Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 245 MPa | 35500 psi | |
Plastcom SLOVAMID 6/66 GF 30 FRG 5 TS PA6/66, 30% glass fibre, flame retardant FeaturesPA 6 + PA 66 alloy for injection moulding, chemically reinforced with 30 % glass fibre, with halogen and phosphorus free flame retardant. Main features: flammability in accordance with UL 94.. |
|||
Flexural Strength | 245 MPa | 35500 psi | |
Plastcom SLOVAMID 66 C 15 MI PA66, 15% mineral filling Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.0.. |
|||
Flexural Strength | 245 MPa @Temperature 23.0 °C |
35500 psi @Temperature 73.4 °F |
DAM; ASTM D790 |
DuPont Performance Polymers Zytel® 77G33L BK031 Nylon 612
(Unverified Data**) Zytel® 77G33L BK031 is a 33% glass fiber reinforced, black polyamide 612 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
Flexural Strength | 245 MPa | 35500 psi | 2 mm/min; ISO 178-A |
Lanxess Durethan® BKV 130 CS DUS008 600091 Nylon 6, 30% Glass Fiber PA 6, 30% glass fiber, injection molding, impact modifiedInformation provided by LANXESS. |
|||
Flexural Strength | 245 MPa | 35500 psi | |
Lehmann & Voss LUVOCOM® 1-0936 Polyamide 66, with glass fiber and PTFE, 8-mm-granulate Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.High dimensionally stable prec.. |
|||
Flexural Strength | 245 MPa | 35500 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP OCP36F PPS - Linear LNP LUBRICOMP* OCP36F is a compound based on PPS - Linear resin containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this grade include: Bearing Grade, Electrically Conductive, Wear R.. |
|||
Flexural Strength | 245 MPa | 35500 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP OCP36F PPS - Linear (Asia Pacific) LNP LUBRICOMP* OCP36F is a compound based on PPS - Linear resin containing Bearing Grade, Carbon Fiber, Lubricants. Added features of this material include: Electrically Conductive. |
|||
Flexural Strength | 245 MPa | 35500 psi | ISO 178 |
Solvay Specialty Polymers Ryton® R-4-232NA Polyphenylene Sulfide (PPS), 40% Glass Fiber Ryton® R-4-232NA 40% glass fiber reinforced polyphenylene sulfide compound complies with United States Food and Drug Administration (FDA) and European Union (EU 10/2011 and 1183/2012) regulations.. |
|||
Flexural Strength | 245 MPa | 35500 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP LF006 PEEK LNP THERMOCOMP* LF006 is a compound based on Polyetheretherketone resin containing 30% Glass Fiber. |
|||
Flexural Strength | 245 MPa | 35500 psi | ASTM D790 |
A. Schulman Aqualoy® 645 Glass Fiber Reinforced Hydrolysis Resistant Nylon 66 Information provided by A. Schulman. |
|||
Flexural Strength | 245 MPa | 35500 psi | ASTM D790 |
Chase Plastics CP Pryme® N233GL (DAM) Nylon 6, 33% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||
Flexural Strength | 245 MPa | 35500 psi | ASTM D790 |
A. Schulman Aqualoy® 645 Glass Fiber Reinforced Hydrolysis Resistant Nylon 66 Information provided by A. Schulman. |
|||
Flexural Strength | 245 MPa | 35500 psi | ASTM D790 |
A. Schulman Aqualoy® 645 Glass Fiber Reinforced Hydrolysis Resistant Nylon 66 Information provided by A. Schulman. |
|||
Flexural Strength | 245 MPa | 35500 psi | ISO 178 |
Polyplastics Duranex® 3400 Polybutylene Terephthalate (PBT), Standard, 40% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Flexural Strength | 245 MPa | 35500 psi | dry; ISO 178 |
DSM Novamid® 1010G30 NA PA6-GF30 30% Glass Reinforced, Injection Molding, Easy Molding Grade, High Flow |
|||
Flexural Strength | 245 MPa | 35500 psi | ASTM D790, ISO 178 |
EPICHEM Epinyl PA 6 GF 30 H Polyamide 6, 30% Glass, Heat Stabilized Characteristics: medium viscosity, 30% glass fibre, heat stabilized |
|||
Flexural Strength | 245 MPa | 35500 psi | ASTM D790, ISO 178 |
EPICHEM Epinyl PA 6 GF 30 Polyamide 6, 30% Glass Characteristics: medium viscosity, 30% glass fibre, excellent mechanical properties |
|||
Flexural Strength | 245 MPa | 35500 psi | ISO 178 |
DuPont Performance Polymers Sorona® 3030GV NC010 Polytrimethylene Terephthalate (PTT) 30% Glass Reinforced Renewably Sourced Polytrimethylene Terephthalate Sorona 3030GV NC010 is a 30% glass reinforced PTT resin containing 25% renewably sourced ingredients by weight (37% based on pol.. |
|||
Flexural Strength | 245 MPa | 35500 psi | 2 [mm/min]; ISO 178 |
Akro-Plastic Akromid® B3 GF 25 (2471) PA 6 Dry, 25% Glass Filled AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur.. |
|||
Flexural Strength | 245 MPa | 35500 psi | 2.8mm/min; ASTM D790 |
Asia International Enterprise (Hong Kong) 60G5 Nylon 66, 25% Filled Information provided by Asia International Enterprise (Hong Kong) Ltd. |
|||
Flexural Strength | 245 MPa | 35500 psi | ISO 178 |
DuPont Performance Polymers Sorona® 3030G NC010 Polytrimethylene Terephthalate (PTT)
(Unverified Data**)& 30% Glass Reinforced Polytrimethylene Terephthalate Sorona 3030G NC010 is a 30% glass reinforced PTT resin containing 25% renewably sourced ingredients by weight (37% based on polymer only) with goo.. |