Polymer Property : Flexural Strength = 41300 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	285 MPa	41300 psi
Plastcom SLOVAMID 6 NG GF 45 PA6, 45% glass fibre FeaturesPA 6 for injection moulding, chemically strengthened with 45% of glass fibre, for mouldings with high strength and toughness used in the automotive, electrical, engineering and consumer-good..
Flexural Strength	285 MPa	41300 psi	ISO 178
Solvay Specialty Polymers Ixef® 1002 Polyarylamide (PARA) (Unverified Data**) Ixef 1002 is a 30% glass-fiber reinforced, general purpose polyarylamide compound which exhibits high strength and rigidity, outstanding surface finish, and excellent creep resistance. - Black: Ixef..
Flexural Strength	285 MPa	41300 psi	3.5%; ISO 178
GEHR Plastics PPS-40GF Polyphenylene Sulfide, 40% Glass Fiber The linear polyphenylensulfide belongs to the semi-crystalline materials and offers a very high mechanical capacity, thermal and chemical resistance distinguished at the same time, high dimensional ..
Flexural Strength	285 MPa	41300 psi	ISO 178
Kuraray Genestarâ„¢ G1350A-M42 Nylon, 35% Glass Filled 35% Glass reinforced injection grade. This grade was developed specifically for improved performance in a 50/50 ethylene glycol and water environment.Main Features:Hydrolysis resistanceHeat resista..
Flexural Strength	285 MPa	41300 psi
Lehmann & Voss LUVOCOMÂ® 1105-0699-1 PEEK, with carbon fiber, PTFE, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High-strength and high-stiff parts; low coefficient of expansion.Improved friction and wea..
Flexural Strength	285 MPa	41300 psi	ISO 178
Solvay TECHNYLÂ® CR 218 V33 Black 21 N Nylon 6, 30% glass fiber, DRY Description: Polyamide PA6 reinforced with 33% of glass fiber, heat stabilized, containing recycled material.Available in: North AmericaProduct Applications: This grade is suitable for none critical..
Flexural Strength	285 MPa	41300 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP UFL36S PPA LNP LUBRICOMP* UFL36S is a compound based on Polyphthalamide resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Heat Stabilized, Wear Resistant, Bearing Grade.
Flexural Strength	285 MPa	41300 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP UFL36SXP PPA LNP LUBRICOMP* UFL36SXP is a compound based on Polyphthalamide resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Heat Stabilized, Wear Resistant.
Flexural Strength	285 MPa	41300 psi	ISO 178
Solvay Specialty Polymers IxefÂ® 1002 Polyarylamide (PARA), 30% Glass Fiber IxefÂ® 1002 is a 30% glass-fiber reinforced, general purpose polyarylamide compound which exhibits high strength and rigidity, outstanding surface finish, and excellent creep resistance.Features: ..
Flexural Strength	285 MPa	41300 psi	ISO 178
Solvay Specialty Polymers RytonÂ® R-4-200NA Polyphenylene Sulfide (PPS), 40% Glass Fiber RytonÂ® R-4-200NA and R-4-200BL 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength and low maintenance molding using conventional molding equipmentFeat..
Flexural Strength	285 MPa	41300 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP QF00A PA6.10 LNP* THERMOCOMP* QF00A is a compound based on Nylon 6/10 containing 50% Glass Fiber.
Flexural Strength	285 MPa	41300 psi	ISO 178
SABIC Innovative Plastics LNP Verton OV00A PPS (Asia Pacific) LNP* Verton* OV00A is a compound based on Polyphenylene Sulfide resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Strength	285 MPa	41300 psi	ISO 178
SABIC Innovative Plastics LNP Verton OX07411 PPS (Asia Pacific) LNP* Verton* OX07411 is a compound based on Polyphenylene Sulfide resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Strength	285 MPa	41300 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Verton RV008ESV PA 66 40% long glass fiber filled PA66 Verton Xtreme XCThis data was supplied by SABIC-IP for the Americas region.
Flexural Strength	285 MPa	41300 psi	ISO 178
SABIC Innovative Plastics LNP VERTON RX10409D PA 66 LNP* VERTON* RX10409D is a compound based on Nylon 66 containing proprietary fillers. Added feature of this grade is: Structural.
Flexural Strength	285 MPa	41300 psi	2 [mm/min]; ISO 178
Akro-Plastic Akromid® A3 GF 30 (2397) PA 6.6 Dry, 30% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat..
Flexural Strength	285 MPa	41300 psi	2 [mm/min]; ISO 178
Akro-Plastic Akromid® T6 GF30 (3501) PPA Dry, 30% Glass Filled The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high..
Flexural Strength	285 MPa	41300 psi	ASTM Test
BASF Petra® 140 45% Glass Filled PET Petra 140 is a 45% glass reinforced injection molding polyethylene terephthalate (PET) offering an increased level of strength, stiffness, high temperature performance and dimensional stability. Ex..
Flexural Strength	285 MPa	41300 psi	2 [mm/min]; ISO 178
Akro-Plastic Akromid® B3 GF 35 (2473) PA 6 Dry, 35% Glass Filled AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur..
Flexural Strength	285 MPa	41300 psi	ISO 178-93
Wellman Wellamid® GF33AO99 HR 33% Glass Fiber Reinforced, Hydrolysis Resistant Nylon 66 Description: Glass Fiber Reinforced, Hydrolysis Resistant Nylon 66Information provided by Wellman.
Flexural Strength	285 MPa	41300 psi	ISO 178
SABIC Innovative Plastics LNP Verton OV00A PPS LNP* Verton* OV00A is a compound based on Polyphenylene Sulfide resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Flexural Strength	285 MPa	41300 psi	ISO 178
SABIC Innovative Plastics LNP Verton OX07411 PPS LNP* Verton* OX07411 is a compound based on Polyphenylene Sulfide resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Americas region.