Polymer Property : Compressive Yield Strength = 20300 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Compressive Yield Strength 140 - 186 MPa
20300 - 27000 psi
Average value: 178 MPa Grade Count:10
Overview of materials for Diallyl Phthalate (DAP) Molding Compound, Long Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Diallyl Phthalate (DAP) Molding Compound, Long Glass Fiber Filled". Each property range of values report..
Compressive Yield Strength 140 MPa
20300 psi
ISO 14126
Menzolit Menzolit® SMC 1400 Unsaturated Polyester UP
SMC 1400 is a special SMC being used in the environment of a combustion engine. The glass level has been selected to combine good mouldability with good stiffness and strength properties. The produc..
Compressive Yield Strength 140 MPa
20300 psi
Haveg 61NA Furfuryl Alcohol-Formaldehyde Resin
A proprietary thermoset plastic consisting of a furfuryl alcohol-formaldehyde resin and non-asbestos silicate fillers.
Compressive Yield Strength 140 MPa

@Temperature 100 °C
20300 psi

@Temperature 212 °F
90º, Wet; DIN65380
Hexcel® HexPly® M12 135°C Curing Epoxy Matrix, TVR380/26% Fiber
Information provided by HexCel
Compressive Yield Strength 140 - 222 MPa
20300 - 32200 psi
Average value: 166 MPa Grade Count:11
Overview of materials for Nylon 6, 30% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E..
Compressive Yield Strength 140 MPa
20300 psi
Compression After Impact @ 6.6 J/mm, Results normalized to 60% fibre volume for Carbon, 50% fibre volume for Kevlar; pr EN 6038
Hexcel® HexPly® 920KX-285-52% 125°C Curing Epoxy Matrix
Kevlar, 4H satin, 171 g/m2Information provided by HexCel