- Polymer Property : Compressive Yield Strength = 1000 psi
Polymer Property : Compressive Yield Strength = 1000 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Max load under tribological use |
| Saint-Gobain Rulon® E Grade Bearing/Seal PTFE
(discontinued **) Rulon® is the Saint-Gobain trade name for their family of proprietary PTFE compounds. This family of materials offers the combination of high compressive strength, low coefficient of friction, and .. |
|||
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Max load under tribological use |
| Saint-Gobain Rulon® 1045 Bearing/Seal PTFE Rulon® 1045 is a dull gold material that has an excellent ability to elongate in a flip seal application. Coupled with excellent frictional characteristics, it offers the added benefit of energy .. |
|||
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Max load under tribological use |
| Saint-Gobain Rulon® 123 Grade Bearing/Seal PTFE Description: Rulon® is the Saint-Gobain trade name for their family of proprietary PTFE compounds. This family of materials offers the combination of high compressive strength, low coefficient of.. |
|||
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Max load under tribological use |
| Saint-Gobain Rulon® 1337 Bearing/Seal PTFE Rulon® 1337 is a tan material made entirely from FDA compliant components. It has excellent physical properties and is chemically compatible with most chemicals, except concentrated sulfuric acid.. |
|||
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Max load under tribological use |
| Saint-Gobain Rulon® 1439 Bearing/Seal PTFE Rulon® 1439 is a white FDA compliant material that is suitable for immersed service with better wear characteristics than most other PTFE compounds. Its color makes it aesthetically pleasing for .. |
|||
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Max load under tribological use |
| Saint-Gobain Rulon® 641 Grade Bearing/Seal PTFE Description: Rulon® is the Saint-Gobain trade name for their family of proprietary PTFE compounds. This family of materials offers the combination of high compressive strength, low coefficient of.. |
|||
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Max load under tribological use |
| Saint-Gobain Rulon® 945 Grade Bearing/Seal PTFE Description: Rulon® is the Saint-Gobain trade name for their family of proprietary PTFE compounds. This family of materials offers the combination of high compressive strength, low coefficient of.. |
|||
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Max load under tribological use |
| Saint-Gobain Rulon® 957 Grade Bearing/Seal PTFE Description: Rulon® is the Saint-Gobain trade name for their family of proprietary PTFE compounds. This family of materials offers the combination of high compressive strength, low coefficient of.. |
|||
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Max load under tribological use |
| Saint-Gobain Rulon® F Grade Bearing/Seal PTFE F Grade Bearing/Seal PTFE is used for applications requiring a long wearing material, especially in dry applications and those requiring high abrasion resistance. Standard tape liner material for Ru.. |
|||
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Max load under tribological use |
| Saint-Gobain Rulon® LR Grade Bearing/Seal PTFE Description: Rulon® is the Saint-Gobain trade name for their family of proprietary PTFE compounds. This family of materials offers the combination of high compressive strength, low coefficient of.. |
|||
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Max load under tribological use |
| Saint-Gobain Rulon® 142 Grade Bearing/Seal PTFE Description: Rulon® is the Saint-Gobain trade name for their family of proprietary PTFE compounds. This family of materials offers the combination of high compressive strength, low coefficient of.. |
|||
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Max load under tribological use |
| Saint-Gobain Rulon® AR Bearing/Seal PTFE Rulon® AR is somewhat more flexible than Rulon® LR, hence suitable for seals and bonded coating of slide surfaces. It has many decades of use in automotive shaft seals and fuel metering pump c.. |
|||
| Compressive Yield Strength | 6.90 MPa | 1000 psi | at 20% Compression, Parallel to thickness |
| Zircar Ceramics HASH-60 Alumina-Silica Insulation ZIRCAR Ceramics Alumina-Silica Insulation Type HASH-60 is a hardened insulation board used primarily for its high temperature dielectric strength in high power electrical switching equipment. Inform.. |
