- Polymer Property : Flexural Strength = 50.0 MPa
Polymer Property : Flexural Strength = 50.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 50.0 MPa | 7250 psi | |
| Plastcom SLOVALEN PH 22 T 40 PP, 40% mineral filling FeaturesModified homopolymer PP for injection moulding with the content of 40% microground, floated, chemically modified talc. Special designed for automotive light housings. Delivered in natural mo.. |
|||
| Flexural Strength | <= 50.0 MPa | <= 7250 psi | ISO 178 |
| Polykemi AB POLYfill PPHC K3020 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
| Flexural Strength | 50.0 - 70.0 MPa | 7250 - 10200 psi | Compression; ISO 178 |
| Raschig Group DECAL® 937 Phenolic Mica reinforced phenolic molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (W.. |
|||
| Flexural Strength | 50.0 - 60.0 MPa | 7250 - 8700 psi | ISO 178 |
| Raschig Group EN 5007 Epoxy Molding Compound Mica reinforced molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, outstanding heat resistance, very goo pourablity. This product meets the allowed upper limits fo.. |
|||
| Flexural Strength | <= 50.0 MPa | <= 7250 psi | ISO 178 |
| Polykemi AB POLYfill PPH K8040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | ISO 178 |
| Nilit FRIANYL B63 H Nylon 6 for injection molding Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | ISO 178 |
| Nilit FRIANYL B63 HH Nylon 6 for injection molding Nylon 6 for injection molding, heat and hydrolysis stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | |
| Quadrant EPP Semitron® ESd 225 POM-C, static dissipative, extruded (ISO Data) Semitron ESd 225 is an acetal based static dissipative material ideal for material handling operations. It is also an excellent choice for fixturing used in the manufacturing of hard disk drives or .. |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® FL900P PC (Europe-Africa-Middle East) Foamable LEXAN, various weight reductions at 6.4 mm. Offers load bearing capability at elavated temp., Combines rigidity, impact & toughness.This data was supplied by SABIC-IP for the Europe-Africa-.. |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | |
| Lehmann & Voss LUVOCOM® 1850-7692 PBT, with glass spheres and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | ASTM D790 |
| Kostat BK-STAT 7048BK ABS Compound BK-STAT Compounds are statically dissipative thermoplastics based on IDP (Inherently Dissipative Polymers) technology. This class of materials have distinctive advantages in hot spots and cleanline.. |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | ASTM D790-95 |
| Multibase Multi-ABS 802 Natural Extrusion Grade Data provided by Multibase. |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | ISO 178 |
| Solvay TECHNYL® B 218 Black 21 N PA66/6, Conditioned Description: Unreinforced copolyamide PA 66/6 , heat stabilized , medium viscosity, for injection molding.Available in: EuropeProduct Applications: TECHNYL® B 218 offers all of the primary proper.. |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | DIN 54352 |
| Schwartz Technical Plastics LAMIGAMID® 300 Cast Polyamide 6, Conditioned Application: slippers and center blocks for heavy rolling mills, outrigger floatsInformation provided by Schwartz Technical Plastics GmbH |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP STAT-LOY 63000CT PC+POLYESTER (Asia Pacific) A permanent antistatic PC-Alloy compound that features transparency and superior cleanliness for advanced semiconductor packaging applications |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP STAT-LOY AX06484 ABS LNP* STAT-LOY* AX06484 is a compound based on ABS resin containing Talc. Added feature of this grade is: Antistatic, Extrudeable. |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | Bending Strength |
| Saint-Gobain Spectrosil® 2000 Optical Fused Quartz Spectrosil® 2000 is a deep UV, fluorescence-free grade.Spectrosil® is a synthetic fused silica manufactured using a patented, environmentally friendly process that results in a virtually chlor.. |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | Bending Strength |
| Saint-Gobain Puropsil® B Infrared Grade Low [OH] Optical Fused Quartz Puropsil® B optical infrared fused quartz is manufactured from naturally occurring quartz crystal using a plasma process to ensure a low OH. It has excellent IR transmission with a useful IR tra.. |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | ASTM D790 |
| Teknor Apex Sinpolene TPP1010 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Talc Filler, 10% Filler by Weight Uses: Appliance Components; Housings Forms: Pellets Processing Method: Injection Mol.. |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | ASTM D790 |
| A. Schulman POLYFORT™ FPP 1237 CaCO3 filled homopolymer polypropylene DescriptionPolyfort® FPP 1237 is a 20% CAC03 filled homopolymer polypropylene product. Information provided by A. Schulman. |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | ASTM D790 |
| Polyram RamOfin PPH313V4 Polypropylene, 20% Mineral Filled 20% mineral filled, impact modified polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | GB/9341 |
| Zhejiang Juner JEPPA003 High Glossy PP Applications: High Glossy PartsInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | ASTM D790 |
| Aclo Accutech Polypropylene Homopolymer HP0336M30CL Mica Reinforced Coupled |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | ASTM D790 |
| Aclo Accutech Polypropylene HP0335T40V Homopolymer Talc Reinforced Approved to ESF-M4D355B White B12391 |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | ISO 178 |
| Ascend Performance Materials Vydyne® 21SPC Nylon 66, Conditioned Vydyne® 21SPC is a general-purpose PA66 resin available in natural color. It is designed principally for injection-molding fabrication. This resin offers a well balanced combination of engineering .. |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | ISO Data |
| BASF Ultramid® 8350 HS PA6 (Dry) Ultramid 8350 HS is a heat stabilized, impact modified type 6 graft copolymer developed for extrusion, tubing, and jacketing applications requiring a high level of toughness combined with a moderate.. |
|||
| Flexural Strength | 50.0 MPa | 7250 psi | ASTM D790 |
| Aclo Accutech Polypropylene Homopolymer HP0339M40CL Mica Reinforced Coupled |
|||
| Flexural Strength | 50.0 - 100 MPa | 7250 - 14500 psi | |
| Alliance BIF-16 Bonded (Composite) Magnetic Material |
|||
| Flexural Strength | <= 50.0 MPa | <= 7250 psi | ISO 178 |
| Polykemi AB POLYfill PPHC K5020 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||