAT-KON DX10315C PC (Asia Pacific)
LNP* Stat-Kon* DX10315C is carbon fiber filled polycarbonate composite with good stiffness, good flow ability, ESD safety, and high level of cleanliness for the most demanding application. This comp..
Flexural Strength 211 MPa
30600 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP D452 PC COPOLYMER (Asia Pacific)
LNP* Thermocomp* D452 (or EXTC8202) is a compound based on SABIC unique Polycarbonate copolymer resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, ..
Flexural Strength 211 MPa
30600 psi
ASTM D790
Unitika AXG-1500-300 Dry
Characteristics: Glass-reinforced grades of the AX1500 resin, excellent in heat and chemical resistancesFavorable rigidity and dimensional accuracyInformation provided by Unitika Ltd.
Flexural Strength 211 MPa
30600 psi
2.8mm/min; ASTM D790
Asia International Enterprise (Hong Kong) 60G5F Nylon 66, 25% Filled
Information provided by Asia International Enterprise (Hong Kong) Ltd.
Flexural Strength 211 MPa
30600 psi
ASTM D790
Applied Composites 179 Polyester SMC
Industry Application: TransportationProduct Application: Auto InteriorsInformation provided by Applied Composites Corporation.
Flexural Strength 211 MPa
30600 psi
ASTM D790
A. Schulman ComAlloy Voloy® 682 Nylon 6/6, Glass Fiber, Nylon 6/6 Alloy, Flame Retardant, UL
Data provided by the manufacturer, ComAlloy International Company.45% Glass Reinforced. Halogen- and phosphorous-freeThe ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength 211 MPa

@Temperature 23.0 °C
30600 psi

@Temperature 73.4 °F
ISO 178
Solvay Specialty Polymers Amodel® A-1565 HS Polyphthalamide (PPA)  (Unverified Data**)
Amodel A-1565 HS is a 65% glass and mineral-reinforced polyphthalamide (PPA) designed to be cost-effective in applications requiring high stiffness, good dimensional stability and good retention of ..