Polymer Property : Flexural Strength = 7250 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 50.0 MPa
7250 psi
Plastcom SLOVALEN PC 71 T 10 PP, 10% mineral filling
FeaturesModified copolymer PP for injection moulding with the content of 10% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decr eased shri..
Flexural Strength 50.0 - 100 MPa
7250 - 14500 psi
1.5mm/min; ISO 178:2001
Nylacast Aquanyl Nylon 612 Copolymer
Aquanyl is a copolymer of Nylon 6 and Nylon 12 produced via the anionic polymerization process using the monomer's Caprolactam and Laurinlactam. It has reduced water absorption, improved stability a..
Flexural Strength <= 50.0 MPa
<= 7250 psi
ISO 178
Polykemi AB POLYfill PPC TS20020 UV Polypropylene Copolymer, Mineral Reinforced, UV-Stabilized
Information provided by Polykemi AB
Flexural Strength 50.0 MPa
7250 psi
ISO 178
Nilit FRIANYL B63 KG20 Nylon 6 for injection molding, 20% chalk filled
Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength 50.0 - 60.0 MPa
7250 - 8700 psi
ISO 178
Raschig Group EN 5004 Epoxy Molding Compound
Mica reinforced molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, outstanding heat resistance, very goo pourablity. This product meets the allowed upper limits fo..
Flexural Strength 50.0 MPa
7250 psi
Quadrant EPP Semitron® ESd 225 POM-C, static dissipative, extruded (ISO Data)
Semitron ESd 225 is an acetal based static dissipative material ideal for material handling operations. It is also an excellent choice for fixturing used in the manufacturing of hard disk drives or ..
Flexural Strength 50.0 MPa
7250 psi
2 mm/min, @ 3.5% strain; ISO 178
Ineos ABS Triax® 3158 ABS + Polyamide Blend (DAM), PA66/ABS Pellets (filled)
Triax® 3158 is a PA+ABS-Blend and on-line paintable (195°C). It has very high heat resistance, reduced moisture, improved impact strength, and a low coefficient of linear thermal expansion. It..
Flexural Strength 50.0 MPa
7250 psi
ASTM D790
Kostat BK-STAT 7048BK ABS Compound
BK-STAT Compounds are statically dissipative thermoplastics based on IDP (Inherently Dissipative Polymers) technology. This class of materials have distinctive advantages in hot spots and cleanline..
Flexural Strength 50.0 MPa
7250 psi
ASTM D790-95
Multibase Multi-ABS 802 Natural Extrusion Grade
Data provided by Multibase.
Flexural Strength 50.0 MPa
7250 psi
ISO 178
Solvay TECHNYL® B 218 Black 21 N PA66/6, Conditioned
Description: Unreinforced copolyamide PA 66/6 , heat stabilized , medium viscosity, for injection molding.Available in: EuropeProduct Applications: TECHNYL® B 218 offers all of the primary proper..
Flexural Strength 50.0 MPa
7250 psi
DIN 54352
Schwartz Technical Plastics LAMIGAMID® 300 Cast Polyamide 6, Conditioned
Application: slippers and center blocks for heavy rolling mills, outrigger floatsInformation provided by Schwartz Technical Plastics GmbH
Flexural Strength 50.0 MPa
7250 psi
Bending Strength
Saint-Gobain Vitreosil® Clear Fused Quartz Tubing
Electrically fused quartz is recognized for its combination of purity, chemical inertness, physical stability, thermal shock resistance, high electrical resistivity, and high operating temperatures...
Flexural Strength 50.0 MPa
7250 psi
DIN EN ISO 178
Wolf Kunststoff ZEDEX® ZX-530CD3 031 Polymer Alloy, Fiber Reinforced and PTFE Modified
Main Characteristics: Dimensionally stable and rigid; Stress resistant; Extremely low wear to 100 ° CApplications: Chemical Engineering; Laboratory Technology; Automitve Technology; Machine ToolsIn..
Flexural Strength 50.0 MPa
7250 psi
GB/9341
Zhejiang Juner JEPP263 Weatherability PP Series
Applications: Air Conditioning SystemInformation provided by Zhejiang Juner New Materials Co, Ltd.
Flexural Strength 50.0 MPa
7250 psi
ASTM D790
A. Schulman POLYFLAM™ RABS 930-01
Information provided by A. Schulman.
Flexural Strength 50.0 MPa
7250 psi
ASTM D790
A. Schulman POLYFLAM™ RABS 930-01
Information provided by A. Schulman.
Flexural Strength 50.0 MPa
7250 psi
ASTM D790
A. Schulman POLYFORT™ FPP 1237 CaCO3 filled homopolymer polypropylene
DescriptionPolyfort® FPP 1237 is a 20% CAC03 filled homopolymer polypropylene product. Information provided by A. Schulman.
Flexural Strength 50.0 MPa
7250 psi
Chengdu Polyster PPHA p-Hydroxybenzoic Acid Polymer
PPHA is difficult to manufacture and brittle as well as low mechanical strength, its compounds have a higher mechanical strength and can be injection moulded. It can work without oil and its perform..
Flexural Strength 50.0 MPa
7250 psi
cond; ISO 178
DSM Novamid® 3010SR NAT PA66
Easy Molding Grade
Flexural Strength 50.0 MPa
7250 psi
ISO 178
DuPont Performance Polymers Crastin® ST820 BK503 Polybutylene Terephthalate (PBT)  (Unverified Data**)
Unreinforced Polybutylene Terephthalate with Excellent Impact Resistance Crastin ST820 BK503 is an unreinforced Super Tough black polybutylene terephthalate resin for injection molding.Information p..
Flexural Strength >= 50.0 MPa
>= 7250 psi
cold bending
China-Yixing Longly Refractories ASM-120 Cordierite-Mullite
Featured mullite, cordierite as the main raw material, the use of advanced production technology, professionally manufacturing the kiln furniture of ceramic and powder metallurgy with load bearing b..
Flexural Strength 50.0 MPa
7250 psi
ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0336M30CL Mica Reinforced Coupled
Flexural Strength 50.0 MPa
7250 psi
ISO 178
Ascend Performance Materials Vydyne® 21SPC1 Nylon 66, Conditioned
Vydyne® 21SPC1 is a general-purpose, improved-flow, lubricated PA66 resin available in natural color. 21SPC1 offers a balanced combination of properties characterized by high strength, rigidity, go..
Flexural Strength 50.0 MPa
7250 psi
ISO Data
BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Conditioned)
Ultramid 8260 HS BK-102 is a heat stabilized, pigmented black, 40% mineral reinforced PA6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined wi..
Flexural Strength 50.0 MPa

@Temperature 120 °C
7250 psi

@Temperature 248 °F
ASTM Test
BASF Ultramid® 8272G HS BK-102 12% Glass Filled PA6 (Dry)
Ultramid 8272G HS BK-102 is a 12% glass fiber reinforced, black pigmented, thermally modified, nylon 6 blow molding compound offering an excellent balance of engineering properties combined with the..
Flexural Strength 50.0 MPa
7250 psi
ISO Data
BASF Ultramid® 8350 HS PA6 (Dry)
Ultramid 8350 HS is a heat stabilized, impact modified type 6 graft copolymer developed for extrusion, tubing, and jacketing applications requiring a high level of toughness combined with a moderate..
Flexural Strength 50.0 MPa
7250 psi
ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0339M40CL Mica Reinforced Coupled
Flexural Strength <= 50.0 MPa
<= 7250 psi
ISO 178
Polykemi AB POLYfill PPH TS15030 Polypropylene Homopolymer, Mineral Reinforced
Information provided by Polykemi AB
Flexural Strength 50.0 MPa
7250 psi
ISO 178
BASF Ultramid® B3M6 Grey 22319 Q94 30% Mineral Filled PA6 (Conditioned)
Description: 30% Mineral-filled injection molding grade for high impact industrial items having very high dimensional stability, such as automobile wheel covers.Information provided by BASF