|||
| Compressive Yield Strength | 6.90 MPa | 1000 psi | at 10% deflection, parallel to thickness |
| Zircar Refractory Composites RS-A1 Refractory Sheet This product is made from Type RS-A Moldable. Type RS-A was developed as an asbestos board replacement for induction coil liners and molten metal transport, and contains no asbestos. Refractory Shee.. |
|||
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Stabilized, typ |
| Hexcel® HexWeb® CR III 1/16-5052-.0007 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR.. |
|||
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Stabilized, typ |
| Hexcel® HexWeb® CR III 3/8-5052-.005 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR.. |
|||
| Compressive Yield Strength | >= 6.89 MPa | >= 1000 psi | Stabilized, min |
| Hexcel® HexWeb® CR III 5/32-5056-.002 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR.. |
|||
| Compressive Yield Strength | >= 6.89 MPa | >= 1000 psi | Bare, min |
| Hexcel® HexWeb® CR-PAA™ 1/8-5052-0.002 Phosphoric Acid Anodized Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the fa.. |
|||
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Stabilized, typ |
| Hexcel® HexWeb® CR-PAA™ 3/8-5052-0.005 Phosphoric Acid Anodized Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the fa.. |
|||
| Compressive Yield Strength | >= 6.89 MPa | >= 1000 psi | Stabilized, min |
| Hexcel® HexWeb® HRH-327 - 3/16 - 8.0 Fiberglass Reinforced Polyimide Honeycomb Designation: Material-Cell Size (inches)-DensityHexWeb® HRH-327 is a glass-fabric, bias weave reinforced plastic honeycomb that incorporates a polyimide resin system for the node adhesive as well a.. |
|||
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Stabilized, typ, preliminary value obtained at .500 inch thickness |
| Hexcel® HexWeb® HRH-327 - 3/8 - 7.0 Fiberglass Reinforced Polyimide Honeycomb Designation: Material-Cell Size (inches)-DensityHexWeb® HRH-327 is a glass-fabric, bias weave reinforced plastic honeycomb that incorporates a polyimide resin system for the node adhesive as well a.. |
|||
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Stabilized |
| Hexcel® HexWeb® HRH-36 - 1/8 - 6.0 Para-Aramid/Phenolic Core Designation: Material-Cell Size (inches)-DensityHexWeb® HRH-36 is manufactured using KEVLAR® paper. The standard resin system is phenolic.Features: Mechanical properties equivalent to KOREX®; Low.. |
|||
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Stabilized, typ |
| Hexcel® HexWeb® HRP - 3/8 - 6.0 Fiberglass/Phenolic Honeycomb Designation: Material-Cell Size (inches)-DensityHexWeb HRP is a glass fabric reinforced honeycomb in which a heat-resistant phenolic resin is used both for initial and final impregnations. This prod.. |
|||
| Compressive Yield Strength | >= 6.89 MPa | >= 1000 psi | Bare, min |
| Hexcel® HexWeb® HRP - 3/8 - 8.0 Fiberglass/Phenolic Honeycomb Designation: Material-Cell Size (inches)-DensityHexWeb HRP is a glass fabric reinforced honeycomb in which a heat-resistant phenolic resin is used both for initial and final impregnations. This prod.. |
|||
| Compressive Yield Strength | >= 6.89 MPa | >= 1000 psi | Bare, min |
| Hexcel® HexWeb® CR III 3/16-5052-.003 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR.. |
|||
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Stabilized, typ |
| Hexcel® HexWeb® CR III 3/16-5056-.002 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR.. |
|||
| Compressive Yield Strength | >= 6.89 MPa | >= 1000 psi | Bare, min |
| Hexcel® HexWeb® CR-PAA™ 3/16-5052-0.003 Phosphoric Acid Anodized Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the fa.. |
|||
| Compressive Yield Strength | 6.89 MPa | 1000 psi | Stabilized, typ |
| Hexcel® HexWeb® CR-PAA™ 3/16-5056-0.002 Phosphoric Acid Anodized Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the fa.. |
|||
| Compressive Yield Strength | >= 6.89 MPa | >= 1000 psi | Bare, min |
| Hexcel® HexWeb® CR III 1/8-5052-.002 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR.. |
|||
| Compressive Yield Strength | 6.89 - 350 MPa | 1000 - 50800 psi | Average value: 161 MPa Grade Count:21 |
| Overview of materials for Epoxy Molding Compound This property data is a summary of similar materials in the MatWeb database for the category "Epoxy Molding Compound". Each property range of values reported is minimum and maximum values of appropr.. |
|||