Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 99.0 MPa | 14400 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Faradex NS0029 PC+ABS (Europe-Africa-Middle East) LNP* Faradex* NS0029 is a compound based on PC+ABS Blend resin containing Flame Retardant, Stainless Steel Fiber. Added features of this material include: EMI/RFI Shielding, Flame Retardant.This da.. |
|||
Flexural Strength | 99.0 MPa @Temperature 22.0 °C |
14400 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
Menzolit Menzolit® BMC 0180 Unsaturated Polyester UP BMC 0180 is a general purpose BMC for electrical applications. Product according to type 803 DIN 16911. The glass content is on a level that combines good mould ability with good strength and stiffn.. |
|||
Flexural Strength | 99.0 MPa @Temperature 22.0 °C |
14400 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
Menzolit Menzolit® BMC 0190 Unsaturated Polyester UP BMC 0190 is a general purpose BMC for applications in the field of electrical industry. Typical applications are housings, covers, wire distribution boxes and metering cabinets. The flammability me.. |
|||
Flexural Strength | 99.0 MPa | 14400 psi | ASTM D790 |
SABIC Innovative Plastics NORYL PX9406P PPE+HIPS (Asia Pacific) Nonbrominated, nonchlorinated, flame retarded. Improved productivity and reliability. 125dc HDT. UL94 V-0 rated. Electrical applications. |
|||
Flexural Strength | 99.0 MPa | 14400 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP ZX05506 PPE+PS LNP LUBRICOMP* ZX05506 is a compound based on PPE+PS Blend resin containing Graphite Powder, PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 99.0 MPa | 14400 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP ZX05506 PPE+PS (Asia Pacific) LNP LUBRICOMP* ZX05506 is a compound based on PPE+PS Blend resin containing Graphite Powder, PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 99.0 MPa | 14400 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRILOY DX08333 PC (Asia Pacific) LNP Lubriloy* DX08333 is an internally lubricated compound based on Lexan* Polycarbonate resin. Added features of this material include: ESD Safe, PTFE-free Wear & Friction solution and balanced mec.. |
|||
Flexural Strength | 99.0 MPa | 14400 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Stat-kon DX92440 PC LNP STAT-KON* DX92440 is a compound based on Polycarbonate resin containing Flame Retardant, Stainless Steel. Added features of this material include: Electrically Conductive.This data was supplied.. |
|||
Flexural Strength | 99.0 MPa | 14400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON 9X04323 PPE+PA66 (Asia Pacific) LNP* Stat-kon* 9X04323 is a compound based on Noryl GTX resin,Added features of this material include: Electrically Conductive. |
|||
Flexural Strength | 99.0 MPa | 14400 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP WH0245A PBT LNP THERMOCOMP* WH0245A is a compound based on Polybutylene Terephalate resin. Added features of this material include: High Specific Gravity. |
|||
Flexural Strength | 99.0 MPa | 14400 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP WH0245A PBT (Asia Pacific) LNP THERMOCOMP* WH0245A is a compound based on Polybutylene Terephalate resin. Added features of this material include: High Specific Gravity. |
|||
Flexural Strength | 99.0 MPa | 14400 psi | ASTM D790 |
Plenco 08133 Polyester BMC, Compression Molded PLENCO 08133 is a renumber of PlasGlas 10313. PLENCO 08133 is a general purpose polyester bulk molding compound that is characterized by adding utility to a number of applications. Because of its co.. |
|||
Flexural Strength | 99.0 MPa | 14400 psi | ISO 178 |
Unitika A1030BRL PA6, Dry Information provided by Unitika Ltd. |
|||
Flexural Strength | 99.0 MPa | 14400 psi | ISO 178 |
Unitika A1030SR PA6, Dry Information provided by Unitika Ltd. |
|||
Flexural Strength | 99.0 MPa | 14400 psi | ASTM D790 |
Unitika L-8005 Chemical resistance, and excellent lubricant propertyInformation provided by Unitika Ltd. |
|||
Flexural Strength | 99.0 MPa | 14400 psi | 2 mm/min; ISO 178 |
Covestro Makrolon® 1952 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardancy• Me.. |
|||
Flexural Strength | 99.0 MPa | 14400 psi | ASTM D790 |
A. Schulman ComAlloy Voloy® 630 Nylon 6/6, Flow Enhanced, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Strength | 99.0 MPa | 14400 psi | 2.8mm/min; ASTM D790 |
Asia International Enterprise (Hong Kong) 3010FW Polybutylene terephthalate Information provided by Asia International Enterprise (Hong Kong) Ltd. |
|||
Flexural Strength | 99.0 MPa | 14400 psi | ASTM D790 |
A. Schulman ComAlloy Hiloy® 636 Nylon 6/6, Glass/Mineral Reinforced, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company.40% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Flexural Strength | 99.0 MPa @Temperature 23.0 °C |
14400 psi @Temperature 73.4 °F |
|
Ceradyne Ceralloy® 398J Yttrium Oxide Ceralloy® 398J Hot Pressed Yttrium Oxide is a high purity hot-pressed ceramic exhibiting excellent corrosion and erosion resistance. Products produced from Hot Pressed Yttrium Oxide are for semicon.. |