Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 324 MPa | 47000 psi | ASTM D790 |
LNP Thermocomp® LC-1006 Polyetheretherketone, Carbon Fiber Reinforcement
(discontinued **) Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names.. |
|||
Flexural Strength | 324 MPa | 47000 psi | ASTM D790 |
Greene Tweed Orthetek® RP Polyketone, Random Carbon Fiber Greene Tweed offers precision-molded thermoplastic components made form out high-performance Orthtek® composite materials for a variety of demanding medical device applications. Orthtek RP is id.. |
|||
Flexural Strength | 324 MPa | 47000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP ECL36XXQ PEI LNP* Lubricomp* ECL36XXQ is a compound based on Polyetherimide containing 30% Carbon Fiber, 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 324 MPa | 47000 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP UCL36S PPA LNP* LUBRICOMP* UCL36S is a compound based on Polyphthalamide resin containing 15% PTFE, 30% Carbon Fiber. Added features of this material include: Wear Resistant, Heat Stabilized, Electrically Con.. |
|||
Flexural Strength | 324 MPa | 47000 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP UCL36S PPA (Asia Pacific) LNP* Lubricomp* UCL36S is a compound based on Polyphthalamide resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Heat Stabilized, Electrically Cond.. |
|||
Flexural Strength | 324 MPa | 47000 psi | ASTM D790 |
Techmer ES HiFill® PA6 CF40 40% Carbon Fiber Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber Reinforcement, 40% Filler by WeightAppearance: Black and Natural ColorInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 324 MPa | 47000 psi | ASTM D790 |
Techmer ES HiFill® PA6 GF50 50% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightProcessing Method: Injection MoldingInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 324 MPa | 47000 psi | ASTM D790 |
Techmer ES HiFill® PA6 GF50 X 50% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAppearance: BlackProcessing Method: Injection MoldingInformation provided by TP Composit.. |
|||
Flexural Strength | 324 MPa | 47000 psi | ASTM D790 |
Techmer ES HiFill® PA6 GF50 X BK 50% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAppearance: BlackProcessing Method: Injection MoldingInformation provided by TP Composit.. |
|||
Flexural Strength | 324 MPa | 47000 psi | ASTM D790 |
Techmer ES HiFill® PA6 GF50 X LE 50% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAdditive: Mold ReleaseProcessing Method: Injection MoldingInformation provided by TP Com.. |
|||
Flexural Strength | 324 MPa | 47000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF009H PA 66 LNP* THERMOCOMP* RF009H is a compound based on Nylon 66 resin containing 45% Glass Fiber. Added feature of this material is: Healthcare. |
|||
Flexural Strength | 324 MPa | 47000 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF009H PA 66 (Asia Pacific) LNP* Thermocomp* RF009H is a compound based on Nylon 66 resin containing Glass Fiber. |
|||
Flexural Strength | 324 MPa | 47000 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP UF00ASW PPA LNP* Thermocomp* UF00ASW is a compound based on Polyphthalamide (PPA) containing glass fiber. Characteristics of this grade of Heat Stabilized and Hot Water Moldable. |
|||
Flexural Strength | 324 MPa | 47000 psi | ISO 178 |
SABIC Innovative Plastics LNP STAT-KON RE0069S PA 66 LNP* STAT-KON* RE0069S is a compound based on Nylon 66 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Heat Stabilized. |
|||
Flexural Strength | 324 MPa | 47000 psi | ASTM D790 |
Chase Plastics CP Pryme® NN143L (Dry) Nylon 66, 43% Glass Fiber Reinforced, Lubricated Features: Good chemical resistanceGrease resistantLubricatedOil resistantHigh rigiditySolvent resistantHigh tensile strengthForm: PelletsApplications: Automotive under the hoodInformation provided b.. |
|||
Flexural Strength | 324 MPa | 47000 psi | ASTM D790 |
E-Polymers TEKAMID® TA250G60 60% Glass Fiber Reinforced, High Modulus PA66 Resin Polyamide (Nylon) Resin. TEKAMID is widely being used in manufacturing of automotive and industrial parts with its outstanding mechanical, thermal and chemical properties.T-series: Impact modified,.. |
|||
Flexural Strength | 324 MPa | 47000 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Verton PV00A PA 6 LNP VERTON* PV00A is a compound based on Nylon 6 resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Strength | 324 MPa | 47000 psi | ASTM D790 |
PolyOne Edgetek® AM 33 GF/000 L HS Black Polyphthalamide (PPA), Glass Filled
(discontinued **) Description/Features:Heat StabilizedBlackEnhanced LubricationGlass Fiber ReinforcedInformation provided by PolyOne Corporation. |
|||
Flexural Strength | 324 MPa | 47000 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Verton PV00A PA 6 (Asia Pacific) LNP* Verton* PV00A is a compound based on Nylon 6 resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |